Using low-temperature molecular beam epitaxy, we study substitutions of Fe atoms for Co ones in Co_3-xFe_xSi Heusler-compound films grown on Si and Ge. Even for the low-temperature grown Heusler-compound films, the Co-Fe atomic substitution at A and C sites can be confirmed by the conversion electron Mossbauer spectroscopy measurements. As a result, the magnetic moment and room-temperature spin polarization estimated by nonlocal spin-valve measurements are systematically changed with the Co-Fe substitutions. This study experimentally verified that the Co-Fe substitution in Co_3-xFe_xSi Heusler compounds can directly affect the room-temperature spin polarization.
قيم البحث
اقرأ أيضاً
Thin highly epitaxial BiFeO$_3$ films were prepared on SrTiO$_3$ (100) substrates by reactive magnetron co-sputtering. Detailed MOKE measurements on BiFeO$_3$/Co-Fe bilayers were performed to investigate the exchange bias as a function of the films t
hicknesses and Co-Fe stoichiometries. We found a maximum exchange bias of H$_{mathrm{eb}}$=92 Oe and a coercive field of H$_{mathrm{c}}$=89 Oe for a 12.5 nm thick BiFeO$_3$ film with a 2 nm thick Co layer. The unidirectional anisotropy is clearly visible in in-plane rotational MOKE measurements. AMR measurements reveal a strongly increasing coercivity with decreasing temperature, but no significant change in the exchange bias field.
We study room-temperature generation and detection of pure spin currents using lateral spin-valve devices with Heusler-compound electrodes, Co$_{2}$FeSi (CFS) or Fe$_{3}$Si (FS). The magnitude of the nonlocal spin-valve (NLSV) signals is seriously af
fected by the dispersion of the resistivity peculiarly observed in the low-temperature grown Heusler compounds with ordered structures. From the analysis based on the one-dimensional spin diffusion model, we find that the spin polarization monotonically increases with decreasing the resistivity, which depends on the structural ordering, for both CFS and FS electrodes, and verify that CFS has relatively large spin polarization compared with FS.
Magnetic anisotropies and magnetization reversal properties of the epitaxial Heusler compound Co$_2$Cr$_{0.6}$Fe$_{0.4}$Al (CCFA) deposited on Fe and Cr buffer layers are studied. Both samples exhibit a growth-induced fourfold anisotropy, and magneti
zation reversal occurs through the formation of stripy domains or 90 degree domains. During rotational magnetometric scans the sample deposited on Cr exhibits about 2 degree sharp peaks in the angular dependence of the coercive field, which are oriented along the hard axis directions. These peaks are a consequence of the specific domain structure appearing in this particular measurement geometry. A corresponding feature in the sample deposited on Fe is not observed.
10 nm and 50 nm Co$_{2}$FeAl (CFA) thin films have been deposited on MgO(001) and Si(001) substrates by magnetron sputtering and annealed at different temperatures. X-rays diffraction revealed polycrystalline or epitaxial growth (according to the rel
ation CFA(001)[110]//MgO(001)[100] epitaxial relation), respectively for CFA films grown on a Si and on a MgO substrate. For these later, the chemical order varies from the A2 phase to the B2 phase when increasing the annealing temperature (Ta) while only the A2 disorder type has been observed for CFA grown on Si. Microstrip ferromagnetic resonance (MS-FMR) measurements revealed that the in-plane anisotropy results from the superposition of a uniaxial and of a fourfold symmetry term for CFA grown on MgO substrates. This fourfold anisotropy, which disappears completely for samples grown on Si, is in accord with the crystal structure of the samples. The fourfold anisotropy field decreases when increasing Ta while the uniaxial anisotropy field is nearly unaffected by Ta within the investigated range. The MS-FMR data also allow for concluding that the gyromagnetic factor remains constant and that the exchange stiffness constant increases with $T_{a}$. Finally, the FMR linewidth decreases when increasing Ta, due to the enhancement of the chemical order. We derive a very low intrinsic damping parameter (1.3*10^-3 and 1.1*10^-3 for films of 50 nm thickness annealed at 615 {deg}C grown on MgO and on Si, respectively).
The effect of Co on the structural, magnetic and magnetocaloric effect (MCE) of Ni50-xCoxMn38Sb12 (x=0,2,3,4,5) Heusler alloys was studied. Using x-ray diffraction, we show the evolution of the martensitic phase from the austenite phase. The martensi
tic transition temperature is found to decrease monotonically with Co concentration. Remarkable enhancement of MCE is observed near room temperature upon Co substitution. The maximum magnetic entropy change of 34 Jkg-1K-1 was achieved in x=5 at 262 K in a field of 50 kOe and a value of 29 Jkg-1K-1 found near room temperature. The significant increase in the magnetization associated with the reverse martensitic transition is responsible for the giant MCE in these compounds.