تسجيل مستخدم جديدMicrophase separation in Pr0.67Ca0.33MnO3 by small angle neutron scattering
126
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We have evidenced by small angle neutron scattering at low temperature the coexistence of ferromagnetism (F) and antiferromagnetism (AF) in Pr0.67Ca0.33MnO3. The results are compared to those obtained in Pr0.80Ca0.20MnO3 and Pr0.63Ca0.37MnO3, which are F and AF respectively. Quantitative analysis shows that the small angle scattering is not due to a mesoscopic mixing but to a nanoscopic electronic and magnetic red cabbage structure, in which the ferromagnetic phase exists in form of thin layers in the AF matrix (stripes or 2D sheets).
قيم البحث
اقرأ أيضاً
We have observed a magnetic vortex lattice (VL) in BaFe2(As_{0.67}P_{0.33})2 (BFAP) single crystals by small-angle neutron scattering (SANS). With the field along the c-axis, a nearly isotropic hexagonal VL was formed in the field range from 1 to 16
T, which is a record for this technique in the pnictides, and no symmetry changes in the VL were observed. The temperature-dependence of the VL signal was measured and confirms the presence of (non d-wave) nodes in the superconducting gap structure for measurements at 5 T and below. The nodal effects were suppressed at high fields. At low fields, a VL reorientation transition was observed between 1 T and 3 T, with the VL orientation changing by 45{deg}. Below 1 T, the VL structure was strongly affected by pinning and the diffraction pattern had a fourfold symmetry. We suggest that this (and possibly also the VL reorientation) is due to pinning to defects aligned with the crystal structure, rather than being intrinsic.
Triblock terpolymers exhibit a rich self-organization behavior including the formation of fascinating cylindrical core-shell structures with a phase separated corona. After crystallization-induced self-assembly of polystryrene-(block)-polyethylene-(b
lock)-poly(methyl methacrylate) triblock terpolymers (abbreviated as SEMs = Styrene-Ethylene-Methacrylates) from solution, worm-like core-shell micelles with a patchy corona of polystryrene and poly(methyl methacrylate) were observed by transmission electron microscopy. However, the solution structure is still a matter of debate. Here, we present a method to distinguish in-situ between a Janus-type (two faced) and a patchy (multiple compartments) configuration of the corona. To discriminate between both models the scattering intensity must be determined mainly by one corona compartment. Contrast variation in small-angle neutron scattering enables us to focus on one compartment of the SEMs. The results validate the existence of the patchy structure also in solution.
We report Small-Angle Neutron Scattering (SANS) measurements on the vortex lattice in a PbIn polycrystal in the presence of an applied current. Using the rocking curves as a probe of the distribution of current in the sample, we observe that vortex p
inning is due to the surface roughness. This leads to a surface current that persists in the flux flow region. We show the influence of surface treatments on the distribution of this current.
Small-angle neutron scattering (SANS) from cationic globular micellar solutions composed of sodium dodecyl sulfate (SDS) and in water was studied with contrast variation approach. Extensive computational studies have demonstrated that the distributio
n of invasive water is clearly an important feature for understanding the self-organization of SDS molecules and the stability of assemblies. However, in existing scattering studies the degree of hydration level was not examined explicitly. Here using the scheme of contrast variation, we establish a methodology of SANS to determine the intra-micellar radial dis-tributions of invasive water and SDS molecules from the evolving spectral lineshapes caused by the varying isotopic ratio of water. A detailed description hydration of SDS micelles is provided, which in an excellent agreement with known results of many existing simulations studies. Extension of our method can be used to provide an in-depth insight into the micellization phenomenon which is commonly found in many soft matter systems.
We present studies of the magnetic field distribution around the vortices in LuNi2B2C. Small-angle neutron scattering measurements of the vortex lattice (VL) in this material were extended to unprecedentedly large values of the scattering vector q, o
btained both by using high magnetic fields to decrease the VL spacing and by using higher order reflections. A square VL, oriented with the nearest neighbor direction along the crystalline [110] direction, was observed up to the highest measured field. The first-order VL form factor, |F(q10)|, was found to decrease exponentially with increasing magnetic field. Measurements of the higher order form factors, |F(qhk)|, reveal a significant in-plane anisotropy and also allow for a real-space reconstruction of the VL field distribution.