Nb$_{3}$Sn is a superconductor of great relevance for perspective RF applications. We present for the first time surface impedance $Z_s$ measurements at 15 GHz and low RF field amplitude on Nb$_{3}$Sn in high magnetic fields up to 12 T, with the aim of increasing the knowledge of Nb$_{3}$Sn behavior in such conditions. $Z_s$ is a fundamental material parameter that directly gives useful information about the dissipative and reactive phenomena when the superconductor is subjected to high-frequency excitations. Therefore, we present an analysis of the measured $Z_s$ with the aim of extracting interesting data about pinning in Nb$_{3}$Sn at high frequencies. From $Z_s$ we extract the vortex motion complex resistivity to obtain the $r$-parameter and the depinning frequency $ u_p$ in high magnetic fields. The comparison of the results with the literature shows that the measured $ u_p$ on bulk Nb$_{3}$Sn is several times greater than that of pure Nb. This demonstrates how Nb$_{3}$Sn can be a good candidate for RF technological applications, also in high magnetic fields.
The high frequency vortex motion in Nb$_3$Sn was analyzed in this work up to 12 T. We used a dielectric loaded resonator tuned at 15 GHz to evaluate the surface impedance $Z$ of a Nb$_3$Sn bulk sample (24.8 at.%Sn). From the field induced variation o
The vortex lattice (VL) in the mixed state of the stannide superconductor Yb$_{3}$Rh$_{4}$Sn$_{13}$ has been studied using small-angle neutron scattering (SANS). The field dependencies of the normalized longitudinal and transverse correlation lengths
Tunneling spectroscopy was performed on Nb pieces prepared by the same processes used to etch and clean superconducting radio frequency (SRF) cavities. Air exposed, electropolished Nb exhibited a surface superconducting gap delta=1.55 meV, characteri
Magnetic impurities affect the spectrum of excitations of a superconductor and thus influence its impedance. We concentrate on the dissipative part of the surface impedance. We investigate its dependence on frequency, the density and strength of magn
We study mechanisms of vortex nucleation in Nb$_3$Sn Superconducting RF (SRF) cavities using a combination of experimental, theoretical, and computational methods. Scanning transmission electron microscopy (STEM) image and energy dispersive spectrosc