Measurements of anisotropic transport properties (dc and high-frequency regime) of driven vortex matter in YBa$_2$Cu$_3$O$_{7-x}$ with elongated strong-pinning sites (c-axis aligned, self-assembled BaZrO$_3$ nanorods) are used to demonstrate that the effective-mass angular scaling takes place only in intrinsic physical quantities (flux-flow resistivity), and not in pinning-related Labusch parameter and critical currents. Comparison of the dynamics at different time scales shows evidence for a transition of the vortex matter toward a Mott phase, driven by the presence of nanorods. The strong pinning in dc arises partially from a dynamic effect.
قيم البحث
اقرأ أيضاً
We present a study of the anisotropic vortex parameters as obtained from measurements of the microwave complex resistivity in the vortex state with a tilted applied magnetic field in YBa2Cu3O7-x thin films with BaZrO3 nanorods. We present the angular
dependence of the vortex viscosity $eta$, the pinning constant k_p and the upper limit for the creep factor chi_M. We show that the directional effect of the nanorods is absent in eta, which is dictated by the mass anisotropy gamma. By contrast, pinning-mediated properties are strongly affected by the nanorods. It is significant that the pinning and creep affected by the nanorods is detectable also at our very high operating frequency, which implies very short-range displacements of the vortices from their equilibrium position.
We report on the field dependence of the microwave complex resistivity data in YBa$_2$Cu$_3$O$_{7-x}$/BaZrO$_3$ films grown by PLD at various BaZrO$_3$ content. The data, analyzed within a recently developed general framework for the mixed-state micr
owave response of superconductors, yield the field dependence of the fluxon parameters such as the vortex viscosity and the pinning constant. We find that pinning undergoes a change of regime when the BaZrO$_3$ content in the target increases from 2.5 mol.% to 5 mol.%. Simultaneously, the vortex viscosity becomes an increasing function of the applied magnetic field. We propose a scenario in which flux lines are pinned as bundles, and a crossover from dilute point pins to dense c-axis correlated defects takes place between 2.5 and 5 mol.% in the BZO concentration. Our data are inconsistent with vortices occupying mainly the BaZrO$_3$ sites at low fields, and suggest instead that vortices occupy both BaZrO$_3$ sites and interstitials in the YBa$_2$Cu$_3$O$_{7-x}$ matrix, even at low fields.
We investigate the effect of the anisotropy and of the directional pinning in YBa$_2$Cu$_3$O$_{7-x}$ films grown by pulsed laser ablation from targets containing BaZrO$_3$ at 5% mol. BaZrO$_3$ inclusions self-assemble to give nanorods oriented along
the c-axis, thus giving a preferential direction for vortex pinning. The directionality of vortex response is studied at high ac frequency with the complex microwave response at 48 GHz, as a function of the applied field and of the angle $theta$ between the field and the c-axis. The complex microwave response does not exhibit any angular scaling, suggesting that the structural anisotropy of YBa$_2$Cu$_3$O$_{7-x}$ is supplemented by at least another preferred orientation. The pinning parameter $r$ shows evidence of directional pinning, effective in a wide range of angles around the c-axis (thus ascribed to BZO nanocolumns).
We discuss pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The E
B process produces low defected crystallites with small grain size providing enhanced pinning at grain boundaries without degradation of Tc. The PLD process produces films with structural disorder on a scale less that the coherence length that further improves pinning, but also depresses Tc.
The magnetoresistivity and critical current density of well characterized Si-nanoparticle doped and undoped Cu-sheathed MgB$_{2}$ tapes have been measured at temperatures $Tgeq 28$ K in magnetic fields $Bleq 0.9$ T. The irreversibility line $B_{irr}(
T)$ for doped tape shows a stepwise variation with a kink around 0.3 T. Such $B_{irr}(T)$ variation is typical for high-temperature superconductors with columnar defects (a kink occurs near the matching field $% B_{phi}$) and is very different from a smooth $B_{irr}(T)$ variation in undoped MgB$_{2}$ samples. The microstructure studies of nanoparticle doped MgB$_{2}$ samples show uniformly dispersed nanoprecipitates, which probably act as a correlated disorder. The observed difference between the field variations of the critical current density and pinning force density of the doped and undoped tape supports the above findings.