تسجيل مستخدم جديدInsulating phase at low temperature in ultrathin La0.8Sr0.2MnO3 films
75
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Metal-insulator transition is observed in the La0.8Sr0.2MnO3 thin films with thickness larger than 5 unit cells. Insulating phase at lower temperature appeared in the ultrathin films with thickness ranging from 6 unit cells to 10 unit cells and it is found that the Mott variable range hopping conduction dominates in this insulating phase at low temperature with a decrease of localization length in thinner films. A deficiency of oxygen content and a resulted decrease of the Mn valence have been observed in the ultrathin films with thickness smaller than or equal to 10 unit cells by studying the aberration-corrected scanning transmission electron microscopy and electron energy loss spectroscopy of the films. These results suggest that the existence of the oxygen vacancies in thinner films suppresses the double-exchange mechanism and contributes to the enhancement of disorder, leading to a decrease of the Curie temperature and the low temperature insulating phase in the ultrathin films. In addition, the suppression of the magnetic properties in thinner films indicates stronger disorder of magnetic moments, which is considered to be the reason for this decrease of the localization length.
قيم البحث
اقرأ أيضاً
We present a study of the thickness dependence of magnetism and electrical conductivity in ultra thin La0.67Sr0.33MnO3 films grown on SrTiO3 (110) substrates. We found a critical thickness of 10 unit cells below which the conductivity of the films di
sappeared and simultaneously the Curie temperature (TC) increased, indicating a magnetic insulating phase at room temperature. These samples have a TC of about 560 K with a significant saturation magnetization of 1.2 +- 0.2 muB/Mn. The canted antiferromagnetic insulating phase in ultra thin films of n< 10 coincides with the occurrence of a higher symmetry structural phase with a different oxygen octahedra rotation pattern. Such a strain engineered phase is an interesting candidate for an insulating tunneling barrier in room temperature spin polarized tunneling devices.
We demonstrate that magnetic skyrmions with a mean diameter around 60 nm can be stabilized at room temperature and zero external magnetic field in an exchange-biased Pt/Co/NiFe/IrMn multilayer stack. This is achieved through an advanced optimization
of the multilayer stack composition in order to balance the different magnetic energies controlling the skyrmion size and stability. Magnetic imaging is performed both with magnetic force microscopy and scanning Nitrogen-Vacancy magnetometry, the latter providing unambiguous measurements at zero external magnetic field. In such samples, we show that exchange bias provides an immunity of the skyrmion spin texture to moderate external magnetic field, in the tens of mT range, which is an important feature for applications as memory devices. These results establish exchange-biased multilayer stacks as a promising platform towards the effective realization of memory and logic devices based on magnetic skyrmions.
The correlated electron system SmNiO3 exhibits a metal-insulator phase transition at 130 {deg}C. Using an ionic liquid as an electric double layer (EDL) gate on three-terminal ultrathin SmNiO3 devices, we investigate gate control of the channel resis
tance and transition temperature. Resistance reduction is observed across both insulating and metallic phases with ~25% modulation at room temperature. We show that resistance modulation is predominantly due to electrostatic charge accumulation and not electrochemical doping by control experiments in inert and air en-vironments. We model the resistance behavior and estimate the accumulated sheet density (~1-2 x 10^14 cm^-2) and EDL capacitance (~12 {mu}F/cm^2).
Electronic states of a correlated material can be effectively modified by structural variations delivered from a single-crystal substrate. In this letter, we show that the CrN films grown on MgO (001) substrates have a (001) orientation, whereas the
CrN films on {alpha}-Al2O3 (0001) substrates are oriented along (111) direction parallel to the surface normal. Transport properties of CrN films are remarkably different depending on crystallographic orientations. The critical thickness for the metal-insulator transition (MIT) in CrN 111 films is significantly larger than that of CrN 001 films. In contrast to CrN 001 films without apparent defects, scanning transmission electron microscopy results reveal that CrN 111 films exhibit strain-induced structural defects, e. g. the periodic horizontal twinning domains, resulting in an increased electron scattering facilitating an insulating state. Understanding the key parameters that determine the electronic properties of ultrathin conductive layers is highly desirable for future technological applications.
This paper reports on the structural and optical properties of Co-doped TiO2 thin films grown onto (0001) Al2O3 substrates by non-reactive pulsed laser deposition (PLD) using argon as buffer gas. It is shown that by keeping constant the substrate tem
perature at as low as 310 C and varying only the background gas pressure between 7 Pa and 70 Pa, it is possible to grow either epitaxial rutile or pure anatase thin films, as well as films with a mixture of both polymorphs. The optical band gaps of the films are red shifted in comparison to the values usually reported for undoped TiO2, which is consistent with n-type doping of the TiO2 matrix. Such band gap red shift brings the absorption edge of the Co-doped TiO2 films into the visible region, which might favour their photocatalytic activity. Furthermore, the band gap red shift depends on the films phase composition, increasing with the increase of the Urbach energy for increasing rutile content.