تسجيل مستخدم جديدFerromagnetism and increased ionicity in epitaxially grown TbMnO3 films
249
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Thin films of TbMnO3 have been grown on SrTiO3 substrates. The films grow under compressive strain and are only partially clamped to the substrate. This produces remarkable changes in the magnetic properties and, unlike the bulk material, the films display ferromagnetic interactions below the ordering temperature of ~40K. X-ray photoemission measurements in the films show that the Mn-3s splitting is 0.3eV larger than that of the bulk. Ab initio embedded cluster calculations yield Mn-3s splittings that are in agreement with the experiment and reveal that the larger observed values are due to a larger ionicity of the films.
قيم البحث
اقرأ أيضاً
The ability to synthesis well-ordered two-dimensional materials under ultra-high vacuum and directly characterize them by other techniques in-situ can greatly advance our current understanding on their physical and chemical properties. In this paper,
we demonstrate that iso-oriented {alpha}-MoO3 films with as low as single monolayer thickness can be reproducibly grown on SrTiO3(001) (STO) substrates by molecular beam epitaxy ( (010)MoO3 || (001)STO, [100]MoO3 || [100]STO or [010]STO) through a self-limiting process. While one in-plane lattice parameter of the MoO3 is very close to that of the SrTiO3 (aMoO3 = 3.96 {AA}, aSTO = 3.905 {AA}), the lattice mismatch along other direction is large (~5%, cMoO3 = 3.70 {AA}), which leads to relaxation as clearly observed from the splitting of streaks in reflection high-energy electron diffraction (RHEED) patterns. A narrow range in the growth temperature is found to be optimal for the growth of monolayer {alpha}-MoO3 films. Increasing deposition time will not lead to further increase in thickness, which is explained by a balance between deposition and thermal desorption due to the weak van der Waals force between {alpha}-MoO3 layers. Lowering growth temperature after the initial iso-oriented {alpha}-MoO3 monolayer leads to thicker {alpha}-MoO3(010) films with excellent crystallinity.
Few-layer PtSe2 films are promising candidates for applications in high-speed electronics, spintronics and photodetectors. Reproducible fabrication of large-area highly crystalline films is, however, still a challenge. Here, we report the fabrication
of epitaxially aligned PtSe2 films using one-zone selenization of pre-sputtered platinum layers. We have studied the influence of the growth conditions on the structural and electrical properties of the films prepared from Pt layers with different initial thickness. The best results were obtained for PtSe2 layers grown at elevated temperatures (600 {deg}C). The films exhibit signatures for a long-range in-plane ordering resembling an epitaxial growth. Charge carrier mobility determined by Hall-effect measurements is up to 24 cm2/V.s in these films.
We studied ZrO2-La2/3Sr1/3MnO3 pillar matrix thin films which were found to show anomalous magnetic and electron transport properties controlled by the amount of ZrO2. With the application of an aberration corrected transmission electron microscope,
structure and chemical information of the system, especially of the pillar matrix interface were revealed at atomic resolution. Minor amounts of Zr were found to occupy Mn positions within the matrix and its solubility within the matrix was found to be less than 6 mol%. Moreover, the Zr concentration reached minimum concentration at the pillar matrix interface accompanied by oxygen deficiency. La and Mn diffusion into the pillar was observed along with a change of the Mn valence state. La and Mn positions inside ZrO2 pillars were also revealed at atomic resolution. These results provide detailed information for future studies of macroscopic properties of these materials.
Two-dimensional (2D) ferromagnetic materials have been exhibiting promising potential in applications, such as spintronics devices. To grow epitaxial magnetic films on silicon substrate, in the single-layer limit, is practically important but challen
ging. In this study, we realized the epitaxial growth of MnSn monolayer on Si(111) substrate, with an atomically thin Sn/Si(111)-$2sqrt{3}times2sqrt{3}$- buffer layer, and controlled the MnSn thickness with atomic-layer precision. We discovered the ferromagnetism in MnSn monolayer with the Curie temperature (Tc) of ~54 K. As the MnSn film is grown to 4 monolayers, Tc increases accordingly to ~235 K. The lattice of the epitaxial MnSn monolayer as well as the Sn/Si(111)-$2sqrt{3}times2sqrt{3}$ is perfectly compatible with silicon, and thus an sharp interface is formed between MnSn, Sn and Si. This system provides a new platform for exploring the 2D ferromagnetism, integrating magnetic monolayers into silicon-based technology, and engineering the spintronics heterostructures.
We studied structural, optical and magnetic properties of high-quality 5 and 15% Co-doped ZnO films grown by plasma-assisted molecular beam epitaxy (MBE) on (0001)-sapphire substrates. Magnetic force microscopy (MFM) and magnetic measurements with SQ
UID magnetometer show clear ferromagnetic behavior of the films up to room temperature whereas they are antiferromagnetic below 200 K approximately. Temperature dependence of the carrier mobility was determined using Raman line shape analysis of the longitudinal-optical-phonon-plasmon coupled modes. It shows that the microscopic mechanism for ferromagnetic ordering is coupling mediated by free electrons between spins of Co atoms. These results bring insight into a subtle interplay between charge carriers and magnetism in MBE-grown Zn(1-x)CoxO films.