On Nematicity and Charge Order in Superoxygenated La$_{2-x}$Sr$_x$CuO$_{4+y}$

238   0   0.0 ( 0 )
 نشر من قبل Zhiwei Zhang
 تاريخ النشر 2017
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

A nematic order in stripe-ordered cuprates was recently identified with (001) reflection at resonant energies associated with the in-plane states. However, whether this resonant reflection is ubiquitous among all 214 cuprates is still unknown. Here we report a Resonant soft X-ray Scattering (RXS) measurement on two La$_{2-x}$Sr$_x$CuO$_{4+y}$ crystals. Charge order was found in La$_2$CuO$_{4+y}$ with a total hole concentration near 0.125/Cu but no measurable (001) peak at any resonance, while in a La$_{1.94}$Sr$_{0.06}$CuO$_{4+y}$ sample near 0.16/Cu a (001) peak resonant was identified to be consistent with the presence of LTT tilting. The lack of such a (001) peak in a compound with stripe-like charge order raises questions about nematicity and the origin of the scattering feature.



قيم البحث

اقرأ أيضاً

We present high energy X-ray diffraction studies on the structural phases of an optimal high-$T_c$ superconductor La$_{2-x}$Sr$_x$CuO$_{4+y}$ tailored by co-hole-doping. This is specifically done by varying the content of two very different chemical species, Sr and O, respectively, in order to study the influence of each. A superstructure known as staging is observed in all samples, with the staging number $n$ increasing for higher Sr dopings $x$. We find that the staging phases emerge abruptly with temperature, and can be described as a second order phase transition with transition temperatures slightly depending on the Sr doping. The Sr appears to correlate the interstitial oxygen in a way that stabilises the reproducibility of the staging phase both in terms of staging period and volume fraction in a specific sample. The structural details as investigated in this letter appear to have no direct bearing on the electronic phase separation previously observed in the same samples. This provides new evidence that the electronic phase separation is determined by the overall hole concentration rather than specific Sr/O content and concommittant structural details.
We present results of inelastic light scattering experiments on single-crystalline La$_{2-x}$Sr$_{x}$CuO$_4$ in the doping range $0.00 le x=p le 0.30$ and Tl$_2$Ba$_2$CuO$_{6+delta}$ at $p=0.20$ and $p=0.24$. The main emphasis is placed on the respon se of electronic excitations in the antiferromagnetic phase, in the pseudogap range, in the superconducting state, and in the essentially normal metallic state at $x ge 0.26$, where no superconductivity could be observed. In most of the cases we compare B$_{1g}$ and B$_{2g}$ spectra which project out electronic properties close to $(pi,0)$ and $(pi/2, pi/2)$, respectively. In the channel of electron-hole excitations we find universal behavior in B$_{2g}$ symmetry as long as the material exhibits superconductivity at low temperature. In contrast, there is a strong doping dependence in B$_{1g}$ symmetry: (i) In the doping range $0.20 le p le 0.25$ we observe rapid changes of shape and temperature dependence of the spectra. (ii) In La$_{2-x}$Sr$_{x}$CuO$_4$ new structures appear for $x < 0.13$ which are superposed on the electron-hole continuum. The temperature dependence as well as model calculations support an interpretation in terms of charge-ordering fluctuations. For $x le 0.05$ the response from fluctuations disappears at B$_{1g}$ and appears at B$_{2g}$ symmetry in full agreement with the orientation change of stripes found by neutron scattering. While, with a grain of salt, the particle-hole continuum is universal for all cuprates the response from fluctuating charge order in the range $0.05 le p < 0.16$ is so far found only in La$_{2-x}$Sr$_{x}$CuO$_4$. We conclude that La$_{2-x}$Sr$_{x}$CuO$_4$ is close to static charge order and, for this reason, may have a suppressed $T_c$.
The in-plane optical conductivity of seven La(2-x)Sr(x)CuO(4) single crystals with x between 0 and 0.15 has been studied from 30 to 295 K. All doped samples exhibit strong peaks in the far-infrared, which closely resemble those observed in Cu-O ladde rs with one-dimensional charge-ordering. The behavior with doping and temperature of the peak energy, width, and intensity allows us to conclude that we are observing charge stripes dynamics in La(2-x)Sr(x)CuO(4) on the fast time scale of infrared spectroscopy.
The magnetic correlations within the cuprates have undergone intense scrutiny as part of efforts to understand high temperature superconductivity. We explore the evolution of the magnetic correlations along the nodal direction of the Brillouin zone i n La2-xSrxCuO4, spanning the doping phase diagram from the anti-ferromagnetic Mott insulator at x = 0 to the metallic phase at x = 0.26. Magnetic excitations along this direction are found to be systematically softened and broadened with doping, at a higher rate than the excitations along the anti-nodal direction. This phenomenology is discussed in terms of the nature of the magnetism in the doped cuprates. Survival of the high energy magnetic excitations, even in the overdoped regime, indicates that these excitations are marginal to pairing, while the influence of the low energy excitations remains ambiguous.
98 - C. Girod , D. LeBoeuf , A. Demuer 2021
The specific heat $C$ of the cuprate superconductors La$_{2-x}$Sr$_x$CuO$_4$ and Bi$_{2+y}$Sr$_{2-x-y}$La$_x$CuO$_{6+delta}$ was measured at low temperature (down to $0.5~{rm K}$), for dopings $p$ close to $p^star$, the critical doping for the onset of the pseudogap phase. A magnetic field up to $35~{rm T}$ was applied to suppress superconductivity, giving direct access to the normal state at low temperature, and enabling a determination of $C_e$, the electronic contribution to the normal-state specific heat, at $T to 0$. In La$_{2-x}$Sr$_x$CuO$_4$ at $x=p = 0.22$, $0.24$ and $0.25$, $C_e / T = 15-16~{rm mJmol}^{-1}{rm K}^{-2}$ at $T = 2~{rm K}$, values that are twice as large as those measured at higher doping ($p > 0.3$) and lower doping ($p < 0.15$). This confirms the presence of a broad peak in the doping dependence of $C_e$ at $p^starsimeq 0.19$, as previously reported for samples in which superconductivity was destroyed by Zn impurities. Moreover, at those three dopings, we find a logarithmic growth as $T to 0$, such that $C_e / T sim {rm B}ln(T_0/T)$. The peak vs $p$ and the logarithmic dependence vs $T$ are the two typical thermodynamic signatures of quantum criticality. In the very different cuprate Bi$_{2+y}$Sr$_{2-x-y}$La$_x$CuO$_{6+delta}$, we again find that $C_e / T sim {rm B}ln(T_0/T$) at $p simeq p^star$, strong evidence that this $ln(1/T)$ dependence - first discovered in the cuprates La$_{1.8-x}$Eu$_{0.2}$Sr$_x$CuO$_4$ and La$_{1.6-x}$Nd$_{0.4}$Sr$_x$CuO$_4$ - is a universal property of the pseudogap critical point. All four materials display similar values of the $rm B$ coefficient, indicating that they all belong to the same universality class.