Pure spin current based research is mostly focused on ferromagnet (FM)/heavy metal (HM) system. Because of the high spin orbit coupling (SOC) these HMs exhibit short spin diffusion length and therefore possess challenges for device application. Low SOC (elements of light weight) and large spin diffusion length make the organic semiconductors (OSCs) suitable for future spintronic applications. From theoretical model it is explained that, due to $pi$ - $sigma$ hybridization the curvature of the C$_{60}$ molecules may increase the SOC strength. Here, we have investigated spin pumping and inverse spin hall effect (ISHE) in CoFeB/C$_{60}$ bilayer system using coplanar wave guide based ferromagnetic resonance (CPW-FMR) set-up. We have performed angle dependent ISHE measurement to disentangle the spin rectification effects for example anisotropic magnetoresistance, anomalous Hall effect etc. Further, effective spin mixing conductance (g$_{eff}^{uparrowdownarrow}$) and spin Hall angle ($theta_{SH}$) for C$_{60}$ have been reported here. The evaluated value for $theta_{SH}$ is 0.055.
قيم البحث
اقرأ أيضاً
High spin to charge conversion efficiency is the requirement for the spintronics devices which is governed by spin pumping and inverse spin Hall effect (ISHE). In last one decade, ISHE and spin pumping are heavily investigated in ferromagnet/ heavy m
etal (HM) heterostructures. Recently antiferromagnetic (AFM) materials are found to be good replacement of HMs because AFMs exhibit terahertz spin dynamics, high spin-orbit coupling, and absence of stray field. In this context we have performed the ISHE in CoFeB/ IrMn heterostructures. Spin pumping study is carried out for $Co_{40}Fe_{40}B_{20} (12 nm)/ Cu (3 nm)/ Ir_{50}Mn_{50} (t nm)/ AlO_{x} (3 nm)$ samples where textit{t} value varies from 0 to 10 nm. Damping of all the samples are higher than the single layer CoFeB which indicates that spin pumping due to IrMn is the underneath mechanism. Further the spin pumping in the samples are confirmed by angle dependent ISHE measurements. We have also disentangled other spin rectifications effects and found that the spin pumping is dominant in all the samples. From the ISHE analysis the real part of spin mixing conductance (textit{$g_{r}^{uparrow downarrow}$}) is found to be 0.704 $pm$ 0.003 $times$ $10^{18}$ $m^{-2}$.
An intriguing feature of spintronics is the use of pure spin-currents to manipulate magnetization, e.g., spin-currents can switch magnetization in spin-torque MRAM, a next-generation DRAM alternative. Giant spin-currents via the spin Hall effect grea
tly expand the technological opportunities. Conversely, a ferromagnet/normal metal junction emits spin-currents under microwave excitation, i.e. spin-pumping. While such spin-currents are modulated at the excitation frequency, there is also a non-linear, rectified component that is commonly detected using the corresponding inverse spin Hall effect (iSHE) dc voltage. However, the ac component should be more conducive for quantitative analysis, as it is up to two orders of magnitude larger and linear. But any device that uses the ac iSHE is also sensitive to inductive signals via Faradays Law and discrimination of the ac iSHE signal must rely on phase-sensitive measurements. We use the inductive signal as a reference for a quantitative measurement of the magnitude and phase of the ac iSHE.
The dependence of the spin-pumping effect on the yttrium iron garnet (Y3Fe5O12, YIG) thickness detected by the inverse spin Hall effect (ISHE) has been investigated quantitatively. Due to the spin-pumping effect driven by the magnetization precession
in the ferrimagnetic insulator YIG film a spin-polarized electron current is injected into the Pt layer. This spin current is transformed into electrical charge current by means of the ISHE. An increase of the ISHE-voltage with increasing film thickness is observed and compared to the theoretically expected behavior. The effective damping parameter of the YIG/Pt samples is found to be enhanced with decreasing YIG film thickness. The investigated samples exhibit a spin mixing conductance of g=(7.43 pm 0.36) times 10^{18} m^{-2} and a spin Hall angle of theta_{ISHE} = 0.009 pm 0.0008. Furthermore, the influence of nonlinear effects on the generated voltage and on the Gilbert damping parameter at high excitation powers are revealed. It is shown that for small YIG film thicknesses a broadening of the linewidth due to nonlinear effects at high excitation powers is suppressed because of a lack of nonlinear multi-magnon scattering channels. We have found that the variation of the spin-pumping efficiency for thick YIG samples exhibiting pronounced nonlinear effects is much smaller than the nonlinear enhancement of the damping.
The polarization of the spin current pumped by a precessing ferromagnet into an adjacent normal metal has a constant component parallel to the precession axis and a rotating one normal to the magnetization. The former component is now routinely detec
ted in the form of a DC voltage induced by the inverse spin Hall effect (ISHE). Here we compute AC-ISHE voltages much larger than the DC signals for various material combinations and discuss optimal conditions to observe the effect. Including the backflow of spins is essential for distilling parameters such as the spin Hall angle from ISHE-detected spin pumping experiments.
We have measured the inverse spin Hall effect (ISHE) in textit{n}-Ge at room temperature. The spin current in germanium was generated by spin pumping from a CoFeB/MgO magnetic tunnel junction in order to prevent the impedance mismatch issue. A clear
electromotive force was measured in Ge at the ferromagnetic resonance of CoFeB. The same study was then carried out on several test samples, in particular we have investigated the influence of the MgO tunnel barrier and sample annealing on the ISHE signal. First, the reference CoFeB/MgO bilayer grown on SiO$_{2}$ exhibits a clear electromotive force due to anisotropic magnetoresistance and anomalous Hall effect which is dominated by an asymmetric contribution with respect to the resonance field. We also found that the MgO tunnel barrier is essential to observe ISHE in Ge and that sample annealing systematically lead to an increase of the signal. We propose a theoretical model based on the presence of localized states at the interface between the MgO tunnel barrier and Ge to account for these observations. Finally, all of our results are fully consistent with the observation of ISHE in heavily doped $n$-Ge and we could estimate the spin Hall angle at room temperature to be $approx$0.001.