We have studied the effect of Al doping on the structural, magnetic and electrical properties of La$_{1-x}$Ba$_x$Mn$_{1-x}$Al$_x$O$_3$ ($0leq x leq 0.25$) manganite, annealed in two 750$^oC$ and 1350$^oC$ temperatures. The XRD analysis shows that the structures in all samples have single phase rhombohedral structure with R$bar{3}$c space group. The unit cell volume almost decrease with increasing the Al doping in all samples. The grain growth with increasing annealing temperature and Al doping also have been studied. We observed that, T$_c$ temperature decreases when the Al ion substitute in Mn ion site. The magnetic study of the samples via magnetic susceptibility results in Griffiths and spin-glass phase for samples doped with aluminium. Along the resistivity measurement results, the $T_{MIT}$ (metal-insulator) transition temperatures decrease and the system become an insulator. The insulator-metal transition occurs for L0 sample in near 165K, while this transition is weak for H0 sample due to oxygen non-stoichiometry.Using three models viz. 1. Adiabatic small polaron hoping, 2.Variable range hopping, and 3. Percolation model, the resistance have been studied.
قيم البحث
اقرأ أيضاً
We report the temperature and magnetic field dependence of transport properties in epitaxial films of the manganite La$_{1-x}$Ca$_{x}$MnO$_{3}$ in the overdoped region of the phase diagram for $x > 0.5$, where a charge--ordered (CO) and an antiferrom
agnetic (AF) phase are present. Resistivity, magnetoresistance and angular dependence of magnetoresistance were measured in the temperature interval $4.2 ~mathrm{K} < T < 300 ~mathrm{K}$, for three concentrations $x = 0.52, 0.58$ and $0.75$ and in magnetic fields up to 5 T. The semiconductor/insulator--like behavior in zero field was observed in the entire temperature range for all three concentrations textit{x} and the electric conduction, at lower temperatures, in the CO state obeys 3D Motts variable--range hopping model. A huge negative magnetoresistance for $x = 0.52$ and $x = 0.58$, a metal--insulator transition for $B > 3 ~mathrm{T}$ for $x = 0.52$ and the presence of anisotropy in magnetoresistance for $x = 0.52$ and $x = 0.58$ show the fingerprints of colossal magnetoresistance (CMR) behavior implying the existence of ferromagnetic (FM) clusters. The declining influence of the FM clusters in the CO/AF part of the phase diagram with increasing $x$ contributes to a possible explanation that a phase coexistence is the origin of the CMR phenomenon.
Epitaxial thin films of the substitutionally alloyed half-Heusler series CoTi$_{1-x}$Fe$_x$Sb were grown by molecular beam epitaxy on InAlAs/InP(001) substrates for concentrations 0.0$leq$x$leq$1.0. The influence of Fe on the structural, electronic,
and magnetic properties was studied and compared to that expected from density functional theory. The films are epitaxial and single crystalline, as measured by reflection high-energy electron diffraction and X-ray diffraction. Using in-situ X-ray photoelectron spectroscopy, only small changes in the valence band are detected for x$leq$0.5. For films with x$geq$0.05, ferromagnetism is observed in SQUID magnetometry with a saturation magnetization that scales linearly with Fe content. A dramatic decrease in the magnetic moment per formula unit occurs when the Fe is substitutionally alloyed on the Co site indicating a strong dependence on the magnetic moment with site occupancy. A crossover from both in-plane and out-of-plane magnetic moments to only in-plane moment occurs for higher concentrations of Fe. Ferromagnetic resonance indicates a transition from weak to strong interaction with a reduction in inhomogeneous broadening as Fe content is increased. Temperature-dependent transport reveals a semiconductor to metal transition with thermally activated behavior for x$leq$0.5. Anomalous Hall effect and large negative magnetoresistance (up to -18.5% at 100 kOe for x=0.3) are observed for higher Fe content films. Evidence of superparamagnetism for x=0.3 and x=0.2 suggests for moderate levels of Fe, demixing of the CoTi$_{1-x}$Fe$_x$Sb films into Fe rich and Fe deficient regions may be present. Atom probe tomography is used to examine the Fe distribution in a x=0.3 film. Statistical analysis reveals a nonhomogeneous distribution of Fe atoms throughout the film, which is used to explain the observed magnetic and electrical behavior.
We report the structural, magnetic, and magnetocaloric properties of Co$_2$Cr$_{1-x}$Ti$_x$Al ($x=$ 0--0.5) Heusler alloys for spintronic and magnetic refrigerator applications. Room temperature X-ray diffraction and neutron diffraction patterns alon
g with Rietveld refinements confirm that the samples are of single phase and possess a cubic structure. Interestingly, magnetic susceptibly measurements indicate a second order phase transition from paramagnetic to ferromagnetic where the Curie temperature (T$_{rm C}$) of Co$_2$CrAl increases from 330~K to 445~K with Ti substitution. Neutron powder diffraction data of the $x=$ 0 sample across the magnetic phase transition taken in a large temperature range confirm the structural stability and exclude the possibility of antiferromagnetic ordering. The saturation magnetization of the $x=$ 0 sample is found to be 8000~emu/mol (1.45~$mu_{rm B}$/{it f.u.}) at 5~K, which is in good agreement with the value (1.35$pm$0.05~$mu_{rm B}$/{it f.u.}) obtained from the Rietveld analysis of the neutron powder diffraction pattern measured at temperature of 4~K. By analysing the temperature dependence of the neutron data of the $x=$ 0 sample, we find that the change in the intensity of the most intense Bragg peak (220) is consistent with the magnetization behavior with temperature. Furthermore, an enhancement of change in the magnetic entropy and relative cooling power values has been observed for the $x=$ 0.25 sample. Interestingly, the critical behavior analysis across the second order magnetic phase transition and extracted exponents ($betaapprox$ 0.496, $gammaapprox$ 1.348, and $deltaapprox$ 3.71 for the $x=$ 0.25 sample) suggest the presence of long-range ordering, which deviates towards 3D Heisenberg type interactions above T$_{rm C}$, consistent with the interaction range value $sigma$.
Using density-functional ab initio theoretical techniques, we study (Ga$_{1-x}$In$_x$)$_2$O$_3$ in both its equilibrium structures (monoclinic $beta$ and bixbyite) and over the whole range of composition. We establish that the alloy exhibits a large
and temperature-independent miscibility gap. On the low-$x$ side, the favored phase is isostructural with $beta$-Ga$_2$O$_3$; on the high-$x$ side, it is isostructural with bixbyite In$_2$O$_3$. The miscibility gap opens between approximately 15% and 55% In content for the bixbyite alloy grown epitaxially on In$_2$O$_3$, and 15% and 85% In content for the free-standing bixbyite alloy. The gap, volume and band offsets to the parent compound also exhibit anomalies as function of $x$. Specifically, the offsets in epitaxial conditions are predominantly type-B staggered, but have opposite signs in the two end-of-range phases.
We report measurements and analyses of resistivity, thermopower, and thermal conductivity of polycrystalline samples of perovskite LaRh$_{1-x}$Ni$_x$O$_3$. The thermopower is found to be large at 800 K (185 $mu$V/K for $x=$0.3), which is ascribed to
the high-temperature stability of the low-spin state of Rh$^{3+}$/Rh$^{4+}$ ions. This clearly contrasts with the thermopower of the isostructural oxide LaCoO$_3$, which rapidly decreases above 500 K owing to the spin-state transition. The spin state of the transition-metal ions is one of the most important parameters in oxide thermoelectrics.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها