تسجيل مستخدم جديدCrystal structure, cobalt and iron speciation and oxygen non-stoichiometry of La0.6Sr0.4Co1-yFeyO3-d nanorods for IT-SOFC cathodes
60
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Single-phased La0.6Sr0.4Co1-yFeyO3-d (y = 0.2, 0.5, 0.8) nanorods exhibiting the rhombohedral perovskite-type phase were synthesized by a pore-wetting technique. We studied their chemical composition, crystal and electronic structures, morphology and hyperfine properties as a function of the Co/Fe content of the samples. Our results demonstrate that Co cations exhibit a slightly lower oxidation state than Fe ones, resulting in a higher oxygen non-stoichiometry d for Co-rich samples. In addition, the values of d determined in this work for nanostructured samples are much higher than those reported in the literature for bulk materials. This can be attributed to the high degree of defects in nanomaterials and is probably one important factor in the high electrochemical performance for the oxygen reduction reaction of nanostructured La0.6Sr0.4Co1-yFeyO3-d IT-SOFC cathodes, which have been reported in a previous work. Keywords: electrode materials; nanostructured materials; X-ray diffraction; NEXAFS; Mossbauer spectroscopy
قيم البحث
اقرأ أيضاً
We evaluated for the first time the use of nanostructured layered perovskites of formulae LnBaCo2O6-d with Ln = Sm and Gd (SBCO and GBCO, respetively) as SOFC cathodes, finding promising electrochemical properties in the intermediate temperature rang
e (~700{deg}C). The synthesis of these nanomaterials, not reported before, was achieved by using porous templates to confine the chemical reagents in regions of about 200 nm and 800 nm. The performance of nanostructured SBCO and GBCO cathodes for the oxygen reduction reaction was analyzed in symmetrical cells using Gd2O3-doped CeO2 (GDC) as electrolyte. For this purpose, nanostructured SBCO and GBCO cathodes were deposited on both sides of the electrolyte by a simple thick-film procedure and evaluated by Electrochemical Impedance Spectroscopy technique under different operating conditions. We found that cathodes synthesized using smaller template pores exhibited better performance. Besides, SBCO cathodes displayed lower area-specific resistance than GBCO ones.
Inelastic neutron scattering was employed to study the crystal-field interaction in the strontium-doped rare-earth compounds R(x)Sr(1-x)CoO(3-z) (R=Pr, Nd, Ho, and Er). Particular emphasis is laid on the effect of oxygen deficiencies which naturally
occur in the synthesis of these compounds. The observed energy spectra are found to be the result of a superposition of crystal fields with different nearest-neighbor oxygen coordination at the R sites. The experimental data are interpreted in terms of crystal-field parameters which behave in a consistent manner through the rare-earth series, thereby allowing a reliable extrapolation for rare-earth ions not considered in the present work.
We have investigated the effect of synthesis and growth conditions on the magnetic, structural, and compositional properties of pyrochlore oxide holmium titanate and demonstrate a method for growing high quality stoichiometric single crystals. A seri
es of polycrystalline samples with various contents of Ti (-0.08 leqslant x leqslant 0.08, and nominal compositions of Ho2Ti2+xO7) were synthesized at different temperatures, and characterized using powder X-ray diffraction. The results show that synthesizing powders at a higher temperature of 1500 {deg}C yield single phase compounds. Ti deficient powders showed an increase of lattice constant due to stuffing (Ho into Ti positions), while Ti rich powders showed a decrease in lattice constant due to anti-stuffing (Ti into Ho positions). A post annealing in O2 was found to be necessary to accomplish the anti-stuffing process. Use of the conventional floating zone (FZ) technique introduced Ti deficiency, stuffing, and oxygen vacancies in the grown crystal. Growth of high structural quality and stoichiometric single crystals of Ho2Ti2O7 by the traveling solvent floating zone (TSFZ) is reported. AC susceptibility measurements revealed that the stoichiometric crystal shows a higher ice freezing temperature, indicating that crystal quality and stoichiometry play a key role on low temperature spin ice properties of this compound.
The effect of oxygen content on the magnetic and transport properties of the ferromagnetic Eu0.9Ca0.1BaCo2O5.5+{delta} has been carried out. Unlike the increase in TC with calcium content, paradoxally the TC value decreases with the increase in oxyge
n (Co4+) content as observed in the undoped phase. This result unveils the hidden generic magnetic feature of the LnBaCo2O5.5 system in the calcium doped phase. This behaviour supports strongly the appearance of Co3+ disproportion action into Co4+ and Co2+ and the magnetic phase separation scenario of ferromagnetic domains embedded in an antiferromagnetic matrix. All the samples covering a wide range of oxygen content, exhibit a p-type conductivity.
We report results of simultaneous x-ray reflectivity and grazing incidence x-ray fluorescence measurements in combination with x-ray standing wave assisted depth resolved near edge x-ray absorption measurements to reveal new insights on chemical spec
iation of W in a W-B4C superlattice structure. Interestingly, our results show existence of various unusual electronic states for the W atoms especially those sitting at the surface and interface boundary of a thin film medium as compared to that of the bulk. These observations are found to be consistent with the results obtained using first principles calculations. Unlike the conventional x-ray absorption measurements the present approach has an advantage that it permits the determination of depth resolved chemical nature of an element in the thin layered materials at atomic length scale resolutions.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها