تسجيل مستخدم جديدStudy of molecular spin-crossover complex Fe(phen)2(NCS)2 thin films
284
0
0.0
(
0
)
تأليف
Shengwei Shi
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report on the growth by evaporation under high vacuum of high-quality thin films of Fe(phen)2(NCS)2 (phen=1,10-phenanthroline) that maintain the expected electronic structure down to a thickness of 10 nm and that exhibit a temperature-driven spin transition. We have investigated the current-voltage characteristics of a device based on such films. From the space charge-limited current regime, we deduce a mobility of 6.5x10-6 cm2/V?s that is similar to the low-range mobility measured on the widely studied tris(8-hydroxyquinoline)aluminium organic semiconductor. This work paves the way for multifunctional molecular devices based on spin-crossover complexes.
قيم البحث
اقرأ أيضاً
We present evidence for spin polarized charge carriers in In$_2$O$_3$ films. Both In$_2$O$_3$ and Cr doped In$_2$O$_3$ films exhibit room temperature ferromagnetism after vacuum annealing, with a saturation moment of approximately 0.5 emu/cm$^3$. We
used Point Contact Andreev Reflection measurements to directly determine the spin polarization, which was found to be approximately 50$pm$5% for both compositions. These results are consistent with suggestions that the ferromagnetism observed in certain oxide semiconductors may be carrier mediated.
The availability of large-area substrates imposes an important constraint on the technological and commercial realization of devices made of layered materials. Aluminum nitride films on silicon are shown to be promising candidate materials as large-a
rea substrates for such devices. Herein, the optical contrast of exemplar 2D layers - MoS2and graphene - on AlN films has been investigated as a necessary first step to realize devices on these substrates. Significant contrast enhancements are predicted and observed on AlN films compared to conventional SiO2films. Quantitative estimates of experimental contrast using reflectance spectroscopy show very good agreement with predicted values.
Magnetic materials without structural inversion symmetry can display the Dzyaloshinskii-Moriya interaction, which manifests itself as chiral magnetic ground states. These chiral states can interact in complex ways with applied fields and boundary con
ditions provided by finite sample sizes that are of the order of the lengthscale of the chiral states. Here we study epitaxial thin films of FeGe with a thickness close to the helix pitch of the helimagnetic ground state, which is about 70 nm, by conventional magnetometry and polarized neutron reflectometry. We show that the helix in an FeGe film reverses under the application of a field by deforming into a helicoidal form, with twists in the helicoid being forced out of the film surfaces on the way to saturation. An additional boundary condition was imposed by exchange coupling a ferromagnetic Fe layer to one of the interfaces of an FeGe layer. This forces the FeGe spins at the interface to point in the same direction as the Fe, preventing node expulsion and giving a handle by which the reversal of the helical magnet may be controlled.
Employing a new experimental technique to measure magnetoelectric response functions, we have measured the magnetoelectric effect in composite films of nano granular metallic iron in anatase titanium dioxide at temperatures below 50 K. A magnetoelect
ric resistance is defined as the ratio of a transverse voltage to bias current as a function of the magnetic field. In contrast to the anomalous Hall resistance measured above 50 K, the magnetoelectic resistance below 50 K is significantly larger and exhibits an even symmetry with respect to magnetic field reversal $Hto -H$. The measurement technique required attached electrodes in the plane of the film composite in order to measure voltage as a function of bias current and external magnetic field. To our knowledge, the composite films are unique in terms of showing magnetoelectric effects at low temperatures, $<$ 50 K, and anomalous Hall effects at high temperatures, $>$ 50 K.
We show that properly engineered amorphous Fe-Gd alloy thin films with perpendicular magnetic anisotropy exhibit room-temperature skyrmion molecules, or a pair of like-polarity, opposite-helicity skyrmions. Magnetic mirror symmetry planes present in
the stripe phase, instead of chiral exchange, determine the internal skyrmion structure and the net achirality of the skyrmion phase. Our study shows that stripe domain engineering in amorphous alloy thin films may enable the creation of skyrmion phases with technologically desirable properties.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها