Octapod-shaped CdSe nanocrystals hosting Pt with high-mass activity for the hydrogen evolution reaction

168   0   0.0 ( 0 )
 نشر من قبل Sebastiano Bellani
 تاريخ النشر 2020
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

The design of efficient electrocatalysts for electrochemical water splitting with minimal amount of precious metal is crucial to attain renewable and sustainable energy conversion. Here, we report the use of a network of CdSe branched colloidal nanocrystals, made of a CdSe core and eight CdSe pods (so-called octapods), able to host on their pods Pt particles, and thus catalyzing water splitting reactions. Thanks to the octapod shape, the resulting Pt-hosting network is mechanically trapped onto carbon nanotube buckypaper, providing mechanically flexible and binder-free electrodes. We found that such hierarchical configuration maximizes the mass activity and the utilization efficiency of Pt for the hydrogen evolution reaction (HER). At a potential of -0.15 V vs. reversible hydrogen electrode, the Pt/octapod network-based electrodes display a Pt mass activity on the HER of 166 A mg-1 and 42 A mg-1 in acidic and alkaline media, respectively. These values correspond to turnover frequencies of 168 s-1 and 42 s-1, respectively, which are in that order 14 and 21 times higher compared to commercially available Pt/C benchmarks. The strong chemical and mechanical interactions between the Pt and the octapod surface, along with pod-aided adhesion of the Pt/octapod network to the buckypaper, result in a long-term durability (>20 h) of the HER-activity in both media. These results experimentally prove that the exploitation of our network of branched nanocrystals hosting Pt particles can circumvent the durability issues of the catalysts while adopting either ultralow Pt loadings or benchmarking carbon-supported Pt nanocrystals. Our work opens up prospects for using porous networks made by branched nanocrystals as catalysts with ultralow amount of noble metals and controlled catalytic properties.



قيم البحث

اقرأ أيضاً

Two-dimensional (2D) boron monolayers have been successfully synthesized on silver substrate very recently. Their potential application is thus of great significance. In this work, we explore the possibility of boron monolayers (BMs) as electrocataly sts for hydrogen evolution reaction (HER) by first-principle method. Our calculations show that the BMs are active catalysts for HER with nearly zero free energy of hydrogen adsorption, metallic conductivity and plenty of active sites in the basal plane. The effect of the substrate on the HER activity is further assessed. It is found that the substrate has a positive effect on the HER performance caused by the competitive effect of mismatch strain and charge transfer. The indepth understanding of the structure dependent HER activity is also provided.
Defined substoichiometric titanium oxides (Ti$_x$O$_{2x-1}$ with $3 < x < 10$) called Magneli phases have been investigated mostly for their unusual high conductivity and metal-like behavior. In photocatalysis, Magneli phase containing titania partic les have been reported to provide favorable charge separation resulting in enhanced reaction efficiency. In the current work we describe a one-step synthesis of Magneli-containing mixed phase nanoparticles that carry directly integrated minute amounts of Pt. Phase optimized nanoparticles that contain only a few hundred ppm Pt are very effective photocatalysts for H$_2$ evolution (they provide a 50-100 times higher H$_2$ evolution than plain anatase loaded with a similar amount of Pt). These photocatalysts are synthesized in a setup combining a hot-wall reactor that is used for TiOx synthesis with a spark generator producing Pt nanoparticles. Different reactor temperatures result in various phase ratios between anatase and Magneli phases. The titania nanoparticles (ca. 24 - 53 nm) were characterized using XRD, HRTEM, XPS and EPR spectra as well as ICP-OES analysis. The best photocatalyst prepared at 900$^circ$C (which consists of mixed phase particles of 32% anatase, 11% rutile and 57% Magneli phases loaded with 290 ppm of Pt) can provide a photocatalytic H$_2$ evolution rate of ca. 5432 micromol h$^{-1} g$^{-1}$ for UV and ca. 1670 micromol h$^{-1} g$^{-1}$ for AM1.5 illumination. For powders converted to higher amounts of Magneli phases (1000$^circ$C and 1100$^circ$C), a drastic loss of the photocatalytic H$_2$ generation activity is observed. Thus, the high photocatalytic efficiency under best conditions is ascribed to an effective synergy between multi-junctions of Magneli titania and Pt that enable a much more effective charge separation and reaction than conventional Pt/anatase junctions.
Understanding the role of elastic strain in modifying catalytic reaction rates is crucial for catalyst design, but experimentally, this effect is often coupled with a ligand effect. To isolate the strain effect, we have investigated the influence of externally applied elastic strain on the catalytic activity of metal films towards the hydrogen evolution reaction (HER). We show that elastic strain tunes the catalytic activity in a controlled and predictable way. Both theory and experiment show strain controls reactivity in a controlled manner consistent with the qualitative predictions of the HER volcano plot and the d-band theory: Ni and Pt activity were accelerated by compression, while Cu activity was accelerated by tension. By isolating the elastic strain effect from the ligand effect, this study provides a greater insight into the role of elastic strain in controlling electrocatalytic activity.
Electrocatalytic hydrogen evolution reaction (HER) in alkaline media is a promising electrochemical energy conversion strategy. Ruthenium (Ru) is an efficient catalyst with a desirable cost for HER, however, the sluggish H2O dissociation process, due to the low H2O adsorption on its surface, currently hampers the performances of this catalyst in alkaline HER. Herein, we demonstrate that the H2O adsorption improves significantly by the construction of Ru-O-Mo sites. We prepared Ru/MoO2 catalysts with Ru-O-Mo sites through a facile thermal treatment process and assessed the creation of Ru-O-Mo interfaces by transmission electron microscope (TEM) and extended X-ray absorption fine structure (EXAFS). By using Fourier-transform infrared spectroscopy (FTIR) and H2O adsorption tests, we proved Ru-O-Mo sites have tenfold stronger H2O adsorption ability than that of Ru catalyst. The catalysts with Ru-O-Mo sites exhibited a state-of-the-art overpotential of 16 mV at 10 mA cm-2 in 1 M KOH electrolyte, demonstrating a threefold reduction than the previous bests of Ru (59 mV) and commercial Pt (31 mV) catalysts. We proved the stability of these performances over 40 hours without decline. These results could open a new path for designing efficient and stable catalysts.
In this work, we demonstrate that a well-established and facile ball milling approach using mixtures of commercial anatase nanoparticles and TiH2 introduces noble-metal-free photocatalytic H2 activity to titania. We characterize this synergistic effe ct in view of the nature of defects, state of hydroxylation, and investigate the effect on the energetics and kinetics of electronic states and the resulting H2 evolution performance.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا