A high temperature W$_2$B cermet for compact neutron shielding

78   0   0.0 ( 0 )
 نشر من قبل Michail Athanasakis
 تاريخ النشر 2019
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

We have developed a new material for neutron shielding applications where space is restricted. W$_2$B is an excellent attenuator of neutrons and gamma-rays, due to the combined gamma attenuation of W and neutron absorption of B. However, its low fracture toughness (~3.5 MPa$cdot$m$^{0.5}$) and high melting point (2670 {deg}C) prevent the fabrication of large fully-dense monolithic parts with adequate mechanical properties. Here we meet these challenges by combining W$_2$B with a minor fraction (43 vol.%) of metallic W. The material was produced by reaction sintering W and BN powders. The mechanical properties under flexural and compressive loading were determined up to 1900 {deg}C. The presence of the ductile metallic W phase enabled a peak flexural strength of ~950 MPa at 1100 {deg}C, which is a factor of 2-3 higher than typical monolithic transition-metal borides. Its ductile-brittle transition temperature of ~1000 {deg}C is typical of W-based composites, which is surprising as the W phase was the minor constituent and did not appear to form a fully continuous network. Compression tests showed hardening below ~1500 {deg}C and significant elongation of the phase domains, which suggest that by forging or rolling, further improvements in ductility may be possible.



قيم البحث

اقرأ أيضاً

Systematic studies of the two high-temperature monolayer oxygen structures that exist on the (110) tungsten surface were performed using low-energy electron microscopy and diffraction measurements. Our work questions the commonly accepted interpretat ion from the literature that striped oxygen superstructures arise from alternating site-exchanged (S-E) domains. We postulate that the superstructures originate from a misfit between tungsten and oxygen lattices while the striped appearance corresponds to a moire pattern. Moreover, we show that the two structures, indicated as 113- and 337-phases due to the characteristic directions of the respective moire patterns, differ considerably in their symmetry properties. This suggests that oxygen atoms in the two overlayers occupy different adsorption sites on average. In particular, the 113-phase features rotational domains that retain mirror symmetries with respect to the [001] and [1-10] directions, whereas the 337-phase is characterized by the appearance of additional domains due to the breaking of these symmetries. We propose structural models for both phases that consistently explain their unusual properties and suggest a universal mechanism for the thermal evolution of oxygen monolayer adsorbed on W(110).
Bimetal transition iodides in two-dimensional scale provide an interesting idea to combine a set of single-transition-metal ferromagnetic semiconductors together. Motivated by structural engineering on bilayer CrI$_3$ to tune its magnetism and works that realize ideal properties by stacking van der Waals transitional metal dichalcogenides in a certain order. Here we stack monolayer VI$_3$ onto monolayer CrI$_3$ with a middle-layer I atoms discarded to construct monolayer V$_2$Cr$_2$I$_9$. Based on this crystal model, the stable and metastable phases are determined among 7 possible phases by first-principles calculations. It is illustrated that both the two phases have Curie temperature $sim$ 6 (4) times higher than monolayer CrI$_3$ and VI$_3$. The reason can be partly attributed to their large magnetic anisotropy energy (the maximum value reaches 412.9 $mu$eV/atom). More importantly, the Curie temperature shows an electric field and strain dependent character and can even surpass room temperature under a moderate strain range. At last, we believe that the bimetal transition iodide V$_2$Cr$_2$I$_9$ monolayer would support potential opportunities for spintronic devices.
X-ray diffraction and Raman scattering measurements, and first-principles calculations are performed to search for the formation of NaCl-hydrogen compound. When NaCl and H$_{2}$ mixture is laser-heated to above 1500 K at pressures exceeding 40 GPa, w e observed the formation of NaClH$_{textit{x}}$ with $textit{P}$6$_{3}$/$textit{mmc}$ structure which accommodates H$_{2}$ molecules in the interstitial sites of NaCl lattice forming ABAC stacking. Upon the decrease of pressure at 300 K, NaClH$_textit{x}$ remains stable down to 17 GPa. Our calculations suggest the observed NaClH$_{textit{x}}$ is NaCl(H$_{2}$). Besides, a hydrogen-richer phase NaCl(H$_{2}$)$_{4}$ is predicted to become stable at pressures above 40 GPa.
We investigated low energy nuclear spin excitations in the layered compound CoCl$_2$ by high resolution back-scattering neutron spectroscopy. We detected inelastic peaks at $E = 1.34 pm 0.03$ $mu$eV on both energy loss and energy sides of the central elastic peak at $T = 2$ K. The energy of the inelastic peaks decrease with temperature continuously and become zero at $T_N approx 25$ K at which the two ielastic peaks merge with the central elastic peak. We interpret the low energy excitations to be due to the transition between hyperfine field split nuclear levels. The present data together with the data on other Co compounds show that the energy of the nuclear spin excitations of a number of compounds follow a linear relationship with the electronic magnetic moment of the Co ion whereas that of other compounds deviate appreciably from this linear behaviour. We ascribe this anomalous behaviour to the presence of unquenched orbital moments of the Co ions.
We report inelastic neutron scattering measurements of the phonon spectra in a pure powder sample of the multiferroic material BiFeO3. A high-temperature range was covered to unravel the changes in the phonon dynamics across the Neel (T_N ~ 650 K) an d Curie (T_C ~ 1100 K) temperatures. Experimental results are accompanied by ab-initio lattice dynamical simulations of phonon density of states to enable microscopic interpretations of the observed data. The calculations reproduce well the observed vibrational features and provide the partial atomic vibrational components. Our results reveal clearly the signature of three different phase transitions both in the diffraction patterns and phonon spectra. The phonon modes are found to be most affected by the transition at the T_C. The spectroscopic evidence for the existence of a different structural modification just below the decomposition limit (T_D ~ 1240 K) is unambiguous indicating strong structural changes that may be related to oxygen vacancies and concomitant Fe3+ to Fe2+ reduction and spin transition.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا