Study of Possible Scintillation Mechanism Damage in PbWO4 Crystals After Pion Irradiation

99   0   0.0 ( 0 )
 نشر من قبل Andrey Ryazantsev
 تاريخ النشر 2004
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

We employed two independent methods to study possible damage to the scintillation mechanism in lead tungstate crystals due to irradiation by a 34 GeV pion beam. First, 10 crystals were irradiated simultaneously over 30 hours by a narrow beam, so that only a small region of each crystal was affected. We studied the effect of the irradiation on the light output non-uniformity. If a localized degradation was observed, it would indicate damage to the scintillation mechanism. Secondly, we detected light output using two phototubes attached to sides of a crystal. Since these phototubes detect scintillation light only from a small localized region, the effect of transmission loss should be minimal. We did not see any statistically significant evidence for scintillation mechanism damage with either method. The effect is consistent with zero, and the upper limit is 0.5% at 95% C.L.



قيم البحث

اقرأ أيضاً

69 - V.Batarin , J.Butler , T.Chen 2003
Studies of the radiation hardness of lead tungstate crystals produced by the Bogoroditsk Techno-Chemical Plant in Russia and the Shanghai Institute of Ceramics in China have been carried out at IHEP, Protvino. The crystals were irradiated by a 40-GeV pion beam. After full recovery, the same crystals were irradiated using a $^{137}Cs$ $gamma$-ray source. The dose rate profiles along the crystal length were observed to be quite similar. We compare the effects of the two types of radiation on the crystals light output.
Ensuring the radiation hardness of PbWO4 crystals was one of the main priorities during the construction of the electromagnetic calorimeter of the CMS experiment at CERN. The production on an industrial scale of radiation hard crystals and their cert ification over a period of several years represented a difficult challenge both for CMS and for the crystal suppliers. The present article reviews the related scientific and technological problems encountered.
A Cerium Fluoride crystal produced during early R&D studies for calorimetry at the CERN Large Hadron Collider was exposed to a 24 GeV/c proton fluence Phi_p=(2.78 +- 0.20) x 10EE13 cm-2 and, after one year of measurements tracking its recovery, to a fluence Phi_p=(2.12 +- 0.15) x 10EE14 cm-2. Results on proton-induced damage to the crystal and its spontaneous recovery after both irradiations are presented here, along with some new, complementary data on proton-damage in Lead Tungstate. A comparison with FLUKA Monte Carlo simulation results is performed and a qualitative understanding of high-energy damage mechanism is attempted.
Fast hadrons have been observed to cause a cumulative damage in Lead Tungstate and LYSO crystals. The underlying mechanism has been proven to be the creation of fission tracks, which act as scattering centres, thus reducing the light collection effic iency. For calorimetry applications in an environment where large, fast hadron fluences are anticipated, predictions about damage in crystals are of great importance for making an informed choice of technology. In the study presented here, simulations using the FLUKA package have been performed on Lead Tungstate, LYSO and Cerium Fluoride, and their results have been compared with measurements. The agreement that is found between simulation results and experimental measurements allows to conclude that the damage amplitude in a given material can be predicted with a precision that is sufficient to anticipate the damage expected during detector operation.
This paper is devoted to the study of a degradation of CsI(Tl)crystals scintillation characteristics under irradiation with gamma-quanta at the uniformly distributed absorbed dose up to 3700 rad. The sample set consisted of 25 crystals of 30 cm long having a truncated pyramid shape and 30 rectangular crystals of the same length. A large difference in the light output deterioration caused by the radiation was observed for the samples of the same shape. A substantial dependence of the average light output loss from the sample shape is seen as well. On the other hand, the crystals from the same ingot behave very similarly under irradiation.