Structure and magnetic properties of nanostructured Pd-Fe thin films produced by pulse electrodeposition

43   0   0.0 ( 0 )
 نشر من قبل G. K. Strukova
 تاريخ النشر 2011
  مجال البحث فيزياء
والبحث باللغة English
 تأليف G.K. Strukova




اسأل ChatGPT حول البحث

Nanostructured Pd-Fe thin films with varied Fe content were prepared by electrodeposition technique from organic electrolytes on Cu and brass substrates. The structure and the magnetic properties of the films were investigated prior to post-deposition annealing. The structure of the Pd1-xFex thin films with x = 0.14, 0.24, and 0.52 was determined by X-ray diffraction (XRD) and transmission electron microscopy (TEM) as a solid solution of iron in palladium face-centered cubic lattice with the (111) orientation of nanograins relatively to the substrate surface. The films with higher iron concentration, x = 0.74, 0.91, have structure of a solid solution based on the body-centered cubic lattice. The average grain size determined by the scanning electron microscopy (SEM) for the first two alloys is 7-10 nm, and for the latter ones it is about 120 nm. The saturation magnetization of the films has linear dependence on the iron content, but coercivity has non-monotonic dependence on x, i.e. the films with x = 0.68 show highest coercivity. The magnetic anisotropy of the samples is studied by ferromagnetic resonance (FMR) spectroscopy.

قيم البحث

اقرأ أيضاً

CaFe2O4 is a highly anisotropic antiferromagnet reported to display two spin arrangements with up-up-down-down (phase A) and up-down-up-down (phase B) configurations. The relative stability of these phases is ruled by the competing ferromagnetic and antiferromagnetic interactions between Fe3+ spins arranged in two different environments, but a complete understanding of the magnetic structure of this material does not exist yet. In this study we investigate epitaxial CaFe2O4 thin films grown on TiO2 (110) substrates by means of Pulsed Laser Deposition (PLD). Structural characterization reveals the coexistence of two out-of-plane crystal orientations and the formation of three in-plane oriented domains. The magnetic properties of the films, investigated macroscopically as well as locally, including highly sensitive Mossbauer spectroscopy, reveal the presence of just one order parameter showing long-range ordering below T = 185 K and the critical nature of the transition. In addition, a non-zero in-plane magnetization is found, consistent with the presence of uncompensated spins at phase or domain boundaries, as proposed for bulk samples.
Room temperature ferromagnetism was observed in n-type Fe-doped In2O3 thin films deposited on c-cut sapphire substrates by pulsed laser deposition. Structure, magnetism, composition, and transport studies indicated that Fe occupied the In sites of th e In2O3 lattice rather than formed any metallic Fe or other magnetic impurity phases. Magnetic moments of films were proved to be intrinsic and showed to have a strong dependence on the carrier densities which depended on the Fe concentration and its valance state as well as oxygen pressure.
We investigated structural, magnetic and electrical properties of sputter deposited Mn-Fe-Ga compounds. The crystallinity of the Mn-Fe-Ga thin films was confirmed using x-ray diffraction. X-ray reflection and atomic force microscopy measurements were utilized to investigate the surface properties, roughness, thickness and density of the deposited Mn-Fe-Ga. Depending on the stoichiometry, as well as the used substrates (SrTiO3 (001) and MgO (001)) or buffer layer (TiN) the Mn-Fe-Ga crystallizes in the cubic or the tetragonally distorted phase. Anomalous Hall effect and alternating gradient magnetometry measurements confirmed strong perpendicular magnetocrystalline anisotropy. Low saturation magnetization and hard magnetic behavior was reached by tuning the composition. Temperature dependent anomalous Hall effect measurements in a closed cycle He-cryostat showed a slight increase in coercivity with decreasing temperature (300K to 2K). TiN buffered Mn2.7Fe0.3Ga revealed sharper switching of the magnetization compared to the unbuffered layers.
Metastable manganite perovskites displaying the antiferromagnetic so-called E-phase are predicted to be multiferroic. Due to the need of high-pressures for the synthesis of this phase, this prediction has only been confirmed in bulk HoMnO3. Here we r eport on the growth and characterization of YbMnO3 perovskite thin films grown under epitaxial strain. Highly-oriented thin films, with thickness down to ~30nm, can be obtained showing magneto-dielectric coupling and magnetic responses as those expected for the E-phase. We observe that the magnetic properties depart from the bulk behavior only in the case of ultrathin films (d< 30nm), which display a glassy magnetic behavior. We show that strain effects alone cannot account for this difference and that the film morphology plays, instead, a crucial role.
The double perovskite Sr2CrReO6 is an interesting material for spintronics, showing ferrimagnetism up to 635 K with a predicted high spin polarization of about 86%. We fabricated Sr2CrReO6 epitaxial films by pulsed laser deposition on (001)-oriented SrTiO3 substrates. Phase-pure films with optimum crystallographic and magnetic properties were obtained by growing at a substrate temperature of 700 degree C in pure O2 of 6.6x10-4 mbar. The films are c-axis oriented, coherently strained, and show less than 20% anti-site defects. The magnetization curves reveal high saturation magnetization of 0.8 muB per formula unit and high coercivity of 1.1 T, as well as a strong magnetic anisotropy.
التعليقات
جاري جلب التعليقات جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها
mircosoft-partner

هل ترغب بارسال اشعارات عن اخر التحديثات في شمرا-اكاديميا