Large perpendicular magnetic anisotropy in epitaxial Fe/MgAl2O4(001) heterostructures

97   0   0.0 ( 0 )
 نشر من قبل Qingyi Xiang
 تاريخ النشر 2018
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

We investigated perpendicular magnetic anisotropy (PMA) and related properties of epitaxial Fe (0.7 nm)/MgAl2O4(001) heterostructures prepared by electron-beam evaporation. Using an optimized structure, we obtained a large PMA energy ~1 MJ/m3 at room temperature, comparable to that in ultrathin-Fe/MgO(001) heterostructures. Both the PMA energy and saturation magnetization show weak temperature dependence, ensuring wide working temperature in application. The effective magnetic damping constant of the 0.7 nm Fe layer was ~0.02 using time-resolved magneto-optical Kerr effect. This study demonstrates capability of the Fe/MgAl2O4 heterostructure for perpendicular magnetic tunnel junctions, as well as a good agreement with theoretical predictions.



قيم البحث

اقرأ أيضاً

We have investigated crystalline magnetic anisotropy in the electric field (EF) for the Fe-Pt surface which have a large perpendicular anisotropy, by means of the first-principles approach. The anisotropy is reduced linearly with respect to the inwar d EF, associated with the induced spin density around the Fe layer. Although the magnetic anisotropy energy (MAE) density reveals the large variation around the atoms, the intrinsic contribution to the MAE is found to mainly come from the Fe layer.
The origin of large perpendicular magneto-crystalline anisotropy (PMCA) in Fe/MgO (001) is revealed by comparing Fe layers with and without the MgO. Although Fe-O $p$-$d$ hybridization is weakly present, it cannot be the main origin of the large PMCA as claimed in previous study. Instead, perfect epitaxy of Fe on the MgO is more important to achieve such large PMCA. As an evidence, we show that the surface layer in a clean free-standing Fe (001) dominantly contributes to $E_{MCA}$, while in the Fe/MgO, those by the surface and the interface Fe layers contribute almost equally. The presence of MgO does not change positive contribution from $langle xz|ell_Z|yzrangle$, whereas it reduces negative contribution from $langle z^2|ell_X|yzrangle$ and $langle xy|ell_X|xz,yzrangle$.
A combination of theoretical modelling and experiments reveals the origin of the large perpendicular magnetic anisotropy (PMA) that appears in nanometer-thick epitaxial Co films intercalated between graphene (Gr) and a heavy metal (HM) substrate, as a function of the Co thickness. High quality epitaxial Gr/Co /HM(111) (HM=Pt,Ir) heterostructures are grown by intercalation below graphene, which acts as a surfactant that kinetically stabilizes the pseudomorphic growth of highly perfect Co face-centered tetragonal ($fct$) films, with a reduced number of stacking faults as the only structural defect observable by high resolution scanning transmission electron microscopy (HR-STEM). Magneto-optic Kerr effect (MOKE) measurements show that such heterostructures present PMA up to large Co critical thicknesses of about 4~nm (20~ML) and 2~nm (10~ML) for Pt and Ir substrates, respectively, while X-ray magnetic circular dichroism (XMCD) measurements show an inverse power law of the anistropy of the orbital moment with Co thickness, reflecting its interfacial nature, that changes sign at about the same critical values. First principles calculations show that, regardless of the presence of graphene, ideal Co $fct$ films on HM buffers do not sustain PMAs beyond around 6~MLs due to the in-plane contribution of the inner bulk-like Co layers. The large experimental critical thicknesses sustaining PMA can only be retrieved by the inclusion of structural defects that promote a local $hcp$ stacking such as twin boundaries or stacking faults. Remarkably, a layer resolved analysis of the orbital momentum anisotropy reproduces its interfacial nature, and reveals that the Gr/Co interface contribution is comparable to that of the Co/Pt(Ir).
The structures of epitaxial ultrathin Co2FeAl/MgO(001) heterostructures relating to the interface-induced perpendicular magnetic anisotropy (PMA) were investigated using scanning transmission electron microscopy, energy dispersive x-ray spectroscopy, and x-ray magnetic circular dichroism. We found that Al atoms from the Co2FeAl layer significantly interdiffuse into MgO, forming an Al-deficient Co-Fe-Al/Mg-Al-O structure near the Co2FeAl/MgO interface. This atomic replacement may play an additional role for enhancing PMA, which is consistent with the observed large perpendicular orbital magnetic moments of Fe atoms at the interface. This work suggests that control of interdiffusion at ferromanget/barrier interfaces is critical for designing an interface-induced PMA system.
In this work we report the appearence of a large perpendicular magnetic anisotropy (PMA) in Fe$_{1-x}$Ga$_x$ thin films grown onto ZnSe/GaAs(100). This arising anisotropy is related to the tetragonal metastable phase in as-grown samples recently repo rted [M. Eddrief {it et al.}, Phys. Rev. B {bf 84}, 161410 (2011)]. By means of ferromagnetic resonance studies we measured PMA values up to $sim$ 5$times$10$^5$ J/m$^3$. PMA vanishes when the cubic structure is recovered upon annealing at 300$^{circ}$C. Despite the important values of the magnetoelastic constants measured via the cantilever method, the consequent magnetoelastic contribution to PMA is not enough to explain the observed anisotropy values in the distorted state. {it Ab initio} calculations show that the chemical ordering plays a crucial role in the appearance of PMA. Through a phenomenological model we are able to explain that an excess of next nearest neighbour Ga pairs (B$_2$-like ordering) along the perpendicular direction arises as the source of PMA in Fe$_{1-x}$Ga$_x$ thin films.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا