We studied the properties of the antiferromagnetic (AFM) UNi0.5Sb2 (TN approx 161 K) compound in Sb-flux grown single crystals by means of measurements of neutron diffraction, magnetic susceptibility ({chi}), specific heat (Cp), thermopower (S), ther
mal conductivity ({kappa}), linear thermal expansion ({Delta}L/L), and electrical resistivity ({rho}) under hydrostatic pressures (P) up to 22 kbar. The neutron diffraction measurements revealed that the compound crystallizes in the tetragonal P42/nmc structure, and the value of the U-moments yielded by the histograms at 25 K is approx 1.85 pm 0.12 {mu}B/U-ion. In addition to the features in the bulk properties observed at TN, two other hysteretic features centered near 40 and 85 K were observed in the measurements of {chi}, S, {rho}, and {Delta}L/L. Hydrostatic pressure was found to raise TN at the rate of approx 0.76 K/kbar, while suppressing the two low temperature features. These features are discussed in the context of Fermi surface and hybridization effects.
We studied the effect of hydrostatic pressure (P) on the structural phase transitions and superconductivity in the ternary and pseudo-ternary iron arsenides CaFe2As2, BaFe2As2, and (Ba0.55K0.45)Fe2As2, by means of measurements of electrical resistivi
ty (rho) in the 1.8 - 300 K temperature (T) range, pressures up to 20 kbar, and magnetic fields up to 9 T. CaFe2As2 and BaFe2As2 (lightly doped with Sn) display structural phase transitions near 170 K and 85 K, respectively, and do not exhibit superconductivity in ambient pressure, while K-doped (Ba0.55K0.45)Fe2As2 is superconducting for T < 30 K. The effect of pressure on BaFe2As2 is to shift the onset of the crystallographic transformation down in temperature at the rate of about -1.04 K/kbar, while shifting the whole rho(T) curves downward, whereas its effect on superconducting (Ba0.55K0.45)Fe2As2 is to shift the onset of superconductivity to lower temperatures at the rate of about -0.21 K/kbar. The effect of pressure on CaFe2As2 is first to suppress the crystallographic transformation and induce superconductivity with onset near 12 K very rapidly, i.e., for P < 5 kbar. However, higher pressures bring about another phase transformation characterized by reduced resistivity, and the suppression of superconductivity, confining superconductivity to a narrow pressure dome centered near 5 kbar. Upper critical field (Hc2) data in (Ba0.55K0.45)Fe2As2 and CaFe2As2 are discussed.
The intermetallic compound LaAgSb2 displays two charge-density-wave (CDW) transitions, which were detected with measurements of electrical resistivity (rho), magnetic susceptibility, and X-ray scattering; the upper transition takes place at T1 approx
. 210 K, and it is accompanied by a large anomaly in rho(T), whereas the lower transition is marked by a much more subtle anomaly at T2 approx. 185 K. We studied the effect of hydrostatic pressure (P) on the formation of the upper CDW state in pure and doped La1-xRxAgSb2 (R = Ce, Nd) compounds, by means of measurements of rho(T) for P < 23 kbar. We found that the hydrostatic pressure, as well as the chemical pressure introduced by the partial substitution of the smaller Ce and Nd ions for La, result in the suppression of the CDW ground state, e.g. the reduction of the ordering temperature T1. The values of dT1/dP are approx. 2-4 times higher for the Ce-doped samples as compared to pure LaAgSb2, or even La0.75Nd0.25AgSb2 Nd-doped with a comparable T1 (P=0). This increased sensitivity to pressure may be due to increasing Ce- hybridization under pressure. The magnetic ordering temperature of the cerium-doped compounds is also reduced by pressure, and the high pressure behavior of the Ce-doped samples is dominated by Kondo impurity scattering.
We studied single-crystalline Pr0.5Sr0.5MnO3 by means of measurements of magnetic susceptibility and specific heat at ambient pressure (P), and electrical resistivity (r) in hydrostatic pressures up to 2 GPa. This material displays ferromagnetic (FM)
order, with Curie temperature TC ~ 255 K. A crystallographic transformation from I4/mcm to Fmmm is accompanied by the onset of antiferromagnetism (AFM), with Neel temperature TN ~ 161 K. The effect of pressure is to lower TC, and raise TN at the approximate rates of -3.2 K/GPa, and 14.2 K/GPa, respectively. Although the value of TN increases with P, due to the enhancement of the superexchange interactions, the AFM-Fmmm state is progressively suppressed, as pressure stabilizes the FM-I4/mcm phase to lower temperatures. The r vs T data suggest that the AFM phase should be completely suppressed near 2.4 GPa.
We studied single-crystals of the antiferromagnetic compound UNi0.5Sb2 (TN ~ 161 K) by means of measurements of magnetic susceptibility (chi), specific heat (Cp), and electrical resistivity (rho) at ambient pressure, and resistivity under hydrostatic
pressures up to 20 kbar, in the temperature range from 1.9 to 300 K. The thermal coefficient of the electrical resistivity (drho/dT) changes drastically from positive below TN to negative above, reflecting the loss of spin-disorder scattering in the ordered phase. Two small features in the rho vs T data centered near 40 and 85 K correlate well in temperature with features in the magnetic susceptibility and are consistent with other data in the literature. These features are quite hysteretic in temperature, i.e., the difference between the warming and cooling cycles are about 10 and 6 K, respectively. The effect of pressure is to raise TN at the approximate rate of 0.76 K/kbar, while progressively suppressing the amplitude of the small features in rho vs T at lower temperatures and increasing the thermal hysteresis.