تسجيل مستخدم جديدEnhanced grain surface effect on magnetic properties of nanometric La0.7Ca0.3MnO3 manganite : Evidence of surface spin freezing of manganite nanoparticles
113
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We have investigated the effect of nanometric grain size on magnetic properties of single phase, nanocrystalline, granular La0.7Ca0.3MnO3 (LCMO) sample. We have considered core-shell structure of our LCMO nanoparticles, which can explain its magnetic properties. From the temperature dependence of field cooled (FC) and zero-field cooled (ZFC) dc magnetization (DCM), the magnetic properties could be distinguished into two regimes: a relatively high temperature regime T > 40 K where the broad maximum of ZFC curve (at T = Tmax) is associated with the blocking of core particle moments, whereas the sharp maximum (at T = TS) is related to the freezing of surface (shell) spins. The unusual shape of M (H) loop at T = 1.5 K, temperature dependent feature of coercive field and remanent magnetization give a strong support of surface spin freezing that are occurring at lower temperature regime (T < 40 K) in this LCMO nanoparticles. Additionally, waiting time (tw) dependence of ZFC relaxation measurements at T = 50 K show weak dependence of relaxation rate [S(t)] on tw and dM/dln(t) following a logarithmic variation on time. Both of these features strongly support the high temperature regime to be associated with the blocking of core moments. At T = 20 K, ZFC relaxation measurements indicates the existence of two different types of relaxation processes in the sample with S(t) attaining a maximum at the elapsed time very close to the wait time tw = 1000 sec, which is an unequivocal sign of glassy behavior. This age-dependent effect convincingly establish the surface spin freezing of our LCMO nanoparticles associated with a background of superparamagnetic (SPM) phase of core moments.
قيم البحث
اقرأ أيضاً
We have used oxygen ions irradiation to generate controlled structural disorder in thin manganite films. Conductive atomic force microscopy CAFM), transport and magnetic measurements were performed to analyze the influence of the implantation process
in the physical properties of the films. CAFM images show regions with different conductivity values, probably due to the random distribution of point defect or inhomogeneous changes of the local Mn3+/4+ ratio to reduce lattice strains of the irradiated areas. The transport and magnetic properties of these systems are interpreted in this context. Metal-insulator transition can be described in the frame of a percolative model. Disorder increases the distance between conducting regions, lowering the observed TMI. Point defect disorder increases localization of the carriers due to increased disorder and locally enhanced strain field. Remarkably, even with the inhomogeneous nature of the samples, no sign of low field magnetoresistance was found. Point defect disorder decreases the system magnetization but doesn t seem to change the magnetic transition temperature. As a consequence, an important decoupling between the magnetic and the metal-insulator transition is found for ion irradiated films as opposed to the classical double exchange model scenario.
We report active control of the friction force at the contact between a nanoscale asperity and a La$_{0.55}$Ca$_{0.45}$MnO$_3$ (LCMO) thin film using electric fields. We use friction force microscopy under ultrahigh vacuum conditions to measure the f
riction force as we change the film resistive state by electric field-induced resistive switching. Friction forces are high in the insulating state and clearly change to lower values when the probed local region is switched to the conducting state. Upon switching back to an insulating state, the friction forces increase again. Thus, we demonstrate active control of friction without having to change the contact temperature or pressure. By comparing with measurements of friction at the metal-to-insulator transition and with the effect of applied voltage on adhesion, we rule out electronic excitations, electrostatic forces and changes in contact area as the reasons for the effect of resistive switching on friction. Instead, we argue that friction is limited by phonon relaxation times which are strongly coupled to the electronic degrees of freedom through distortions of the MnO6 octahedra. The concept of controlling friction forces by electric fields should be applicable to any materials where the field produces strong changes in phonon lifetimes.
The structure, electronic, and magnetic properties of the Mo-doped perovskite La0.7Ca0.3Mn1-xMoxO3 (x < 0.1) have been studied. A significant increase in resistivity and lattice parameters were observed with Mo doping. A marginal decrease in the Curi
e temperature Tc and the associated metal-insulator transition Tp were observed. Magnetization data reveal that long-range ferromagnetic ordering persists in all samples studied and the saturation moment decreases linearly as x increases. Enhancement in magnetoresistance at near Tc in the Mo-doped compounds with an optimum doping value x = 0.05 was observed. The overall experimental results can be explained by considering the induced Mn2+ ions with Mo6+ in the Mo-doped systems, with the strong FM coupling between Mn4+/2+- O - Mn3+.
The effect of doping of rare earth Gd 3+ ion replacing Nd 3+ in Nd0.7Sr0.3MnO3 is investigated in details. Measurements of resistivity, magnetoresistance, magnetization, linear and non linear ac magnetic susceptibility on chemically synthesized (Nd0.
7-xGdx)Sr0.3MnO3 shows various interesting features with doping level x=0.3. Comparative study has been carried out between a bulk and a nanometric sample (grain size ~ 60 nm) synthesized from the same as prepared powder to maintain identical stoichiometry. Resistivity of the samples shows strong dependence on the magnetic field - temperature history. The magnetoresistance of the samples also show strong irreversibility with respect to sweeping of the field between highest positive and negative values. Moreover, resistivity is found to increase with time after field cooling and then switching off the field. All these phenomena have been attributed to phase separation effect and arrest of phases in the samples. Furthermore, the bulk sample displays a spin glass like behaviour as evident from frequency dependence of linear ac magnetic susceptibility and critical divergence of the nonlinear ac magnetic susceptibility. The experimentally obtained characteristic time t after dynamical scaling analysis of the frequency dependence of the ac susceptibility is found to be t=10-17 s which implies that the system is different from a canonical spin glass. An unusual frequency dependence of the second harmonic of ac susceptibility around the magnetic transition temperature led us to designate the magnetic state of the sample to be glassy ferromagnetic. On reduction of grain size low field magnetoresistance and phase arrest phenomena are found to enhance but the glassy state is observed to be destabilized in the nanometric sample.
We have studied the temperature dependence of low-field magnetoresistance and current-voltage characteristics of a low-angle bi-crystal grain boundary junction in perovskite manganite La_{2/3}Sr_{1/3}MnO_3 thin film. By gradually trimming the junctio
n we have been able to reveal the non-linear behavior of the latter. With the use of the relation M_{GB} propto M_{bulk}sqrt{MR^*} we have extracted the grain boundary magnetization. Further, we demonstrate that the built-in potential barrier of the grain boundary can be modelled by V_{bi}propto M_{bulk}^2 - M_{GB}^2. Thus our model connects the magnetoresistance with the potential barrier at the grain boundary region. The results indicate that the band-bending at the grain boundary interface has a magnetic origin.