Single crystals of (Ca1-xLax)10(Pt3As8)(Fe2As2)5 (x = 0 to 0.182) superconductors have been grown and characterized by X-ray, microprobe, transport and thermodynamic measurements. Features in the magnetic susceptibility, specific heat and two kinks i
n the derivative of the electrical resistivity around 100 K in the x = 0 compound support the existence of decoupled structural and magnetic phase transitions. With La doping, the structural/magnetic phase transitions are suppressed and a half-dome of superconductivity with a maximal Tc around 26 K is observed in the temperature-concentration phase diagram.
Microscopic, structural, transport and thermodynamic measurements of single crystalline Ba(Fe1-xTMx)2As2 (TM = Ni and Cu) series, as well as two mixed TM = Cu / Co series, are reported. All the transport and thermodynamic measurements indicate that t
he structural and magnetic phase transitions at 134 K in pure BaFe2As2 are monotonically suppressed and increasingly separated in a similar manner by these dopants. In the Ba(Fe1-xNix)2As2 (x =< 0.072), superconductivity, with Tc up to 19 K, is stabilized for 0.024 =< x =< 0.072. In the Ba(Fe1-xCux)2As2 (x =< 0.356) series, although the structural and magnetic transitions are suppressed, there is only a very limited region of superconductivity: a sharp drop of the resistivity to zero near 2.1 K is found only for the x = 0.044 samples. In the Ba(Fe1-x-yCoxCuy)2As2 series, superconductivity, with Tc values up to 12 K (x ~ 0.022 series) and 20 K (x ~ 0.047 series), is stabilized. Quantitative analysis of the detailed temperature-dopant concentration (T-x) and temperature-extra electrons (T-e) phase diagrams of these series shows that there exists a limited range of the number of extra electrons added, inside which the superconductivity can be stabilized if the structural and magnetic phase transitions are suppressed enough. Moreover, comparison with pressure-temperature phase diagram data, for samples spanning the whole doping range, further reenforces the conclusion that suppression of the structural / magnetic phase transition temperature enhances Tc on the underdoped side, but for the overdoped side Tcmax is determined by e. Therefore, by choosing the combination of dopants that are used, we can adjust the relative positions of the upper phase lines (structural and magnetic phase transitions) and the superconducting dome to control the occurrence and disappearance of the superconductivity in transition metal, electron-doped BaFe2As2.