The effect of magnetron power on the room temperature 1.54 $mu$m infra-red photoluminescence intensity of erbium doped AlN films grown by r. f. magnetron sputtering, has been studied. The AlN:Er thin films were deposited on (001) Silicon substrates. The study presents relative photoluminescence intensities of nanocrystallized samples prepared with identical sputtering parameters for two erbium doping levels (0.5 and 1.5 atomic %). The structural evolution of the crystallites as a function of the power is followed by transmission electron microscopy. Copyright line will be provided by the publisher 1 Introduction For some time now, rare-earth (RE)-doped semiconductors represent significant potential applications in the field of opto-electronic technology. Part of this technological interest relies on the shielded 4f levels of the RE ions as they give rise to sharp and strong luminescence peaks [1-5]. Among the RE elements, Er is preferred to its counterparts since the Er ions can produce both visible light at 558 nm (green, one of the primary colours) and IR light at 1.54 $mu$m whose spectrum region coincides with the main low-loss region in the absorption spectrum of silica-based optical fibres, combining so potential applications towards photonic devices and towards optical communication devices operating in the infrared domain. These interesting emissions can however only be exploited when placed into host matrixes. On one side, the shielding of the intra 4f levels prevents the shifting of the RE 3+ energy levels and ensures the frequency emission stability. Moreover the intra 4f transitions are parity forbidden for the isolated ions. Matrixes can render the Er 3+ ions optically active, via a relaxation of selection rules due to crystal field effects. As silicon based materials were tested in the 1960s to the 90s with no clear industrial success it was found that the
Er-doped aluminum nitride films, containing different Er concentrations, were obtained at room temperature by reactive radio frequency magnetron sputtering. The prepared samples show a nano-columnar microstructure and the size of the columns is depen
In the prospect of understanding the photoluminescence mechanisms of AlN films doped with erbium and targeting photonic applications we have synthesized non doped and Er-doped AlN films with different crystallized nanostructures by using PVD magnetro
Nanocrystalline n-AlN:Er thin films were deposited on (001) Silicon substrates by r. f. magnetron sputtering at room temperature to study the correlation between 1.54 $mu$m IR photoluminescence (PL) intensity, AlN crystalline structure and Er concent
In this work, we studied phase formation, structural and magnetic properties of iron-nitride (Fe-N) thin films deposited using high power impulse magnetron sputtering (HiPIMS) and direct current magnetron sputtering (dc-MS). The nitrogen partial pres
Rare-earth (R) nickelates (such as perovskite RNiO3, trilayer R4Ni3O10, and infinite layer RNiO2) have attracted tremendous interest very recently. However, unlike widely studied RNiO3 and RNiO2 films, the synthesis of trilayer nickelate R4Ni3O10 fil