High-temperature superconducting YBa2Cu3O7-d (YBCO) thin-film detectors with improved responsivities were developed for fast time-domain measurements in the THz frequency range. YBCO thin films of 30 nm thickness were patterned to micro- and nanobrid
ges and embedded into planar log-spiral THz antennas. The YBCO thin-film detectors were characterized with continuous wave radiation at 0.65 THz. Responsivity values as high as 710 V/W were found for the YBCO nanobridges. Pulsed measurements in the THz frequency range were performed at the electron storage ring ANKA from the Karlsruhe Institute of Technology (KIT). Due to the high responsivities of the nanobridges no biasing was required for the detection of the coherent synchrotron radiation pulses achieving very good agreement between the measured pulse shapes and simulations.
The photoresponse of YBa2Cu3O7-d thin film microbridges with thicknesses between 15 and 50 nm was studied in the optical and terahertz frequency range. The voltage transients in response to short radiation pulses were recorded in real time with a res
olution of a few tens of picoseconds. The bridges were excited by either femtosecond pulses at a wavelength of 0.8 mu m or broadband (0.1 - 1.5 THz) picosecond pulses of coherent synchrotron radiation. The transients in response to optical radiation are qualitatively well explained in the framework of the two-temperature model with a fast component in the picosecond range and a bolometric nanosecond component whose decay time depends on the film thickness. The transients in the THz regime showed no bolometric component and had amplitudes up to three orders of magnitude larger than the two-temperature model predicts. Additionally THz-field dependent transients in the absence of DC bias were observed. We attribute the response in the THz regime to a rearrangement of vortices caused by high-frequency currents.