Large size single crystals of bis(thiourea)zinc(II) chloride (BTZC), a potential nonlinear optical material, have been grown successfully by the Sankaranarayanan Ramasamy (SR) method. Powder X-ray diffraction and Fourier transform infrared analyses confirmed the material of the grown crystal. Thermal stability was assessed by the thermogravimetric differential thermal analysis. The high-resolution X-ray diffraction and dielectric measurements indicate that the crystal grown by the SR method has good crystalline perfection and low density of defects.
قيم البحث
اقرأ أيضاً
Single crystals of the three-dimensional frustrated magnet and spin liquid candidate compound PbCuTe$_2$O$_6$, were grown using both the Travelling Solvent Floating Zone (TSFZ) and the Top-Seeded Solution Growth (TSSG) techniques. The growth conditio
ns were optimized by investigating the thermal properties. The quality of the crystals was checked by polarized optical microscopy, X-ray Laue and X-ray powder diffraction, and compared to the polycrystalline samples. Excellent quality crystals were obtained by the TSSG method. Magnetic measurements of these crystals revealed a small anisotropy for different crystallographic directions in comparison with the previously reported data. The heat capacity of both single crystal and powder samples reveal a transition anomaly around 1~K. Curiously the position and magnitude of the transition are strongly dependent on the crystallite size and it is almost entirely absent for the smallest crystallites. A structural transition is suggested which accompanies the reported ferroelectric transition, and a scenario whereby it becomes energetically unfavourable in small crystallites is proposed.
The title paper by Boopathi and Ramasamy reports a study on the crystal growth and characterization of dibromobis (L-proline)Cd(II) (1). Many points of criticism, concerning the crystal structure of (1) and the magnetic properties of (1) dibromo bis(
L-proline)Zn(II) (2) and diiodo bis(2-aminopyridine)Cd(II) (3) are reported to show that compounds 1 to 3 are not soft magnets but instead diamagnetic solids.
Single crystals of (Nd1-xCex)2Fe14B are grown out of Fe-(Nd,Ce) flux. Chemical and structural analysis of the crystals indicates that (Nd1-xCex)2Fe14B forms a solid solution until at least x = 0.38 with a Vegard-like variation of the lattice constant
s with x. Refinements of single crystal neutron diffraction data indicate that Ce has a slight site preference (7:3) for the 4g rare earth site over the 4f site. Magnetization measurements show that for x = 0.38 the saturation magnetization at 400 K, a temperature important to applications, falls from 29.8 for the parent Nd2Fe14B to 27.6 (mu)B/f.u., the anisotropy field decreases from 5.5 T to 4.7 T, and the Curie temperature decreases from 586 to 543 K. First principles calculations carried out within density functional theory are used to explain the decrease in magnetic properties due to Ce substitution. Though the presence of the lower-cost and more abundant Ce slightly affects these important magnetic characteristics, this decrease is not large enough to affect a multitude of applications. Ce-substituted Nd2Fe14B is therefore a potential high-performance permanent magnet material with substantially reduced Nd content.
The crystallographic orientation of SrIrO3 surfaces is decisive for the occurrence of topological surface states. We show from DFT computations that (001) and (110) free surfaces have comparable energies, and, correspondingly, we experimentally obser
ve that single micro-crystals exhibit both facet orientations. These surfaces are found to relax over typically the length of one oxygen octahedron, defining a structural critical thickness for thin films. A reconstruction of the electronic density associated to tilts of the oxygen octahedra is observed. On the other hand, thin films have invariably been reported to grow along the (110) direction. We show that the interfacial energy associated to the oxygen octahedra distortion for epitaxy is likely at the origin of this specific feature, and propose leads to induce (001) SrIrO3 growth.
Single crystals of A$_{1-x}$K$_x$Fe$_2$As$_2$ (A=Ba, Sr) with high quality have been grown successfully by FeAs self-flux method. The samples have sizes up to 4 mm with flat and shiny surfaces. The X-ray diffraction patterns suggest that they have hi
gh crystalline quality and c-axis orientation. The non-superconducting crystals show a spin-density-wave (SDW) instability at about 173 K and 135 K for Sr-based and Ba-based compound, respectively. After doping K as the hole dopant into the BaFe$_2$As$_2$ system, the SDW transition is smeared, and superconducting samples with the compound of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (0 $< x leqslant$ 0.4) are obtained. The superconductors characterized by AC susceptibility and resistivity measurements exhibit very sharp superconducting transition at about 36 K, 32 K, 27 K and 23 K for x= 0.40,0.28,0.25 and 0.23, respectively.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها