تسجيل مستخدم جديدThermal expansion of the magnetically ordering intermetallics RTMg (R = Eu, Gd and T = Ag, Au)
172
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report measurements of the thermal expansion for two Eu$^{+2}$- and two Gd$^{+3}$-based intermetallics which exhibit ferro- or antiferromagnetic phase transitions. These materials show sharp positive (EuAgMg and GdAuMg) and negative (EuAuMg and GdAgMg) peaks in the temperature dependence of the thermal expansion coefficient $alpha$ which become smeared and/or displaced in an external magnetic field. Together with specific heat data we determine the initial pressure dependences of the transition temperatures at ambient pressure using the Ehrenfest or Clausius-Clapeyron relation. We find large pressure dependences indicating strong spin-phonon coupling, in particular for GdAgMg and EuAuMg where a quantum phase transition might be reached at moderate pressures of a few GPa.
قيم البحث
اقرأ أيضاً
The classic metallurgical systems -- noble metal alloys -- that have formed the benchmark for various alloy theories, are revisited. First-principles fully relaxed general potential LAPW total energies of a few ordered structures are used as input to
a mixed-space cluster expansion calculation to study the phase stability, thermodynamic properties and bond lengths in Cu-Au, Ag-Au, Cu-Ag and Ni-Au alloys. (i) Our theoretical calculations correctly reproduce the tendencies of Ag-Au and Cu-Au to form compounds and Ni-Au and Cu-Ag to phase separate at T=0 K. (ii) Of all possible structures, Cu/sub 3/Au (L1/sub 2/) and CuAu (L1/sub 0/) are found to be the most stable low-temperature phases of Cu/sub 1-x/Au/sub x/ with transition temperatures of 530 K and 660 K, respectively, compared to the experimental values 663 K and 670 K. The significant improvement over previous first-principles studies is attributed to the more accurate treatment of atomic relaxations in the present work. (iii) LAPW formation enthalpies demonstrate that L1/sub 2/, the commonly assumed stable phase of CuAu/sub 3/, is not the ground state for Au-rich alloys, but rather that ordered <100> superlattices are stabilized. (iv) We extract the non-configurational (e.g., vibrational) entropies of formation and obtain large values for the size mismatched systems: 0.48 k/sub B//atom in Ni/sub 0.5/Au/sub 0.5/ (T=1100 K), 0.37 k/sub B//atom in Cu/sub 0.14/Ag/sub 0.86/ (T=1052 K), and 0.16 k/sub B//atom in Cu/sub 0.5/Au/sub 0.5/ (T=800 K). (v) Using 8 atom/cell special quasirandom structures we study the bond lengths in disordered Cu-Au and Ni-Au alloys and obtain good qualitative agreement with recent EXAFS measurements.
We report a Raman scattering study of six rare earth orthoferrites RFeO3, with R = La, Sm, Eu, Gd, Tb, Dy. The use of extensive polarized Raman scattering of SmFeO3 and first-principles calculations enable the assignment of the observed phonon modes
to vibrational symmetries and atomic displacements. The assignment of the spectra and their comparison throughout the whole series allows correlating the phonon modes with the orthorhombic structural distortions of RFeO3 perovskites. In particular, the positions of two specific Ag modes scale linearly with the two FeO6 octahedra tilt angles, allowing the distortion throughout the series. At variance with literature, we find that the two octahedra tilt angles scale differently with the vibration frequencies of their respective Ag modes. This behavior as well as the general relations between the tilt angles, the frequencies of the associated modes and the ionic radii are rationalized in a simple Landau model. The reported Raman spectra and associated phonon-mode assignment provide reference data for structural investigations of the whole series of orthoferrites.
We present measurements of the thermal expansion coefficient $alpha$ of polycrystalline RFeAsO (R = La,Ce,Pr,Sm,Gd). Anomalies at the magnetic ordering transitions indicate a significant magneto-elastic coupling and a negative pressure dependence of
$T_{rm N}$ . The structural transitions are associated by large anomalies in $alpha$. Rare earth magnetic ordering in CeFeAsO, PrFeAsO, and SmFeAsO yields large positive anomalies at low temperatures.
The effect of rare-earth ion size on the octahedral distortions in rare-earth chromites (RCrO3, R = Lu, Tb, Gd, Eu, Sm) crystallizing in the orthorhombic structure has been studied using Raman scattering and synchrotron powder x-ray diffraction up to
20 GPa. From our studies on RCrO3 we found that the octahedral tilts (distortions) increase with pressure. This is contrary to the earlier report which suggests that in LaCrO3, the distortions decrease with pressure leading to a more ordered phase at high pressure. Here we observe that the rate of increase in distortion decreases with the increase in R-ion radii. This occurs due to the reduction in the compression of RO12 polyhedra with a corresponding increase in the compression of the CrO6 octahedra with increasing R-ion radii. From the Raman studies, we predict a critical R-ion radii, above which we expect the distortions in RCrO3 to reduce with increasing pressure leading to what is observed in the case of LaCrO3. These Raman results are consistent with our pressure dependent structural studies on RCrO3 (R = Gd, Eu, Sm). Also, our results suggest that the pressure dependence of Neel temperature, TNCr, (where the Cr3+ spin orders) in RCrO3 is mostly affected by the compressions of Cr-O bonds rather than the alteration of octahedral tilts.
Part of developing new strategies for fabrications of nanowire structures involves in many cases the aid of metal nanoparticles (NPs). It is highly beneficial if one can define both diameter and position of the initial NPs and make well-defined nanow
ire arrays. This sets additional requirement on the NPs with respect to being able to withstand a pre-growth annealing process (i.e. de- oxidation of the III-V semiconductor surface) in an epitaxy system. Recently, it has been demonstrated that Ag may be an alternative to using Au NPs as seeds for particle-seeded nanowire fabrication. This work brings light onto the effect of annealing of Au, Ag and Au-Ag alloy NP arrays in two commonly used epitaxial systems, the Molecular Beam Epitaxy (MBE) and the Metalorganic Vapor Phase Epitaxy (MOVPE). The NP arrays are fabricated with the aid of Electron Beam Lithography on GaAs 100 and 111B wafers and the evolution of the NPs with respect to shape, size and position on the surfaces are studied after annealing using Scanning Electron Microscopy (SEM). We find that while the Au NP arrays are found to be stable when annealed up to 600 $^{circ}$C in a MOVPE system, a diameter and pitch dependent splitting of the particles are seen for annealing in a MBE system. The Ag NP arrays are less stable, with smaller diameters ($leq$ 50 nm) dissolving during annealing in both epitaxial systems. In general, the mobility of the NPs is observed to differ between the two the GaAs 100 and 111B surfaces. While the initial pattern is found be intact on the GaAs 111B surface for a particular annealing process and particle type, the increased mobility of the NP on the 100 may influence the initial pre-defined positions at higher annealing temperatures. The effect of annealing on Au-Ag alloy NP arrays suggests that these NP can withstand necessary annealing conditions for a complete de-oxidation of GaAs surfaces.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها