The magnetic structure of the Eu2+ moments in the superconducting EuFe2(As1-xPx)2 sample with x = 0.15 has been determined using element specific x-ray resonant magnetic scattering. Combining magnetic, thermodynamic and scattering measurements, we conclude that the long range ferromagnetic order of the Eu2+ moments aligned primarily along the c axis coexists with the bulk superconductivity at zero field. At an applied magnetic field >= 0.6 T, superconductivity still coexists with the ferromagnetic Eu2+ moments which are polarized along the field direction. We propose a spontaneous vortex state for the coexistence of superconductivity and ferromagnetism in EuFe2(As0.85P0.15)2.
قيم البحث
اقرأ أيضاً
Superconductivity is found in 50% K-doped EuFe2As2 sample below 33 K. Our results of electrical resistivity, magnetic susceptibility and 57Fe and 151Eu Mossbauer spectroscopy provide clear evidence that the ordering of the Fe moments observed at 190
K in undoped EuFe2As2 is completely suppressed in our 50% K doped sample, thus there is no coexistence between the Fe magnetic order and the superconducting state. However, short range ordering of the Eu moments is coexisting with the superconducting state below 15 K. A bump in the susceptibility well below Tc as well as a slight broadening of the Fe Mossbauer line below 15 K evidence an interplay between the Eu magnetism and the superconducting state.
By performing high-pressure single-crystal neutron diffraction measurements, the evolution of structure and magnetic ordering in EuFe2As2 under hydrostatic pressure were investigated. Both the tetragonal-toorthorhombic structural transition and the F
e spin-density-wave (SDW) transition are gradually suppressed and become decoupled with increasing pressure. The antiferromagnetic order of the Eu sublattice is, however, robust against the applied pressure up to 24.7 kbar, without showing any change of the ordering temperature. Under the pressure of 24.7 kbar, the lattice parameters of EuFe2As2 display clear anomalies at 27(3) K, well consistent with the superconducting transition observed in previous high-pressure resistivity measurements. Such an anomalous thermal expansion around Tc strongly suggests the appearance of bulk superconductivity and strong electron-lattice coupling in EuFe2As2 induced by the hydrostatic pressure. The coexistence of long-range ordered Eu-antiferromagnetism and pressure-induced superconductivity is quite rare in the EuFe2As2-based iron pnictides.
We show the observation of the coexistence of bulk superconductivity and ferromagnetism in CeO1-xFxBiS2(x = 0 - 1.0) prepared by annealing under high-pressure. In CeO1-xFxBiS2 system, both superconductivity and two types of ferromagnetism with respec
tive magnetic transition temperatures of 4.5 K and 7.5 K are induced upon systematic F substitution. This fact suggests that carriers generated by the substitution of O by F are supplied to not only the BiS2 superconducting layers but also the CeO blocking layers. Furthermore, the highest superconducting transition temperature is observed when the ferromagnetism is also enhanced, which implies that superconductivity and ferromagnetism are linked to each other in the CeO1-xFxBiS2 system.
Unambiguous evidence for the microscopic coexistence of ferromagnetism and superconductivity in UCoGe ($T_{rm Curie} sim 2.5$ K and $T_{rm SC}$ $sim$ 0.6 K) is reported from $^{59}$Co nuclear quadrupole resonance (NQR). The $^{59}$Co-NQR signal below
1 K indicates ferromagnetism throughout the sample volume, while nuclear spin-lattice relaxation rate $1/T_1$ in the ferromagnetic (FM) phase decreases below $T_{rm SC}$ due to the opening of the superconducting(SC) gap. The SC state was found to be inhomogeneous, suggestive of a self-induced vortex state, potentially realizable in a FM superconductor. In addition, the $^{59}$Co-NQR spectrum around $T_{rm Curie}$ show that the FM transition in UCoGe possesses a first-order character, which is consistent with the theoretical prediction that the low-temperature FM transition in itinerant magnets is generically of first-order.
Superconducting characteristics such as the Meissner-Ochsenfeld state, screening supercurrents and hysteresis loops of type-II superconductors were observed from the temperature and magnetic field dependences of the magnetic moment, m(T, H), in graph
ite powders reacted with sulfur for temperatures below 9.0 K. The temperature dependence of the lower critical field Hc1(T) was determined and the zero-temperature penetration depth, lambda(0), was estimated (lambda (0) = 227 nm). The superconductivity was observed to be highly anisotropic and to coexist with a ferromagnetic state that has a Curie temperature well above room temperature. A continuous transition from the superconducting state to the ferromagnetic state could be achieved by simply increasing the applied magnetic field.