تسجيل مستخدم جديدSlip-hydride interactions in Zircaloy-4: Multiscale mechanical testing and characterisation
87
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
The interactions between {delta}-hydrides and plastic slip in a commercial zirconium alloy, Zircaloy-4, under stress were studied using in situ secondary electron microscope (SEM) micropillar compression tests of single crystal samples and ex situ digital image correlation (DIC) macroscale tensile tests of polycrystalline samples. The hydrides decorate near basal planes in orientation, and for micropillars orientated for <a> basal slip localised shear at the hydride-matrix interface is favoured over slip in {alpha}-Zr matrix due to a lower shear stress required. In contrast, for pillars oriented for <a> prismatic slip the shear stress needed to trigger plastic slip within the hydride is slightly higher than the critical resolved shear stress (CRSS) for the <a> prismatic slip system. In this case, slip in the hydride is likely achieved through <110>-type shear which is parallel to the activated <a>-type shear in the parent matrix. At a longer lengthscale, these results are used to inform polycrystalline samples analysed using high spatial resolution DIC. Here localised interface shear remains to be a significant deformation path which can both cause and be caused by matrix slip on planes closely-oriented to the phase boundaries. Matrix slip on planes nearly perpendicular to the adjacent hydride-matrix interfaces can either result in plastic slip within the hydrides or get arrested at the interfaces, generating local stress concentration. Through these mechanisms, the presence of {delta}-hydrides leads to enhanced strain localisation in Zircaloy-4 early in the plastic regime.
قيم البحث
اقرأ أيضاً
The long-term safety of water-based nuclear reactors relies in part on the reliability of zirconium-based nuclear fuel. Yet the progressive ingress of hydrogen during service makes zirconium alloys subject to delayed hydride cracking. Here, we use a
combination of electron back-scattered diffraction and atom probe tomography to investigate specific microstructural features from the as-received sample and in the blocky-alpha microstructure, before and after electrochemical charging with hydrogen or deuterium followed by a low temperature heat treatment at 400C for 5 hours followed by furnace cooling at a rate of 0. 5C per min. Specimens for atom probe were prepared at cryogenic temperature to avoid the formation of spurious hydrides. We report on the compositional evolution of grains and grain boundaries over the course of the samples thermal history, as well as the ways the growth of the hydrides modifies locally the composition and the structure of the alloy. We observe a significant amount of deuterium left in the matrix, even after the slow cooling and growth of the hydrides. Stacking faults form ahead of the growth front and Sn segregates at the hydride-matrix interface and on these faults. We propose that this segregation may facilitate further growth of the hydride. Our systematic investigation enables us discuss how the solute distribution affects the evolution of the alloys properties during its service lifetime.
Crystal-level strain rate sensitivity and temperature sensitivity are investigated in Zircaloy-4 using combined of bending creep test, digital image correlation, electron backscatter detection and thermo-mechanical tensile tests with crystal plastici
ty modelling. Crystal rate-sensitive properties are extracted from room temperature microscale creep, and temperature sensitivity from thermal polycrystalline responses. Crystal plasticity results show that large microscale creep strain is observed near notch tip increased up to 50% due to cross-slip activation. Grain-level microscale SRS is highly heterogeneous, and its crystallographic sensitivity is dependent on plastic deformation rate and underlying grain-based dislocation slip activation. Pyramidal <c+a> slip and total dislocation pileups contribute to temperature-sensitive texture effect on yielding and strength hardening. A faithful reconstruction of polycrystal and accurate rate-sensitive single-crystal properties are the key to capture multi-scale SRSs.
Atomically thin boron nitride (BN) nanosheets are important two-dimensional nanomaterials with many unique properties distinct from those of graphene, but the investigation of their mechanical properties still greatly lacks. Here we report that high-
quality single-crystalline mono- and few-layer BN nanosheets are one of the strongest electrically insulating materials. More intriguingly, few-layer BN shows mechanical behaviors quite different from those of few-layer graphene under indentation. In striking contrast to graphene, whose strength decreases by more than 30% when the number of layers increases from 1 to 8, the mechanical strength of BN nanosheets is not sensitive to increasing thickness. We attribute this difference to the distinct interlayer interactions and hence sliding tendencies in these two materials under indentation. The significantly better mechanical integrity of BN nanosheets makes them a more attractive candidate than graphene for several applications, e.g. as mechanical reinforcements.
Here we report targeted high-pressure synthesis of two novel high-$T_C$ hydride superconductors, $P6_3/mmc$-$ThH_9$ and $Fmbar{3}m$-$ThH_{10}$, with the experimental critical temperatures ($T_C$) of 146 K and 159-161 K and upper critical magnetic fie
lds ($mu$$H_C$) 38 and 45 Tesla at pressures 170-175 Gigapascals, respectively. Superconductivity was evidenced by the observation of zero resistance and a decrease of $T_C$ under external magnetic field up to 16 Tesla. This is one of the highest critical temperatures that has been achieved experimentally in any compounds, along with such materials as $LaH_{10}$, $H_3S$ and $HgBa_2Ca_xCu_2O_{6+z}$. Our experiments show that $fcc$-$ThH_{10}$ has stabilization pressure of 85 GPa, making this material unique among all known high-$T_C$ metal polyhydrides. Two recently predicted Th-H compounds, $I4/mmm$-$ThH_4$ (> 86 GPa) and $Cmc2_1$-$ThH_6$ (86-104 GPa), were also synthesized. Equations of state of obtained thorium polyhydrides were measured and found to perfectly agree with the theoretical calculations. New phases were examined theoretically and their electronic, phonon, and superconducting properties were calculated.
Atomic and electronic structures of Cu2H and CuH have been investigated by high pressure NMR spectroscopy, X-ray diffraction and ab-initio calculations. Metallic Cu2H was synthesized at a pressure of 40 GPa, and semi-metallic CuH at 90 GPa, found sta
ble up to 160 GPa. Experiments and computations suggest the formation of a metallic 1H-sublattice as well as a high 1H mobility of ~10-7 cm2/s in Cu2H. Comparison of Cu2H and FeH data suggests that deviations from Fermi gas behavior, formation of conductive hydrogen networks, and high 1H mobility could be common features of metal hydrides.