Half-Heusler YPtSb thin films were fabricated by magnetron co-sputtering method on MgO-buffered SiO2/Si(001) substrates. X-ray diffraction pattern and Energy dispersive X-ray spectroscopy confirmed the high-quality growth and stoichiometry. The temperature dependence of the resistivity shows a semiconducting-type behavior down to low temperature. The Hall mobility was determined to be 450 cm2/Vs at 300K, which is much higher than the bulk value (300 cm2/Vs). In-plane magnetoresistance (MR) measurements with fields applied along and perpendicular to the current direction show opposite MR signs, which suggests the possible existence of the topological surface states.
قيم البحث
اقرأ أيضاً
Simple vacuum evaporation technique for deposition of dyes on various solid surfaces has been developed. The method is compatible with conventional solvent-free nanofabrication processing enabling fabrication of nanoscale optoelectronic devices. Thin
films of fluorescein were deposited on glass, fluorine-tin-oxide (FTO) coated glass with and without atomically layer deposited (ALD) nanocrystalline 20 nm thick anatase TiO2 coating. Surface topology, absorption and emission spectra of the films depends on their thickness and the material of supporting substrate. On a smooth glass surface the dye initially formes islands before merging into a uniform layer after 5 to 10 monolayers. On FTO covered glass the absorption spectra are similar to fluorescein solution in ethanol. Absorption spectra on ALD-TiO2 is red shifted compared to the film deposited on bare FTO. The corresponding emission spectra at {lambda} = 458 nm excitation show various thickness and substrate dependent features, while the emission of films deposited on TiO2 is quenched due to the effective electron transfer to the semiconductor conduction band.
The discovery of topological insulators (TIs), materials with bulk band gaps and protected cross-gap surface states, in compounds such as Bi2Se3 has generated much interest in identifying topological surface states (TSSs) in other classes of material
s. In particular, recent theory calculations suggest that TSSs may be found in half-Heusler ternary compounds. If experimentally realizable, this would provide a materials platform for entirely new heterostructure spintronic devices that make use of the structurally-identical but electronically-varied nature of Heusler compounds. Here, we show the presence of a TSS in epitaxially grown thin films of the half-Heusler compound PtLuSb. Spin and angle-resolved photoemission spectroscopy (ARPES), complemented by theoretical calculations, reveals a surface state with linear dispersion and a helical tangential spin texture consistent with previous predictions. This experimental verification of TI behavior is a significant step forward in establishing half-Heusler compounds as a viable material system for future spintronics devices.
BaZrS3 is a prototypical chalcogenide perovskite, an emerging class of unconventional semiconductor. Recent results on powder samples reveal that it is a material with a direct band gap of 1.7-1.8 eV, a very strong light-matter interaction, and a hig
h chemical stability. However, many of the fundamental properties are unknown, hindering the ability to apply BaZrS3 for optoelectronics. Here we report the fabrication of BaZrS3 thin films, by sulfurization of oxide films deposited by pulsed laser deposition. We show that these films are n-type with carrier densities in the range of 10^19-10^20 cm^-3. Depending on the processing temperature, the Hall mobility ranges from 2.1 to 13.7 cm^2/Vs. The absorption coefficient is > 10^5 cm-1 at photon energy > 1.97 eV. Temperature dependent conductivity measurements suggest shallow donor levels. These results assure that BaZrS3 is a promising candidate for optoelectronics such as photodetectors, photovoltaics, and light emitting diodes.
We correlate simultaneously recorded magnetotransport and spatially resolved magneto optical Kerr effect (MOKE) data in Co2FeAl Heusler compound thin films micropatterned into Hall bars. Room temperature MOKE images reveal the nucleation and propagat
ion of domains in an externally applied magnetic field and are used to extract a macrospin corresponding to the mean magnetization direction in the Hall bar. The anisotropic magnetoresistance calculated using this macrospin is in excellent agreement with magnetoresistance measurements. This suggests that the magnetotransport in Heusler compounds can be adequately simulated using simple macrospin models, while the magnetoresistance contribution due to domain walls is of negligible importance.
The factors that affect the thermal conductivity of semiconductors is a topic of great scientific interest, especially in relation to thermoelectrics. Key developments have been the concept of the phonon-glass-electron-crystal (PGEC) and the related
idea of rattling to achieve this. We use first principles phonon and thermal conductivity calculations in order to explore the concept of rattling for stoichiometric ordered half-Heusler compounds. These compounds can be regarded as filled zinc blende materials, and the filling atom could be viewed as a rattler if it is weakly bound. We use two simple metrics, one related to the frequency and the other to bond frustration and anharmonicity. We find that both measures correlate with thermal conductivity. This suggests that both may be useful in screening materials for low thermal conductivity.