Anisotropic Proton and Oxygen Ion Conductivity in Epitaxial Ba2In2O5 Thin Films

125   0   0.0 ( 0 )
 نشر من قبل Daniele Pergolesi
 تاريخ النشر 2019
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

Solid oxide oxygen ion and proton conductors are a highly important class of materials for renewable energy conversion devices like solid oxide fuel cells. Ba2In2O5 (BIO) exhibits both oxygen ion and proton conduction, in dry and humid environment, respectively. In dry environment, the brownmillerite crystal structure of BIO exhibits an ordered oxygen ion sublattice, which has been speculated to result in anisotropic oxygen ion conduction. The hydrated structure of BIO, however, resembles a perovskite and the protons in it were predicted to be ordered in layers. To complement the significant theoretical and experimental efforts recently reported on the potentially anisotropic conductive properties in BIO, we measure here the proton and oxygen ion conductivity along different crystallographic directions. Using epitaxial thin films with different crystallographic orientations the charge transport for both charge carriers is shown to be anisotropic. The anisotropy of the oxygen ion conduction can indeed be explained through the layered structure of the oxygen sublattice in brownmillerite BIO. The anisotropic proton conduction however, further supports the suggested ordering of the protonic defects in the material. The differences in proton conduction along different crystallographic directions attributed to proton ordering in BIO are of a similar extent as those observed along different crystallographic directions in materials where proton ordering is not present but where protons find preferential conduction pathways through chain-like or layered structures.



قيم البحث

اقرأ أيضاً

The interrelation between the epitaxial strain and oxygen deficiency in La0.7Ca0.3MnO3-{delta} thin films was studied in terms of structural and functional properties. The films with a thickness of 1000{AA} were prepared using a PLD system equipped w ith a RHEED facility and a pyrometric film temperature control. The epitaxial strain and the oxygen deficiency in the samples were systematically modified using three different substrates: SrTiO3, (LaAlO3)0.3-(Sr2AlTaO6)0.7 and LaSrAlO4, and four different oxygen pressures during film growth ranging from 0.27mbar to 0.1mbar. It could be demonstrated that the oxygen incorporation depends on the epitaxial strain: oxygen vacancies were induced to accommodate tensile strain whereas the compressive strain suppressed the generation of oxygen vacancies.
We have synthesized highly oxygen deficient HfO$_{2-x}$ thin films by controlled oxygen engineering using reactive molecular beam epitaxy. Above a threshold value of oxygen vacancies, p-type conductivity sets in with up to 6 times 10^{21} charge carr iers per cm3. At the same time, the band-gap is reduced continuously by more than 1 eV. We suggest an oxygen vacancy induced p-type defect band as origin of the observed behavior.
We studied the symmetry of magnetic properties and the resulting magnetic textures in ultra-thin epitaxial Au$_{0.67}$Pt$_{0.33}$/Co/W, a model system exhibiting perpendicular magnetic anisotropy and interface Dzyaloshinskii-Moriya interaction (DMI). As a peculiar feature, the C$_mathrm{2v}$ crystal symmetry induced by the Co/W interface results in an additional uniaxial in-plane magnetic anisotropy in the cobalt layer. Photoemission electron microscopy with magnetic sensitivity reveals the formation of self-organized magnetic stripe domains oriented parallel to the hard in-plane magnetization axis. We attribute this behavior to the lower domain wall energy when oriented along this axis, where both the DMI and the in-plane magnetic anisotropy favor a N{e}el domain wall configuration. The anisotropic domain wall energy also leads to the formation of elliptical skyrmion bubbles in a weak out-of-plane magnetic field.
We studied the ferroelectric and ferromagnetic properties of compressive strained and unstrained BiMnO3 thin films grown by rf-magnetron sputtering. BiMnO3 samples exhibit a 2D cube-on-cube growth mode and a pseudo-cubic struc-ture up to a thickness of 15 nm and of 25 nm when deposited on (001) SrTiO3 and (110) DyScO3, respectively. Above these thicknesses we observe a switching to a 3D island growth and a simultaneous structural change to a monoclinic structure characterized by a (00l) orientation of the monoclinic unit cell. While ferromagnetism is observed below Tc = 100 K for all samples, signatures of room temperature ferroelectricity were found only in the pseudo-cubic ultra-thin films, indicating a correlation between electronic and structural orders.
We report on the observation of metallic behavior in thin films of oxygen-deficient SrTiO$_3$ - down to 9 unit cells - when coherently strained on (001) SrTiO$_3$ or DyScO$_3$-buffered (001) SrTiO$_3$ substrates. These films have carrier concentratio ns of up to 2$times10^{22}$ cm$^{-3}$ and mobilities of up to 19,000 cm$^2$/V-s at 2 K. There exists a non-conducting layer in our SrTiO$_{3-delta}$ films that is larger in films with lower carrier concentrations. This non-conducting layer can be attributed to a surface depletion layer due to a Fermi level pinning potential. The depletion width, transport, and structural properties are not greatly affected by the insertion of a DyScO$_3$ buffer between the SrTiO$_3$ film and SrTiO$_3$ substrate.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا