تسجيل مستخدم جديدHigh performance new MgB2 superconducting hollow wires
104
0
0.0
(
0
)
تأليف
G.Giunchi
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
MgB2 hollow wires have been produced with a new technique which uses a conventional wire manufacturing process but is applied to composite billets containing the elemental B and Mg precursors in an appropriate shape. The technique has been applied to the manufacture of both monofilamentary and multifilamentary wires of several tens meters length. The superconducting transport properties of the MgB2 hollow wires have been measured in magnetic field and in the temperature range from 4.2 to 30 K. Promising results are obtained, which indicate the possibility of application of these wires as superconductors in the temperature range of 15-30 K and at medium-high values of magnetic field.
قيم البحث
اقرأ أيضاً
In DC and AC practical applications of MgB2 superconducting wires an important role is represented by the material sheath which has to provide, among other things, a suitable electrical and thermal stabilization. A way to obtain a large enough amount
of low resistivity material in to the conductor architecture is to use it as external sheath. In this paper we study ex-situ multifilamentary MgB2 wires using oxide-dispersion-strengthened copper (GlidCop) as external sheath in order to reach a good compromise between critical current density and thermal properties. We prepared three GlidCop samples differing by the content of dispersed sub-microscopic Al2O3 particles. We characterized the superconducting and thermal properties and we showed that the good thermal conductivity together the good mechanical properties and a reasonable critical current density make of GlidCop composite wire a useful conductor for applications where high thermal conductivity is request at temperature above 30K, such as Superconducting-FCL.
We have performed microwave measurements on superconducting hot-isostatically- pressed (HIPed) bulk MgB2 using a parallel-plate resonator technique. The high density and strength of the HIPed material allowed preparation of samples with mirror-like s
urfaces for microwave measurements. The microwave surface resistance decreased by about 40% at 20 K when the root-mean-square surface roughness was reduced from 220 nm to 110 nm through surface-polishing and ion-milling. The surface resistance was independent of surface microwave magnetic field at least up to 4 Oe and below 30 K. We attribute this behavior, and the overall low surface resistance (~0.8 mOhms at 10 GHz and 20 K), to the high density of our samples and the absence of weak links between grains.
MgB2 monofilamentary nickel-sheated tapes and wires were fabricated by means of the ex-situ powder-in-tube method using either high-energy ball milled and low temperature synthesized powders. All sample were sintered at 920 C in Ar flow. The milling
time and the revolution speed were tuned in order to maximize the critical current density in field (Jc): the maximum Jc value of 6 x 10e4 A/cm2 at 5 K and 4 T was obtained corresponding to the tape prepared with powders milled for 144h at 180rpm. Vorious synthesis temperature were also investigated (730-900 C) finding a best Jc value for the wire prepared with powders synthesized at 745 C. We speculate that this optimal temperature is due to the fluidifying effect of unreacted magnesium content before the sintering process which could better connect the grains.
The d-wave symmetry of the superconducting order in the cuprate high temperature superconductors is a well established fact, and one which identifies them as unconventional. However, in macroscopic contexts -- including many potential applications ({
it i.e.} superconducting wires) -- the material is a composite of randomly oriented superconducting grains in a metallic matrix, in which Josephson coupling between grains mediates the onset of long-range phase coherence. Here, we analyze the physics at length scales large compared to the size of such grains, and in particular the macroscopic character of the long-range order that emerges. While XY-glass order and macroscopic d-wave superconductivity may be possible, we show that under many circumstances -- especially when the d-wave superconducting grains are embedded in a metallic matrix -- the most likely order has global s-wave symmetry.
We report on the superconducting performance of the ex-situ SiC doped MgB2 monofilamentary tapes. Polycrystalline powders of MgB2 doped with 5 and 10 wt% SiC were synthesized by conventional solid-state reaction route and characterized for their supe
rconducting performance. It is found that superconducting parameters i.e. upper critical field (Hc2), irreversibility field (Hirr) and critical current density (Jc) are all improved significantly with SiC addition. Also it was found that relatively lower synthesis temperature (700 C) resulted in further improved superconducting parameters. As synthesized powders are used for ex-situ powder-in-tube (PIT) monofilamentary tapes and superconducting parameters are determined. Albeit the superconducting transition temperature (Tc) is decreased slightly (2K) for SiC doped tapes, the superconducting performance in terms of critical current density (Jc), being determined from both magnetization and transport measurements, is improved significantly. In particular the SiC doped and 700 {deg}C synthesized MgB2 tapes exhibited the transport Jc of nearly 10^4 A/cm2 under applied fields of as high as 7 Tesla. Further it is found that the Jc anisotropy decreases significantly for SiC doped tapes. Disorder due to substitution of C at B site being created from broken SiC and the presence of nano SiC respectively in SiC added ex-situ MgB2 tapes are responsible for decreased anisotropy and improved Jc(H) performance.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها