We present evidence for spin polarized charge carriers in In$_2$O$_3$ films. Both In$_2$O$_3$ and Cr doped In$_2$O$_3$ films exhibit room temperature ferromagnetism after vacuum annealing, with a saturation moment of approximately 0.5 emu/cm$^3$. We used Point Contact Andreev Reflection measurements to directly determine the spin polarization, which was found to be approximately 50$pm$5% for both compositions. These results are consistent with suggestions that the ferromagnetism observed in certain oxide semiconductors may be carrier mediated.
قيم البحث
اقرأ أيضاً
We study the surface and bulk electronic structure of the room-temperature ferromagnet Co:TiO2 anatase films using soft and hard x-ray photoemission spectroscopy with probe sensitivities of ~1 nm and ~10 nm, respectively. We obtain direct evidence of
metallic Ti$^{3+}$ states in the bulk, which get suppressed to give a surface semiconductor, thus indicating a surface-bulk dichotomy. X-ray absorption and high-sensitivity resonant photoemission spectroscopy reveal Ti$^{3+}$ electrons at the Fermi level (E$_F$) and high-spin Co$^{2+}$ electrons occurring away from E$_F$. The results show the importance of the charge neutrality condition: Co$^{2+}$ + V$_{O}$$^{2-}$ + 2Ti$^{4+}$ $leftrightarrow$ Co$^{2+}$ + 2Ti$^{3+}$ (V$_O$ is oxygen vacancy), which gives rise to the elusive Ti 3d carriers mediating ferromagnetism via the Co 3d-O 2p-Ti 3d exchange interaction pathway of the occupied orbitals.
We report spin-to-charge and charge-to-spin conversion at room temperature in heterostructure devices that interface an archetypal Dirac semimetal, Cd3As2, with a metallic ferromagnet, Ni0.80Fe0.20 (permalloy). The spin-charge interconversion is dete
cted by both spin torque ferromagnetic resonance and ferromagnetic resonance driven spin pumping. Analysis of the symmetric and anti-symmetric components of the mixing voltage in spin torque ferromagnetic resonance and the frequency and power dependence of the spin pumping signal show that the behavior of these processes is consistent with previously reported spin-charge interconversion mechanisms in heavy metals, topological insulators, and Weyl semimetals. We find that the efficiency of spin-charge interconversion in Cd3As2/permalloy bilayers can be comparable to that in heavy metals. We discuss the underlying mechanisms by comparing our results with first principles calculations.
We studied the ferroelectric and ferromagnetic properties of compressive strained and unstrained BiMnO3 thin films grown by rf-magnetron sputtering. BiMnO3 samples exhibit a 2D cube-on-cube growth mode and a pseudo-cubic struc-ture up to a thickness
of 15 nm and of 25 nm when deposited on (001) SrTiO3 and (110) DyScO3, respectively. Above these thicknesses we observe a switching to a 3D island growth and a simultaneous structural change to a monoclinic structure characterized by a (00l) orientation of the monoclinic unit cell. While ferromagnetism is observed below Tc = 100 K for all samples, signatures of room temperature ferroelectricity were found only in the pseudo-cubic ultra-thin films, indicating a correlation between electronic and structural orders.
We present results on the longitudinal spin Seebeck effect (LSSE) shown by semiconducting ferrimagnetic NiFe2O4/Pt films from room temperature down to 50K base temperature. To the best of our knowledge, this is the first observation of spin caloric e
ffect in NiFe2O4 thin films. The temperature dependence of the conductivity has been studied in parallel to obtain information about the origin of the electric potentials detected at the Pt coverage of the ferrimagnet in order to distinguish the LSSE from the anomalous Nernst effect. Furthermore, the dependence of the LSSE on temperature gradients as well as the influence of an external magnetic field direction is investigated.
The effects of space charges on hysteresis loops and field distributions in ferroelectrics have been investigated numerically using the phenomenological Landau-Ginzburg-Devonshire theory. Cases with the ferroelectric fully and partially depleted have
been considered. In general, increasing the number of charged impurities results in a lowering of the polarization and coercive field values. Squarer loops were observed in the partially depleted cases and a method was proposed to identify fully depleted samples experimentally from dielectric and polarization measurements alone. Unusual field distributions found for higher dopant concentrations have some interesting implications for leakage mechanisms and limit the range of validity of usual semiconductor equations for carrier transport.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها