The superconducting system La2-xBaxCuO4 is known to show a minimum in the transition temperature, Tc, at x = 1/8 where maximal stripe order is pinned by the anisotropy within the CuO2 planes that occurs in the low-temperature-tetragonal (LTT) crystal
structure. For x = 0.095, where Tc reaches its maximum value of 32 K, there is a roughly coincident structural transition to a phase that is very close to LTT. Here we present a neutron scattering study of the structural transition, and demonstrate how features of it correlate with anomalies in the magnetic susceptibility, electrical resistivity, thermal conductivity, and thermoelectric power. We also present measurements on a crystal with 1% Zn substituted for Cu, which reduces Tc to 17 K, enhances the spin stripe order, but has much less effect on the structural transition. We make the case that the structural transition correlates with a reduction of the Josephson coupling between the CuO2 layers, which interrupts the growth of the superconducting order. We also discuss evidence for two-dimensional superconducting fluctuations in the normal state, analyze the effective magnetic moment per Zn impurity, and consider the significance of the anomalous thermopower often reported in the stripe-ordered phase.
We performed elastic neutron scattering measurements on the charge- and magnetically-ordered multiferroic material LuFe(2)O(4). An external electric field along the [001] direction with strength up to 20 kV/cm applied at low temperature (~100 K) does
not affect either the charge or magnetic structure. At higher temperatures (~360 K), before the transition to three-dimensional charge-ordered state, the resistivity of the sample is low, and an electric current was applied instead. A reduction of the charge and magnetic peak intensities occurs when the sample is cooled under a constant electric current. However, after calibrating the real sample temperature using its own resistance-temperature curve, we show that the actual sample temperature is higher than the thermometer readings, and the intensity reduction is entirely due to internal sample heating by the applied current. Our results suggest that the charge and magnetic orders in LuFe(2)O(4) are unaffected by the application of external electric field/current, and previously observed electric field/current effects can be naturally explained by internal sample heating.
We report on neutron-scattering results on the impact of a magnetic field on stripe order in the cuprate La$_{1.875}$Ba$_{0.125}$CuO$_4$. It is found that a 7 T magnetic field applied along the {it c} axis causes a small but finite enhancement of the
spin-order peak intensity and has no observable effect on the peak width. Inelastic neutron-scattering measurements indicate that the low-energy magnetic excitations are not affected by the field, within experimental error. In particular, the small energy gap that was recently reported is still present at low temperature in the applied field. In addition, we find that the spin-correlation length along the antiferromagnetic stripes is greater than that perpendicular to them.
We present high energy x-ray (67 keV) and neutron scattering measurements on a single crystal of K$_{1-x}$Li$_x$TaO$_3$ for which the Li content ($x=0.02$) is less than $x_c = 0.022$, the critical value below which no structural phase transitions hav
e been reported in zero field. While the crystal lattice does remain cubic down to T=10 K under both zero-field and field-cooled ($E le 4$ kV/cm) conditions, indications of crystal symmetry lowering are seen at $T_C=63$ K where the Bragg peak intensity changes significantly. A strong and frequency-dependent dielectric permittivity is observed at ambient pressure, a defining characteristic of relaxors. However an extensive search for static polar nanoregions, which is also widely associated with relaxor materials, detected no evidence of elastic neutron diffuse scattering between 300 K and 10 K. Neutron inelastic scattering methods were used to characterize the transverse acoustic and optic phonons (TA1 and TO1 modes) near the (200) and (002) Bragg peaks. The zone center TO1 mode softens monotonically with cooling but never reaches zero energy in either zero field or in external electric fields of up to 4 kV/cm. These results are consistent with the behavior expected for a dipolar glass in which the local polar moments are frozen and exhibit no long-range order at low temperatures.
Effects of the growth velocity on the crystal growth behavior of Bi_2Sr_2Ca_1Cu_2O_x (Bi-2212) have been studied by floating zone technique. The results show that a necessary condition for obtaining large single crystals along the c-axis is that the
solid-liquid interface of a growing rod maintains a stable planar growth front. The planar liquid-solid growth interface tends to break down into a cellular interface, while the growth velocity is higher than 0.25 mm/h. Single crystals of up to 50x7.2x7 mm3 along the a-, b- and caxes have been cut in a 7.2 mm diameter rod with optimum growth conditions. Tconset is 91 K measured by magnetic properties measurement system (MPMS) for as-grown crystals. Optical polarization microscope and neutron diffraction show that the quality of the single crystals is good.