X-ray magnetic circular dichroism study of epitaxial magnetite ultrathin film on MgO (100)

223   0   0.0 ( 0 )
 نشر من قبل Wenqing Liu
 تاريخ النشر 2015
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

The spin and orbital magnetic moments of the Fe3O4 epitaxial ultrathin film synthesized by plasma assisted simultaneous oxidization on MgO(100) have been studied with X-ray magnetic circular dichroism (XMCD). The ultrathin film retains a rather large total magnetic moment, i.e. (2.7+-0.15) uB/f.u., which is ~ 70% of that for the bulk-like Fe3O4. A significant unquenched orbital moment up to (0.54+-0.05) uB/f.u. was observed, which could come from the symmetry breaking at the Fe3O4/MgO interface. Such sizable orbital moment will add capacities to the Fe3O4-based spintronics devices in the magnetization reversal by the electric field.



قيم البحث

اقرأ أيضاً

We performed a soft x-ray magnetic circular dichroism (XMCD) study of a Zn$_{1-x}$V$_x$O thin film which showed small ferromagnetic moment. Field and temperature dependences of V 2$p$ XMCD signals indicated the coexistence of Curie-Weiss paramagnetic , antiferromagnetic, and possibly ferromagnetic V ions, quantitatively consistent with the magnetization measurements. We attribute the paramagnetic signal to V ions substituting Zn sites which are somewhat elongated along the c-axis.
Soft x-ray magnetic circular dichroism (XMCD) measurements at the Co L2,3 edges of Co doped rutile TiO2 at room temperature have revealed clear multiplet features characteristic of ferromagnetic Co2+ ions coordinated by O2- ions, being in sharp contr ast to the featureless XMCD spectrum of Co metal or metallic clusters. The absorption and XMCD spectra agree well with a full atomic-multiplet calculation for the Co2+ high-spin state in the D2h-symmetry crystal field at the Ti site in rutile TiO2. The results indicate that the ferromagnetism arises from the Co2+ ions substituting the Ti4+ ions.
Nanoscale Fe3O4 epitaxial thin film has been synthesized on MgO/GaAs(100) spintronic heterostructure, and studied with X-ray magnetic circular dichroism (XMCD). We have observed a total magnetic moment of (3.32 +- 0.1) uB/f.u., retaining 83% of the b ulk value. Unquenched orbital moment of (0.47 +- 0.05) uB/f.u. has been confirmed by carefully applying the sum rule. The results offer direct experimental evidence of the bulk-like total magnetic moment and a large orbital moment in the nanoscale fully epitaxial Fe3O4/MgO/GaAs(100) heterostructure, which is significant for spintronics applications.
Temperature dependent magnetometry and transport measurements on epitaxial Fe3O4 films grown on BaTiO3(100) single crystals by molecular beam epitaxy show a series of discontinuities, that are due to changes in the magnetic anisotropy induced by stra in in the different crystal phases of BaTiO3. The magnetite film is under tensile strain at room temperature, which is ascribed to the lattice expansion of BaTiO3 at the cubic to tetragonal transition, indicating that the magnetite film is relaxed at the growth temperature. From the magnetization versus temperature curves, the variation in the magnetic anisotropy is determined and compared with the magnetoelastic anisotropies. These results demonstrate the possibility of using the piezoelectric response of BaTiO3 to modulate the magnetic anisotropy of magnetite films.
We have performed x-ray magnetic circular dichroism (XMCD) and valence-band photoemission studies of the diluted ferromagnetic semiconductor Zn$_{1-x}$Cr$_x$Te. XMCD signals due to ferromagnetism were observed at the Cr 2p absorption edge. Comparison with atomic multiplet calculations suggests that the magnetically active component of the Cr ion was divalent under the tetrahedral crystal field with tetragonal distortion along the crystalline a-, b-, and c-axes. In the valence-band spectra, spectral weight near the Fermi level was strongly suppressed, suggesting the importance of Jahn-Teller effect and the strong Coulomb interaction between the Cr 3d electrons.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا