تسجيل مستخدم جديدHigh Pressure Study of Structural Phase Transitions and Superconductivity in La1.48Nd0.4Sr0.12CuO4
104
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We have determined the crystal structures and superconducting transition temperatures of La1.48Nd0.4Sr0.12CuO4 under nearly hydrostatic pressures in diamond anvil cells to 5.0 GPa and 19.0 GPa, respectively. Synchrotron x-ray powder diffraction measurements were used to establish the pressure-temperature structural phase diagram. Under pressure the superconducting transition temperature increases rapidly from Tc = 3 K to a maximum value of 22 K at 5 GPa, a pressure slightly greater than that required to stabilize the undistorted I4/mmm structure in the superconducting state. Increasing the pressure further to 19 GPa leads to a decrease in Tc to ~12 K. These results are discussed in relation to earlier high pressure measurements for similar materials.
قيم البحث
اقرأ أيضاً
High pressure electrical resistance and x-ray diffraction measurements have been performed on ruthenium-doped Ba(Fe0.9Ru0.1)2As2, up to pressures of 32 GPa and down to temperatures of 10 K, using designer diamond anvils under quasi-hydrostatic condit
ions. At 3.9 GPa, there is an evidence of pressure-induced superconductivity with Tc onset of 24 K and zero resistance at Tc zero of ~14.5 K. The superconducting transition temperature reaches maximum at ~5.5 GPa and then decreases gradually with increase in pressure before completely disappearing above 11.5 GPa. Upon increasing pressure at 200 K, an isostructural phase transition from a tetragonal (I4/mmm) phase to a collapsed tetragonal phase is observed at 14 GPa and the collapsed phase persists up to at least 30 GPa. The changes in the unit cell dimensions are highly anisotropic across the phase transition and are qualitatively similar to those observed in undoped BaFe2As2 parent.
We studied the effect of hydrostatic pressure (P) on the structural phase transitions and superconductivity in the ternary and pseudo-ternary iron arsenides CaFe2As2, BaFe2As2, and (Ba0.55K0.45)Fe2As2, by means of measurements of electrical resistivi
ty (rho) in the 1.8 - 300 K temperature (T) range, pressures up to 20 kbar, and magnetic fields up to 9 T. CaFe2As2 and BaFe2As2 (lightly doped with Sn) display structural phase transitions near 170 K and 85 K, respectively, and do not exhibit superconductivity in ambient pressure, while K-doped (Ba0.55K0.45)Fe2As2 is superconducting for T < 30 K. The effect of pressure on BaFe2As2 is to shift the onset of the crystallographic transformation down in temperature at the rate of about -1.04 K/kbar, while shifting the whole rho(T) curves downward, whereas its effect on superconducting (Ba0.55K0.45)Fe2As2 is to shift the onset of superconductivity to lower temperatures at the rate of about -0.21 K/kbar. The effect of pressure on CaFe2As2 is first to suppress the crystallographic transformation and induce superconductivity with onset near 12 K very rapidly, i.e., for P < 5 kbar. However, higher pressures bring about another phase transformation characterized by reduced resistivity, and the suppression of superconductivity, confining superconductivity to a narrow pressure dome centered near 5 kbar. Upper critical field (Hc2) data in (Ba0.55K0.45)Fe2As2 and CaFe2As2 are discussed.
Recently, natural van der Waals heterostructures of (MnBi2Te4)m(Bi2Te3)n have been theoretically predicted and experimentally shown to host tunable magnetic properties and topologically nontrivial surface states. In this work, we systematically inves
tigate both the structural and electronic responses of MnBi2Te4 and MnBi4Te7 to external pressure. In addition to the suppression of antiferromagnetic order, MnBi2Te4 is found to undergo a metal-semiconductor-metal transition upon compression. The resistivity of MnBi4Te7 changes dramatically under high pressure and a non-monotonic evolution of r{ho}(T) is observed. The nontrivial topology is proved to persists before the structural phase transition observed in the high-pressure regime. We find that the bulk and surface states respond differently to pressure, which is consistent with the non-monotonic change of the resistivity. Interestingly, a pressure-induced amorphous state is observed in MnBi2Te4, while two high pressure phase transitions are revealed in MnBi4Te7. Our combined theoretical and experimental research establishes MnBi2Te4 and MnBi4Te7 as highly tunable magnetic topological insulators, in which phase transitions and new ground states emerge upon compression.
In this study, we succeeded in synthesizing new antiperovskite phosphides $M$Pd$_3$P ($M$ = Ca, Sr, Ba) and discovered the appearance of a superconducting phase (0.17 $leq$ $x$ $leq$ 0.55) in a solid solution (Ca$_{1-x}$Sr$_x$)Pd$_3$P. Three perovski
te-related crystal structures were identified in (Ca$_{1-x}$Sr$_x$)Pd$_3$P and a phase diagram was built on the basis of experimental results. The first phase transition from centrosymmetric ($Pnma$) to non-centrosymmetric orthorhombic ($Aba$2) occurred in CaPd$_3$P near room temperature. The phase transition temperature decreased as Ca$^{2+}$ was replaced with a larger-sized isovalent Sr$^{2+}$. Bulk superconductivity at a critical temperature ($T$$_c$) of approximately 3.5 K was observed in a range of $x$ = 0.17 - 0.55; this was associated with the centrosymmetric orthorhombic phase. Thereafter, a non-centrosymmetric tetragonal phase ($I$41$md$) remained stable for 0.6 $leq$ $x$ $leq$ 1.0, and superconductivity was significantly suppressed as samples with $x$ = 0.75 and 1.0 showed ($T$$_c$) values as low as 0.32 K and 57 mK, respectively. For further substitution with a larger-sized isovalent Ba$^{2+}$, namely (Sr$_{1-y}$Ba$_y$)Pd$_3$P, the tetragonal phase continued throughout the composition range. BaPd$_3$P no longer showed superconductivity down to 20 mK. Since the inversion symmetry of structure and superconductivity can be precisely controlled in (Ca$_{1-x}$Sr$_x$)Pd$_3$P, this material may offer a unique opportunity to study the relationship between inversion symmetry and superconductivity.
At ambient pressure CaFe2As2 has been found to undergo a first order phase transition from a high temperature, tetragonal phase to a low temperature orthorhombic / antiferromagnetic phase upon cooling through T ~ 170 K. With the application of pressu
re this phase transition is rapidly suppressed and by ~ 0.35 GPa it is replaced by a first order phase transition to a low temperature collapsed tetragonal, non-magnetic phase. Further application of pressure leads to an increase of the tetragonal to collapsed tetragonal phase transition temperature, with it crossing room temperature by ~ 1.7 GPa. Given the exceptionally large and anisotropic change in unit cell dimensions associated with the collapsed tetragonal phase, the state of the pressure medium (liquid or solid) at the transition temperature has profound effects on the low temperature state of the sample. For He-gas cells the pressure is as close to hydrostatic as possible and the transitions are sharp and the sample appears to be single phase at low temperatures. For liquid media cells at temperatures below media freezing, the CaFe2As2 transforms when it is encased by a frozen media and enters into a low temperature multi-crystallographic-phase state, leading to what appears to be a strain stabilized superconducting state at low temperatures.