Variable-field Hall measurements were performed on epitaxial graphene grown on Si-face and C-face SiC. The carrier transport involves essentially a single-type of carrier in few-layer graphene, regardless of SiC face. However, in multi-layer graphene (MLG) grown on C-face SiC, the Hall measurements indicated the existence of several groups of carriers with distinct mobilities. Electrical transport in MLG can be properly described by invoking three independent conduction channels in parallel. Two of these are n- and p-type, while the third involves nearly intrinsic graphene. The carriers in this lightly doped channel have significantly higher mobilities than the other two.
قيم البحث
اقرأ أيضاً
The single layer of Zirconium pentatelluride (ZrTe5) has been predicted to be a large-gap two-dimensional (2D) topological insulator, which has attracted particular attention in the topological phase transitions and potential device application. Here
we investigated the transport properties in ZrTe5 films with the dependence of thickness from a few nm to several hundred nm. We find that the temperature of the resistivity anomalys peak (Tp) is inclining to increase as the thickness decreases, and around a critical thickness of ~40 nm, the dominating carriers in the films change from n-type to p-type. With comprehensive studying of the Shubnikov-de Hass (SdH) oscillations and Hall resistance at variable temperatures, we demonstrate the multi-carrier transport instinct in the thin films. We extract the carrier densities and mobilities of two majority carriers using the simplified two-carrier model. The electron carriers can be attributed to the Dirac band with a non-trivial Berrys phase {pi}, while the hole carriers may originate from the surface chemical reaction or unintentional doping during the microfabrication process. It is necessary to encapsulate ZrTe5 film in the inert or vacuum environment to make a substantial improvement in the device quality.
Magneto-transmission of a thin layer of bulk graphite is compared with spectra taken on multilayer epitaxial graphene prepared by thermal decomposition of a SiC crystal. We focus on the spectral features evolving as sqrt{B}, which are evidence for th
e presence of Dirac fermions in both materials. Whereas the results on multi-layer epitaxial graphene can be interpreted within the model of 2D Dirac fermions, the data obtained on bulk graphite can only be explained taking into account the 3D nature of graphite, e.g. by using the standard Slonczewski-Weiss-McClure model.
We present a comparative study of high carrier density transport in mono-, bi-, and trilayer graphene using electric-double-layer transistors to continuously tune the carrier density up to values exceeding 10^{14} cm^{-2}. Whereas in monolayer the co
nductivity saturates, in bi- and trilayer flling of the higher energy bands is observed to cause a non-monotonic behavior of the conductivity, and a large increase in the quantum capacitance. These systematic trends not only show how the intrinsic high-density transport properties of graphene can be accessed by field-effect, but also demonstrate the robustness of ion-gated graphene, which is crucial for possible future applications.
Multi-layer epitaxial graphene (MEG) is investigated using far infrared (FIR) transmission experiments in the different limits of low magnetic fields and high temperatures. The cyclotron-resonance like absorption is observed at low temperature in mag
netic fields below 50 mT, allowing thus to probe the nearest vicinity of the Dirac point and to estimate the conductivity in nearly undoped graphene. The carrier mobility is found to exceed 250,000 cm$^2$/(V.s). In the limit of high temperatures, the well-defined Landau level (LL) quantization is observed up to room temperature at magnetic fields below 1 T, a phenomenon unique in solid state systems. A negligible increase in the width of the cyclotron resonance lines with increasing temperature indicates that no important scattering mechanism is thermally activated, supporting recent expectations of high room-temperature mobilities in graphene.
Monolayer epitaxial graphene (EG) grown on hexagonal Si-terminated SiC substrates is intrinsically electron-doped (carrier density is about 10^13 cm^(-2)). We demonstrate a clean device fabrication process using a precious-metal protective layer, and
show that etching with aqua regia results in p-type (hole) molecular doping of our un-gated, contamination-free EG. Devices fabricated by this simple process can reach a carrier density in the range of 10^10 cm^(-2) to 10^11 cm^(-2) with mobility about 8000 cm^2/V/s or higher. In a moderately doped device with a carrier density n = 2.4 x 10^11 cm^(-2) and mobility = 5200 cm^2/V/s, we observe highly developed quantized Hall resistance plateaus with filing factor of 2 at magnetic field strengths of less than 4 T. Doping concentrations can be restored to higher levels by heat treatment in Ar, while devices with both p-type and n-type majority carriers tend to drift toward lower carrier concentrations in ambient air.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها