In this work we report the appearence of a large perpendicular magnetic anisotropy (PMA) in Fe$_{1-x}$Ga$_x$ thin films grown onto ZnSe/GaAs(100). This arising anisotropy is related to the tetragonal metastable phase in as-grown samples recently repo
rted [M. Eddrief {it et al.}, Phys. Rev. B {bf 84}, 161410 (2011)]. By means of ferromagnetic resonance studies we measured PMA values up to $sim$ 5$times$10$^5$ J/m$^3$. PMA vanishes when the cubic structure is recovered upon annealing at 300$^{circ}$C. Despite the important values of the magnetoelastic constants measured via the cantilever method, the consequent magnetoelastic contribution to PMA is not enough to explain the observed anisotropy values in the distorted state. {it Ab initio} calculations show that the chemical ordering plays a crucial role in the appearance of PMA. Through a phenomenological model we are able to explain that an excess of next nearest neighbour Ga pairs (B$_2$-like ordering) along the perpendicular direction arises as the source of PMA in Fe$_{1-x}$Ga$_x$ thin films.
Since Reactor Pressure Vessel steels are ferromagnetic, they provide a convenient means to monitor changes in the mechanical properties of the material upon irradiation with high energy particles, by measuring their magnetic properties. Here, we disc
uss the correlation between these two properties (i.e. mechanical and magnetic properties) and microstructure, by studying the flux effect on the nuclear pressure vessel steel used in reactors currently under construction in Argentina. Charpy-V notched specimens of this steel were irradiated in the RA1 experimental reactor at 275{deg}C with two lead factors (LFs), 93 and 183. The magnetic properties were studied by means of DC magnetometry and ferromagnetic resonance. The results show that the coercive field and magnetic anisotropy spatial distribution are sensitive to the LF and can be explained by taking into account the evolution of the microstructure with this parameter. The saturation magnetization shows a dominant dependence on the accumulated damage. Consequently, the mentioned techniques are suitable to estimate the degradation of the reactor vessel steel.