Recently, lithographic quantum dots in strained-Ge/SiGe have become a promising candidate for quantum computation, with a remarkably quick progression from demonstration of a quantum dot to qubit logic demonstrations. Here we present a measurement of the out-of-plane $g$-factor for single-hole quantum dots in this material. As this is a single-hole measurement, this is the first experimental result that avoids the strong orbital effects present in the out-of-plane configuration. In addition to verifying the expected $g$-factor anisotropy between in-plane and out-of-plane magnetic ($B$)-fields, variations in the $g$-factor dependent on the occupation of the quantum dot are observed. These results are in good agreement with calculations of the $g$-factor using the heavy- and light-hole spaces of the Luttinger Hamiltonian, especially the first two holes, showing a strong spin-orbit coupling and suggesting dramatic $g$-factor tunability through both the $B$-field and the charge state.
The effective g-factor of 2D holes in modulation doped mbox{p-SiGe/Ge/SiGe} structures was studied. The AC conductivity of samples with hole densities from $3.9 times 10^{11}$~to $6.2 times 10^{11}~text{cm}^{-2}$ was measured in perpendicular magneti
We report measurements of the effective $g$ factor of low-density two-dimensional holes in a Ge quantum well. Using the temperature dependence of the Shubnikov-de Haas oscillations, we extract the effective $g$ factor in a magnetic field perpendicula
We present angle-dependent measurements of the effective g-factor g* in a Ge-Si core-shell nanowire quantum dot. g* is found to be maximum when the magnetic field is pointing perpendicular to both the nanowire and the electric field induced by local
We report density-dependent effective hole mass measurements in undoped germanium quantum wells. We are able to span a large range of densities ($2.0-11times10^{11}$ cm$^{-2}$) in top-gated field effect transistors by positioning the strained buried
The high-frequency (ac) conductivity of a high quality modulation doped GeSi/Ge/GeSi single quantum well structure with hole density $p$=6$times$10$^{11}$cm$^{-2}$ was measured by the surface acoustic wave (SAW) technique at frequencies of 30 and 85~