The high-temperature ferroelectric order and a remarkable magnetoelectric effect driven by the magnetic field cooling are reported in R2BaCuO5 (R = Er, Dy, Sm) series. The ferroelectric (FE) orders are observed at much higher temperatures than their magnetic orders for all three members. The value of FE Curie temperature (TFE) is considerably high as ~ 235 K with the polarization value (P) of ~ 1410 {mu}C/m2 for a 4 kV/cm poling field in case of Er2BaCuO5, whereas the values of TFE and P are also promising as ~ 232 K and ~ 992 {mu}C/m2 for Dy2BaCuO5, and ~ 184 K and ~ 980 {mu}C/m2 for Sm2BaCuO5. The synchrotron diffraction studies of Dy2BaCuO5 confirm a structural transition at TFE to a polar Pna21 structure, which correlates the FE order. An unusual magnetoelectric coupling is observed below the R order for Er and Dy compounds and below the Cu order for Sm compound, when the pyroelectric current is recorded only with the magnetic field both in heating and cooling cycles i.e. typical magnetic field cooled effect. The magnetic field cooled effect driven emergence of polarization is ferroelectric in nature, as it reverses due to the opposite poling field. The unexplored R2BaCuO5 series attracts the community for large TFE, high P value, and strange magnetoelectric consequences.
We have made a magnetic characterization of Nd0.5Sr0.5MnO3, Nd0.5Ca0.5MnO3, Sm0.5Ca0.5MnO3, Dy0.5Ca0.5MnO3 and Ho0.5Ca0.5MnO3 polycrystalline samples. Ferromagnetic, antiferromagnetic and charge ordering transitions in our samples agree with previous
The single crystal study of CaBaCo4O7, a non collinear ferrimagnet (TC=64K), with a polar orthorhombic space group (Pbn21) between 4 K and 293 K, shows the appearance below TC of a large electric polarization along its c axis, reaching 17mC.m-2 at 10
The time-differential perturbed-angular-correlation (TDPAC) technique was applied to the study of the internal electric-field gradient (EFG) in Eu- and Ho-sesquioxides in their cubic bixbyite phases. The results, as well as previous characterizations
We present a unique example of giant magnetoelectric effect in a conventional multiferroic HoMnO3, where polarization is very large (~56 mC/m2) and the ferroelectric transition temperature is higher than the magnetic ordering temperature by an order.
The magnetic structures of the title compounds have been studied by neutron diffraction. In contrast to the isomorphous RNi2B2C compounds wherein a variety of exotic incommensurate modulated structures has been observed, the magnetic structure of ErC