تسجيل مستخدم جديدThe MRO-accompanied modes of Re-implantation into SiO2-host matrix: XPS and DFT based scenarios
146
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
The following scenarios of Re-embedding into SiO2-host by pulsed Re-implantation were derived and discussed after XPS-and-DFT electronic structure qualification: (i) low Re-impurity concentration mode -> the formation of combined substitutional and interstitial impurities with Re2O7-like atomic and electronic structures in the vicinity of oxygen vacancies; (ii) high Re-impurity concentration mode -> the fabrication of interstitial Re-metal clusters with the accompanied formation of ReO2-like atomic structures and (iii) an intermediate transient mode with Re-impurity concentration increase, when the precursors of interstitial defect clusters are appeared and growing in the host-matrix structure occur. An amplification regime of Re-metal contribution majority to the final Valence Band structure was found as one of the sequences of intermediate transient mode. It was shown that most of the qualified and discussed modes were accompanied by the MRO (middle range ordering) distortions in the initial oxygen subnetwork of the a-SiO2 host-matrix because of the appeared mixed defect configurations.
قيم البحث
اقرأ أيضاً
This is the abstract. The results of measurements of X-ray photoelectron spectra (XPS) of a-SiO2-host material after pulsed implantation with [Mn+] and [Co+, Mn+]-ions as well as DFT-calculations are presented. The low-energy shift is found in XPS Si
2p and O 1s core-levels of single [Mn+] and dual [Co+, Mn+] pulsed ion-implanted a-SiO2 (E = 30 keV, D = 2*10^17 cm^-2) with respect to those of untreated a-SiO2.The similar changes are found in XPS Si 2p and O 1s of stishovite compared to those of quartz. This means that the pulsed ion-implantation induces the local high pressure effect which leads to an appearance of SiO6-structural units in alpha-SiO2 host, forming stishovite-like local atomic structure. This process can be described within electronic bonding transition from the four-fold quartz-like to six-fold stishovite-like high-pressure phase in SiO2 host-matrix. It is found that such octahedral conversion depends on the fluence and starts with doses higher than D = 3*10^16 cm^-2.
Two different types of boron-doped graphene/copper interfaces synthesized using two different flow rates of Ar through the bubbler containing the boron source were studied. X-ray photoelectron spectra (XPS) and optically stimulated electron emission
(OSEE) measurements have demonstrated that boron-doped graphene coating provides a high corrosion resistivity of Cu-substrate with the light traces of the oxidation of carbon cover. The density functional theory calculations suggest that for the case of substitutional (graphitic) boron-defect only the oxidation near boron impurity is energetically favorable and creation of the vacancies that can induce the oxidation of copper substrate is energetically unfavorable. In the case of non-graphitic boron defects oxidation of the area, a nearby impurity is metastable that not only prevent oxidation but makes boron-doped graphene. Modeling of oxygen reduction reaction demonstrates high catalytic performance of these materials.
The results of characterization of TiAlSiON hard coatings deposited on ferric-chromium AISI 430 stainless steel by plasma enhanced magnetron sputtering are presented. The coating with maximum hardness (of 45 GPa) was obtained at the following optimal
values of elemental concentrations: Si ~5 at.%, Al ~15 at.%, and Ti ~27 at.%. The elastic modulus of the coating was 590 GPa. The reading of gaseous mixture (Ar-N2) pressure was 1*10-3 Torr and the reading of partial pressure of oxygen (O2) was 1*10-5 Torr. The X-ray diffraction (XRD) measurements showed the presence of Ti(Al)N. High-energy resolved XPS spectra of core levels revealed the formation of Ti-N, Ti-O-N, Si-N and Al-O-N bonds. Comparison of XPS valence band spectra with specially performed density functional theory calculations for two ordered and few disordered TiN1-xOx (0 =< x <= 1) demonstrates that a Ti(Al)OxNy phase is formed on the surface of AISI430 steel upon the plasma enhanced magnetron sputtering, which provides this material with a good combination of high hardness and improved oxidation resistance.
We compare, through first-principles pseudopotential calculations, the structural, electronic and optical properties of different size silicon nanoclusters embedded in a SiO2 crystalline or amorphous matrix, with that of free-standing, hydrogenated a
nd hydroxided silicon nanoclusters of corresponding size and shape. We find that the largest effect on the opto-electronic behavior is due to the amorphization of the embedded nanocluster. In that, the amorphization reduces the fundamental gap while increasing the absorption strength in the visible range. Increasing the nanocluster size does not change substantially this picture but only leads to the reduction of the absorption threshold, following the quantum confinement rule. Finally, through the calculation of the optical absorption spectra both in a indipendent-particle and many-body approach, we show that the effect of local fields is crucial for describing properly the optical behavior of the crystalline case while it is of minor importance for amorphous systems.
By combining classical molecular dynamics simulations and density functional theory total energy calculations, we study the possibility of doping graphene with B/N atoms using low-energy ion irradiation. Our simulations show that the optimum irradiat
ion energy is 50 eV with substitution probabilities of 55% for N and 40% for B. We further estimate probabilities for different defect configurations to appear under B/N ion irradiation. We analyze the processes responsible for defect production and report an effective swift chemical sputtering mechanism for N irradiation at low energies (~125 eV) which leads to production of single vacancies. Our results show that ion irradiation is a promising method for creating hybrid C-B/N structures for future applications in the realm of nanoelectronics.