Photoexcited Small Polaron Formation in Goethite ({alpha}-FeOOH) Nanorods Probed by Transient Extreme Ultraviolet Spectroscopy

64   0   0.0 ( 0 )
 نشر من قبل Ilana Porter
 تاريخ النشر 2019
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

Small polaron formation limits the mobility and lifetimes of photoexcited carriers in metal oxides. As the ligand field strength increases, the carrier mobility decreases, but the effect on the photoexcited small polaron formation is still unknown. Extreme ultraviolet transient absorption spectroscopy is employed to measure small polaron formation rates and probabilities in goethite ({alpha}-FeOOH) crystalline nanorods at pump photon energies from 2.2 to 3.1 eV. The measured polaron formation time increases with excitation photon energy from 70 {pm} 10 fs at 2.2 eV to 350 {pm} 30 fs at 2.6 eV, whereas the polaron formation probability (85 {pm} 10%) remains constant. By comparison to hematite ({alpha}-Fe2O3), an oxide analog, the role of ligand composition and metal center density in small polaron formation time is discussed. This work suggests that incorporating small changes in ligands and crystal structure could enable the control of photoexcited small polaron formation in metal oxides.

قيم البحث

اقرأ أيضاً

Few-femtosecond extreme ultraviolet (XUV) transient absorption spectroscopy, performed with optical 500-1000 nm supercontinuum and broadband XUV pulses (30-50 eV), simultaneously probes dynamics of photoexcited carriers in WS$_{2}$ at the W O$_3$ edg e (37-45 eV) and carrier-induced modifications of core-exciton absorption at the W N$_{6,7}$ edge (32-37 eV). Access to continuous core-to-conduction band absorption features and discrete core-exciton transitions in the same XUV spectral region in a semiconductor provides a novel means to investigate the effect of carrier excitation on core-exciton dynamics. The core-level transient absorption spectra, measured with either pulse arriving first to explore both core-level and valence carrier dynamics, reveal that core-exciton transitions are strongly influenced by the photoexcited carriers. A $1.2pm0.3$ ps hole-phonon relaxation time and a $3.1pm0.4$ ps carrier recombination time are extracted from the XUV transient absorption spectra from the core-to-conduction band transitions at the W O$_{3}$ edge. Global fitting of the transient absorption signal at the W N$_{6,7}$ edge yields $sim 10$ fs coherence lifetimes of core-exciton states and reveals that the photoexcited carriers, which alter the electronic screening and band filling, are the dominant contributor to the spectral modifications of core-excitons and direct field-induced changes play a minor role. This work provides a first look at the modulations of core-exciton states by photoexcited carriers and advances our understanding of carrier dynamics in metal dichalcogenides.
We utilize coherent femtosecond extreme ultraviolet (EUV) pulses derived from a free electron laser (FEL) to generate transient periodic magnetization patterns with periods as short as 44 nm. Combining spatially periodic excitation with resonant prob ing at the dichroic M-edge of cobalt allows us to create and probe transient gratings of electronic and magnetic excitations in a CoGd alloy. In a demagnetized sample, we observe an electronic excitation with 50 fs rise time close to the FEL pulse duration and ~0.5 ps decay time within the range for the electron-phonon relaxation in metals. When the experiment is performed on a sample magnetized to saturation in an external field, we observe a magnetization grating, which appears on a sub-picosecond time scale as the sample is demagnetized at the maxima of the EUV intensity and then decays on the time scale of tens of picoseconds via thermal diffusion. The described approach opens prospects for studying dynamics of ultrafast magnetic phenomena on nanometer length scales.
123 - Emily Sistrunk 2014
Nonlinear spectroscopy in the extreme ultraviolet (EUV) and soft x-ray spectral range offers the opportunity for element selective probing of ultrafast dynamics using core-valence transitions (Mukamel et al., Acc. Chem. Res. 42, 553 (2009)). We demon strate a step on this path showing core-valence sensitivity in transient grating spectroscopy with EUV probing. We study the optically induced insulator-to-metal transition (IMT) of a VO2 film with EUV diffraction from the optically excited sample. The VO2 exhibits a change in the 3p-3d resonance of V accompanied by an acoustic response. Due to the broadband probing we are able to separate the two features.
Silicon nanoparticles have the promise to surpass the theoretical efficiency limit of single-junction silicon photovoltaics by the creation of a phonon bottleneck, a theorized slowing of the cooling rate of hot optical phonons that in turn reduces th e cooling rate of hot carriers in the material. To verify the presence of a phonon bottleneck in silicon nanoparticles requires simultaneous resolution of electronic and structural changes at short timescales. Here, extreme ultraviolet transient absorption spectroscopy is used to observe the excited state electronic and lattice dynamics in polycrystalline silicon nanoparticles following 800 nm photoexcitation, which excites carriers with $0.35 pm 0.03$ eV excess energy above the ${Delta}_1$ conduction band minimum. The nanoparticles have nominal 100 nm diameters with crystalline grain sized of about ~16 nm. The extracted carrier-phonon and phonon-phonon relaxation times of the nanoparticles are compared to those for a silicon (100) single crystal thin film at similar carrier densities ($2$ x $10^{19} cm^{-3}$ for the nanoparticles and $6$ x $10^{19} cm^{-3}$ for the thin film). The measured carrier-phonon and phonon-phonon scattering lifetimes for the polycrystalline nanoparticles are $870 pm 40$ fs and $17.5 pm 0.3$ ps, respectively, versus $195 pm 20$ fs and $8.1 pm 0.2$ ps, respectively, for the silicon thin film. The reduced scattering rates observed in the nanoparticles are consistent with the phonon bottleneck hypothesis.
The optical properties of magnetite at room temperature were studied by infrared reflectivity measurements as a function of pressure up to 8 GPa. The optical conductivity spectrum consists of a Drude term, two sharp phonon modes, a far-infrared band at around 600 cm$^{-1}$, and a pronounced mid-infrared absorption band. With increasing pressure both absorption bands shift to lower frequencies and the phonon modes harden in a linear fashion. Based on the shape of the MIR band, the temperature dependence of the dc transport data, and the occurrence of the far-infrared band in the optical conductivity spectrum the polaronic coupling strength in magnetite at room temperature should be classified as intermediate. For the lower-energy phonon mode an abrupt increase of the linear pressure coefficient occurs at around 6 GPa, which could be attributed to minor alterations of the charge distribution among the different Fe sites.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا