The H-T phase diagrams of single crystalline electron-doped K0.83Fe1.83Se2 (KFS1), K0.8Fe2Se2 (KFS2) and hole-doped Eu0.5K0.5Fe2As2 (EKFA) have been deduced from tunnel diode oscillator-based contactless measurements in pulsed magnetic fields up to 57 T for the inter-plane (H//c) and in-plane (H//ab) directions. The temperature dependence of the upper critical magnetic field Hc2(T) relevant to EFKA is accounted for by the Pauli model including an anisotropic Pauli paramagnetic contribution (mu_BHp=114 T for H//ab and 86 T for H//c). This is also the case of KFS1 and KFS2 for H//ab whereas a significant upward curvature, accounted for by a two-gap model, is observed for H//c. Despite the presence of antiferromagnetic lattice order within the superconducting state of the studied compounds, no influence of magnetic ordering on the temperature dependence of Hc2(T) is observed.
Early work on the iron-arsenide compounds supported the view, that a reduced dimensionality might be a necessary prerequisite for high-Tc superconductivity. Later, however, it was found that the zero-temperature upper critical magnetic field, Hc2(0),
Superconductivity of Ca1-xLaxFe2As2 single crystals with various doping level were investigated via electromagnetic measurements for out-plane (H//c) and in-plane (H//ab) directions. Obvious double superconducting transitions, which can survive in ma
We report measurements of the temperature dependence of the radio-frequency magnetic penetration depth in Ba_0.68K_0.32Fe_2As_2 and Ba(Fe_0.93Co_0.07)_2As_2 single crystals in pulsed magnetic fields up to 60 T. From our data, we construct an H-T phas
Optimally-doped La1.85Sr0.15CuO4 single crystals have been investigated by dc and ac magnetic measurements. These crystals have rectangular needle-like shapes with the long needle axis parallel to the crystallographic c axis (c-crystal) or parallel t
We present heat capacity measurements of the upper critical fields of single-crystal NdFeAsO1-xFx. In zero-magnetic field a clear step in the heat capacity is observed at Tc = 47K . In fields applied perpendicular to the FeAs-layers the step broadens