Spin-charge-lattice coupling mediated by multi-magnon processes is demonstrated in multiferroic BiFeO3. Experimental evidence of two and three magnons excitations as well as multimagnon coupling at electronic energy scales and high temperatures are reported. Temperature dependent Raman experiments show up to five resonant enhancements of the 2-magnon excitation below the Neel temperature. These are shown to be collective interactions between on-site Fe d-d electronic resonance, phonons and multimagnons
قيم البحث
اقرأ أيضاً
Raman scattering measurements on BiFeO3 single crystals show an important coupling between the magnetic order and lattice vibrations. The temperature evolution of phonons shows that the lowest energy E and A1 phonon modes are coupled to the spin orde
r up to the Neel temperature. Furthermore, low temperature anomalies associated with the spin re-orientation are observed simultaneously in both the E phonon and the magnon. These results suggest that magnetostriction plays an important role in BiFeO3.
A prominent band centered at around 1000-1300 cm-1 and associated with resonant enhancement of two-phonon Raman scattering is reported in multiferroic BiFeO3 thin films and single crystals. A strong anomaly in this band occurs at the antiferromagneti
c Neel temperature. This band is composed of three peaks, assigned to 2A4, 2E8, and 2E9 Raman modes. While all three peaks were found to be sensitive to the antiferromagnetic phase transition, the 2E8 mode, in particular, nearly disappears at TN on heating, indicating a strong spin-two phonon coupling in BiFeO3.
Lattice and spin excitations have been studied by Raman scattering in hexagonal YbMnO3 single crystals. The temperature dependences of the phonon modes show that the E2 mode at 256 cm-1 related to the displacement of Mn and O ions in a-b plane is cou
pled to the spin order. The A1 phonon mode at 678 cm-1 presents a soft mode behavior at the Neel temperature. Connected to the motion of the apical oxygen ions along the c direction, this mode controls directly the Mn-Mn interactions between adjacent Mn planes and the superexchange path. Crystal field and magnon mode excitations have been identified. The temperature investigation of the spin excitations shows that the spin structure is strongly influence by the Yb-Mn interaction. Under a magnetic field along the c axis, we have investigated the magnetic reordering and its impact on the spin excitations.
We used Raman and terahertz spectroscopies to investigate lattice and magnetic excitations and their cross-coupling in the hexagonal YMnO3 multiferroic. Two phonon modes are strongly affected by the magnetic order. Magnon excitations have been identi
fied thanks to comparison with neutron measurements and spin wave calculations but no electromagnon has been observed. In addition, we evidenced two additional Raman active peaks. We have compared this observation with the anti-crossing between magnon and acoustic phonon branches measured by neutron. These optical measurements underly the unusual strong spin-phonon coupling.
We present a comprehensive study of polar and magnetic excitations in BiFeO3 ceramics and a thin film epitaxially grown on an orthorhombic (110) TbScO3 substrate. Infrared reflectivity spectroscopy was performed at temperatures from 5 to 900 K for th
e ceramics and below room temperature for the thin film. All 13 polar phonons allowed by the factor-group analysis were observed in theceramic samples. The thin-film spectra revealed 12 phonon modes only and an additional weak excitation, probably of spin origin. On heating towards the ferroelectric phase transition near 1100 K, some phonons soften, leading to an increase in the static permittivity. In the ceramics, terahertz transmission spectra show five low-energy magnetic excitations including two which were not previously known to be infrared active; at 5 K, their frequencies are 53 and 56 cm-1. Heating induces softening of all magnetic modes. At a temperature of 5 K, applying an external magnetic field of up to 7 T irreversibly alters the intensities of some of these modes. The frequencies of the observed spin excitations provide support for the recently developed complex model of magnetic interactions in BiFeO3 (R.S. Fishman, Phys. Rev. B 87, 224419 (2013)). The simultaneous infrared and Raman activity of the spin excitations is consistent with their assignment to electromagnons.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها