Imaging Flux Vortices in MgB2 using Transmission Electron Microscopy

We report the successful imaging of flux vortices in single crystal MgB2 using transmission electron microscopy. The specimen was thinned to electron transparency (350 nm thickness) by focussed ion beam milling. An artefact of the thinning process was the production of longitudinal thickness undulations of height 1-2 nm in the sample which acted as pinning sites due to the energy required for the vortices to cross them. These had a profound effect on the patterns of vortex order observed which we examine here. Supplementary information can be downloaded from http://www-hrem.msm.cam.ac.uk/people/loudon/#publications

Determination of the Nature of the Tetragonal to Orthorhombic Phase Transition in SrFe_2As_2 by Measurement of the Local Order Parameter

SrFe2As2 is the end-member for a series of iron-pnictide superconductors and has a tetragonal-to-orthorhombic phase transition near 200 K. Previous macroscopic measurements to determine the nature of the transition gave seemingly inconsistent results so we use electron microscopy to monitor the local order parameter showing that the transformation is first order and that the orthorhombic phase grows as needle domains. This suggests the transition occurs via the passage of transformation dislocations, explaining the apparent inconsistencies. This mechanism may be common to similar transitions.