We report three-dimensional laser microfabrication, which enables microstructuring of materials on the scale of 0.2-1 micrometers. The two different types of microfabrication demonstrated and discussed in this work are based on holographic recording, and light-induced damage in transparent dielectric materials. Both techniques use nonlinear optical excitation of materials by ultrashort laser pulses (duration < 1 ps).
قيم البحث
اقرأ أيضاً
We report on fabrication of whispering-gallery-mode microlasers in a Nd:glass chip by femtosecond laser three-dimensional (3D) micromachining. Main fabrication procedures include the fabrication of freestanding microdisks supported by thin pillars by
femtosecond laser ablation of the glass substrate immersed in water, followed by CO2 laser annealing for surface smoothing. Lasing is observed at a pump threshold as low as ~69 {mu}W at room temperature with a continuous-wave laser diode operating at 780nm. This technique allows for fabrication of microcavities of high quality factors in various dielectric materials such as glasses and crystals.
The dispersion of index-guiding microstructured polymer optical fibers is calculated for second-harmonic generation. The quadratic nonlinearity is assumed to come from poling of the polymer, which in this study is chosen to be the cyclic olefin copol
ymer Topas. We found a very large phase mismatch between the pump and the second-harmonic waves. Therefore the potential for cascaded quadratic second-harmonic generation is investigated in particular for soliton compression of fs pulses. We found that excitation of temporal solitons from cascaded quadratic nonlinearities requires an effective quadratic nonlinearity of 5 pm/V or more. This might be reduced if a polymer with a low Kerr nonlinear refractive index is used. We also found that the group-velocity mismatch could be minimized if the design parameters of the microstructured fiber are chosen so the relative hole size is large and the hole pitch is on the order of the pump wavelength. Almost all design-parameter combinations resulted in cascaded effects in the stationary regime, where efficient and clean soliton compression can be found. We therefore did not see any benefit from choosing a fiber design where the group-velocity mismatch was minimized. Instead numerical simulations showed excellent compression of $lambda=800$ nm 120 fs pulses with nJ pulse energy to few-cycle duration using a standard endlessly single-mode design with a relative hole size of 0.4.
Nanostructuring hard optical crystals has so far been exclusively feasible at their surface, as stress induced crack formation and propagation has rendered high precision volume processes ineffective. We show that the inner chemical etching reactivit
y of a crystal can be enhanced at the nanoscale by more than five orders of magnitude by means of direct laser writing. The process allows to produce cm-scale arbitrary three-dimensional nanostructures with 100 nm feature sizes inside large crystals in absence of brittle fracture. To showcase the unique potential of the technique, we fabricate photonic structures such as sub-wavelength diffraction gratings and nanostructured optical waveguides capable of sustaining sub-wavelength propagating modes inside yttrium aluminum garnet crystals. This technique could enable the transfer of concepts from nanophotonics to the fields of solid state lasers and crystal optics.
All-optical switching of 77 fs pulses centered at 1560 nm, driven by 270 fs, 1030 nm pulses in a dual-core optical fiber exhibiting high index contrast is presented. The fiber is made of a thermally matched pair of lead silicate and borosilicate glas
ses used as core and cladding material, respectively. The novel switching approach is based on nonlinear balancing of dual-core asymmetry, by control pulse intensity induced group velocity reduction of the fast fiber channel. Due to the fiber core made of soft glass with high nonlinearity high switching contrast exceeding 20 dB is attained under application of control pulses of only few nanojoule energy. The optimization of the fiber length brought the best results at 14 mm, which is in good correspondence with the calculated coupling length at the signal wavelength. The results express significant progress in comparison to similar studies based on self-switching of solitonic pulses in dual-core fibers and represent high application potential.
We exploit inverse Raman scattering and solvated electron absorption to perform a quantitative characterization of the energy loss and ionization dynamics in water with tightly focused near-infrared femtosecond pulses. A comparison between experiment
al data and numerical simulations suggests that the ionization energy of water is 8 eV, rather than the commonly used value of 6.5 eV. We also introduce an equation for the Raman gain valid for ultra-short pulses that validates our experimental procedure.