We report on the formation of the dilute $Pd_{1-x}Fe_x$ compositions with tunable magnetic properties under an ion-beam implantation of epitaxial Pd thin films. Binary $Pd_{1-x}Fe_x$ alloys with a mean iron content $x$ of $0.025$, $0.035$ or $0.075$ were obtained by the implantation of $40 keV$ $Fe^+$ ions into the palladium films on MgO (001) substrate to the doses of $0.5cdot10^{16}, 1.0cdot10^{16}$ and $3.0cdot10^{16}$ $ions/cm^2$, respectively. Structural and magnetic studies have shown that iron atoms occupy regular fcc-lattice Pd-sites without the formation of any secondary crystallographic phase. All the iron implanted Pd films reveal ferromagnetism at low temperatures (below $200 K$) with both the Curie temperature and saturation magnetization determined by the implanted iron dose. In contrast to the magnetic properties of the molecular beam epitaxy grown $Pd_{1-x}Fe_x$ alloy films with the similar iron contents, the Fe-implanted Pd films possess weaker in-plane magnetocrystalline anisotropy, and, accordingly, a lower coercivity. The observed multiple ferromagnetic resonances in the implanted $Pd_{1-x}Fe_x$ films indicate a formation of a magnetically inhomogeneous state due to spinodal decomposition into regions, presumably layers, with identical crystal symmetry but different iron contents. The multiphase magnetic structure is robust with respect to the vacuum annealing at $770 K$, though develops towards well-defined local $Pd-Fe$ compositions.
This paper has been withdrawn by the author
Insulating uniaxial room-temperature ferromagnets are a prerequisite for commonplace spin wave-based devices, the obstacle in contemporary ferromagnets being the coupling of ferromagnetism with large conductivity. We show that the uniaxial $A^{1+2x}$
We report on nanoscale strain gradients in ferroelectric HoMnO3 epitaxial thin films, resulting in a giant flexoelectric effect. Using grazing-incidence in-plane X-ray diffraction, we measured strain gradients in the films, which were 6 or 7 orders o
Magnetodynamics in epitaxial Fe1-xCox films on GaAs (100) are studied using time-resolved ferromagnetic resonance, in which the free precession of the magnetization after an impulsive excitation is measured using the polar Kerr effect. The sample is
Doping ferroelectric Hf0.5Zr0.5O2 with La is a promising route to improve endurance. However, the beneficial effect of La on the endurance of polycrystalline films may be accompanied by degradation of the retention. We have investigated the endurance