Raman spectroscopic investigations are carried out on one-dimensional nanostructures of InN,such as nanowires and nanobelts synthesized by chemical vapor deposition. In addition to the optical phonons allowed by symmetry; A1, E1 and E2(high) modes, t
wo additional Raman peaks are observed around 528 cm-1 and 560 cm-1 for these nanostructures. Calculations for the frequencies of surface optical (SO) phonon modes in InN nanostructures yield values close to those of the new Raman modes. A possible reason for large intensities for SO modes in these nanostructures is also discussed.
UV Raman scattering studies show longitudinal optical (LO) mode up to 4th order in wurtzite GaN nanowire system. Frohlich interaction of electron with the long range electrostatic field of ionic bonded GaN gives rise to enhancement in LO phonon modes
. Good crystalline quality, as indicated by the crystallographic as well as luminescence studies, is thought to be responsible for this significant observation. Calculated size dependence, incorporating size corrected dielectric constants, of electron-phonon interaction energy agrees well with measured values and also predict stronger interaction energy than that of the bulk for diameter below ~3 nm.