تسجيل مستخدم جديدAsymmetric Pt/Co/Pt structure as a platform for extracting pure spin Hall torque
74
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We have quantitatively studied the spin-orbit torque purely generated by the spin Hall effect in a wide range of temperatures by intensionally eliminating the Rashba spin-orbit torque using Pt/Co/Pt trilayers with asymmetric thicknesses of the top and bottom Pt layers. The vanishingly small contribution from the Rashba effect has been confirmed through the vector measurements of the current-induced effective fields. In order to precisely determine the value of the spin Hall torque, the complete cancelation of the spin Hall torque has been verified by fabricating symmetric Pt/Co/Pt structure on SiO2 and Gd3Ga5O12 (GGG) substrates. Despite of the complete cance- lation on the GGG substrate, the spin Hall torque cannot be completely canceled out even when the top and bottom Pt layers have same thicknesses on the SiO2 substrate, which suggests that Pt/Co/Pt trilayers on a GGG substrate is a suitable system for precise measurements of the spin Hall torque. The result of the vector measurements on Pt/Co/Pt/GGG from 300 to 10 K shows that the spin Hall torque is almost independent of temperature, which is quantitatively reproduced under the assumption of the temperature-independent spin Hall angle of Pt.
قيم البحث
اقرأ أيضاً
We present the Co-Gd composition dependence of the spin-Hall magnetoresistance (SMR) and anisotropic magnetoresistance (AMR) for ferrimagnetic Co100-xGdx / Pt bilayers. With Gd concentration x, its magnetic moment increasingly competes with the Co mo
ment in the net magnetization. We find a nearly compensated ferrimagnetic state at x = 24. The AMR changes sign from positive to negative with increasing x, vanishing near the magnetization compensation. On the other hand, the SMR does not vary significantly even where the AMR vanishes. These experimental results indicate that very different scattering mechanisms are responsible for AMR and SMR. We discuss a possible origin for the alloy composition dependence.
We experimentally investigate the current-induced magnetization reversal in Pt/[Co/Ni]$_3$/Al multilayers combining the anomalous Hall effect and magneto-optical Kerr effect techniques in crossbar geometry. The magnetization reversal occurs through n
ucleation and propagation of a domain of opposite polarity for a current density of the order of 0.3 TA/m$^2$. In these experiments we demonstrate a full control of each stage: i)the {O}rsted field controls the domain nucleation and ii) domain-wall propagation occurs by spin torque from the Pt spin Hall effect. This scenario requires an in-plane magnetic field to tune the domain wall center orientation along the current for efficient domain wall propagation. Indeed, as nucleated, domain walls are chiral and Neel like due to the interfacial Dzyaloshinskii-Moriya interaction.
The magnetic proximity effect in top and bottom Pt layers induced by Co in Ta/Pt/Co/Pt multilayers has been studied by interface sensitive, element specific x-ray resonant magnetic reflectivity. The asymmetry ratio for circularly polarized x-rays of
left and right helicity has been measured at the Pt $L_3$ absorption edge (11567 eV) with an in-plane magnetic field ($pm158$ mT) to verify its magnetic origin. The proximity-induced magnetic moment in the bottom Pt layer decreases with the thickness of the Ta buffer layer. Grazing incidence x-ray diffraction has been carried out to show that the Ta buffer layer induces the growth of Pt(011) rather than Pt(111) which in turn reduces the induced moment. A detailed density functional theory study shows that an adjacent Co layer induces more magnetic moment in Pt(111) than in Pt(011). The manipulation of the magnetism in Pt by the insertion of a Ta buffer layer provides a new way of controlling the magnetic proximity effect which is of huge importance in spin-transport experiments across similar kind of interfaces.
Extensive efforts have been devoted to the study of spin-orbit torque in ferromagnetic metal/heavy metal bilayers and exploitation of it for magnetization switching using an in-plane current. As the spin-orbit torque is inversely proportional to the
thickness of the ferromagnetic layer, sizable effect has only been realized in bilayers with an ultrathin ferromagnetic layer. Here we demonstrate that, by stacking ultrathin Pt and FeMn alternately, both ferromagnetic properties and current induced spin-orbit torque can be achieved in FeMn/Pt multilayers without any constraint on its total thickness. The critical behavior of these multilayers follows closely three-dimensional Heisenberg model with a finite Curie temperature distribution. The spin torque effective field is about 4 times larger than that of NiFe/Pt bilayer with a same equivalent NiFe thickness. The self-current generated spin torque is able to switch the magnetization reversibly without the need for an external field or a thick heavy metal layer. The removal of both thickness constraint and necessity of using an adjacent heavy metal layer opens new possibilities for exploiting spin-orbit torque for practical applications.
We investigate the spin Hall magnetoresistance (SMR) at room temperature in thin film heterostructures of antiferromagnetic, insulating, (0001)-oriented alpha-Fe2O3 (hematite) and Pt. We measure their longitudinal and transverse resistivities while r
otating an applied magnetic field of up to 17T in three orthogonal planes. For out-of-plane magnetotransport measurements, we find indications for a multidomain antiferromagnetic configuration whenever the field is aligned along the film normal. For in-plane field rotations, we clearly observe a sinusoidal resistivity oscillation characteristic for the SMR due to a coherent rotation of the Neel vector. The maximum SMR amplitude of 0.25% is, surprisingly, twice as high as for prototypical ferrimagnetic Y3Fe5O12/Pt heterostructures. The SMR effect saturates at much smaller magnetic fields than in comparable antiferromagnets, making the alpha-Fe2O3/Pt system particularly interesting for room-temperature antiferromagnetic spintronic applications.