It is thought that growing large, oriented grains of perovskite can lead to more efficient devices. We study MAPbI3 films fabricated via Flash Infrared Annealing (FIRA) consisting of highly oriented, large grains. Domains observed in the SEM are often misidentified with crystallographic grains, but SEM images dont provide diffraction information. We measure the grain size, crystal structure and grain orientation using Electron Back-Scattered Diffraction (EBSD) and we study how these affect the optoelectronic properties as characterized by local photoluminescence (PL) and time-resolved microwave conductivity measurements (TRMC). We find a spherulitic growth yielding large (tens of micron), highly oriented grains along the (112) and (400) planes in contrast to randomly oriented, smaller (400 nm) grains observed in films fabricated via conventional antisolvent (AS) dripping. We observe a local enhancement and shift of the photoluminescence emission at different regions of the FIRA clusters, but these can be explained with a combination of light-outcoupling and self-absorption. We observe no effect of crystal orientation on the optoelectronic properties. Additionally, despite a substantial difference in grain size between our FIRA sample and a conventional AS sample, we find similar photoluminescence and charge carrier mobilities and lifetime for the two films. These findings show that the optoelectronic quality is not necessarily related to the orientation and size of crystalline domains in perovskite films indicating that fabrication requirements may be more relaxed for perovskites.
Previous theoretical calculations show azetidinium has the right radial size to form a 3D perovskite with lead halides [1], and has been shown to impart, as the A-site cation of ABX3 unit, beneficial properties to ferroelectric perovskites [2]. Howev
In recent years, organic-inorganic hybrid perovskites have attracted wide attention due to their excellent optoelectronic properties in the application of optoelectronic devices. In the manufacturing process of perovskite solar cells, perovskite film
Layered materials (LMs) are at the centre of an ever increasing research effort due to their potential use in a variety of applications. The presence of imperfections, such as bi- or multilayer areas, holes, grain boundaries, isotropic and anisotropi
Halide perovskites perform remarkably in optoelectronic devices including tandem photovoltaics. However, this exceptional performance is striking given that perovskites exhibit deep charge carrier traps and spatial compositional and structural hetero
Two-dimensional (2D) organic-inorganic perovskites have recently attracted increasing attention due to their great environmental stability, remarkable quantum confinement effect and layered characteristic. Heterostructures consisting of 2D layered pe