Single crystal epitaxial thin films of UN and U$_2$N$_3$ have been grown for the first time by reactive DC magnetron sputtering. These films provide ideal samples for fundamental research into the potential accident tolerant fuel, UN, and U$_2$N$_3$, its intermediate oxidation product. Films were characterised using x-ray diffraction (XRD) and x-ray photoelectron spectroscopy (XPS), with XRD analysis showing both thin films to be [001] oriented and composed of a single domain. The specular lattice parameters of the UN and U$_2$N$_3$ films were found to be 4.895,AA{} and 10.72,AA{}, respectively, with the UN film having a miscut of 2.6,$^circ$. XPS showed significant differences in the N-1s peak between the two films, with area analysis showing both films to be stoichiometric.
قيم البحث
اقرأ أيضاً
Magnetite epitaxial thin films have been prepared by pulsed laser deposition at 340 C on MgO and Si substrates. One key result is that the thin film properties are almost identical to the properties of bulk material. For 40 - 50 nm thick films, the s
aturation magnetization and conductivity are respectively 453 emu/cm^3 and 225 1/(Ohm cm) at room temperature. The Verwey transition is at 117 K. The Hall effect indicates an electron concentration corresponding to 0.22 electrons per formula unit at room temperature. Normal and anomalous Hall effect both have a negative sign.
We examine the magnetic ordering of UN and of a closely related nitride, U2N3, by preparing thin epitaxial films and using synchrotron x-ray techniques. The magnetic configuration and subsequent coupling to the lattice are key features of the electro
nic structure. The well-known antiferromagnetic (AF) ordering of UN is confirmed, but the expected accompanying distortion at Tn is not observed. Instead, we propose that the strong magneto-elastic interaction at low temperature involves changes in the strain of the material. These strains vary as a function of the sample form. As a consequence, the accepted AF configuration of UN may be incorrect. In the case of cubic a-U2N3, no single crystals have been previously prepared, and we have determined the AF ordering wave-vector. The AF Tn is close to that previously reported. In addition, resonant diffraction methods have identified an aspherical quadrupolar charge contribution in U2N3 involving the 5f electrons; the first time this has been observed in an actinide compound.
We report molecular beam epitaxy growth of Sr-doped Bi$_2$Se$_3$ films on (111) BaF$_2$ substrate, aimed to realize unusual superconducting properties inherent to Sr$_x$Bi$_2$Se$_3$ single crystals. Despite wide range of the compositions, we do not a
chieve superconductivity. To explore the reason for that we study structural, morphological and electronic properties of the films and compare them to the corresponding properties of the single crystals. The dependence of the c-lattice constant in the films on Sr content appears to be more than an order of magnitude stronger than in the crystals. Correspondingly, all other properties also differ substantially, indicating that Sr atoms get different positions in lattices. We argue that these structural discrepancies come from essential differences in growth conditions. Our research calls for more detailed structural studies and novel growth approaches for design of superconducting Sr$_x$Bi$_2$Se$_3$ thin films.
The lattice of (001)-oriented BiFeO$_3$ epitaxial thin film has been identified by synchrotron x-ray diffraction. By choosing proper scattering zones containing the fixed (001) reflection, we have shown that low-symmetry phases similar to a $M_A$ pha
se exist in the thin film at room temperature. These results demonstrate a change in phase stability from rhombohedral in bulk single crystals, to a modified monoclinic structure in epitaxial thin films.
We report experiments to determine the effect of radiation damage on the phonon spectra of the most common nuclear fuel, UO$_2$. We have irradiated thin ($sim$ 300 nm) epitaxial films of UO$_2$ with 2.1 MeV He$^{2+}$ ions to 0.15 dpa and a lattice sw
elling of $Delta$a/a $sim$ 0.6 %, and then used grazing-incidence inelastic X-ray scattering to measure the phonon spectrum. We succeeded to observe the acoustic modes, both transverse and longitudinal, across the Brillouin zone. The phonon energies, in both the pristine and irradiated samples, are unchanged from those observed in bulk material. On the other hand, the phonon linewidths (inversely proportional to the phonon lifetimes), show a significant broadening when comparing the pristine and irradiated samples. This effect is shown to increase with phonon energy across the Brillouin zone. The decreases in the phonon lifetimes of the acoustic modes are roughly consistent with a 50 % reduction in the thermal conductivity.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها