The structural properties of the SrFe2As2 and CaFe2As2 compounds have been extensively analyzed by transmission electron microscopy (TEM) from room temperature down to 20K. The experimental results demonstrate that the SrFe2As2 crystal, in consistenc
e with previous x-ray data, has a tetragonal structure at room temperature and undergoes a tetragonal (T)-orthorhombic (O) phase transition at about 210K. Moreover, twinning lamella arising from T-O transition evidently appears in the orthorhombic phase. On the other hand, TEM observations of CaFe2As2 reveal the presence of a pseudo-periodic structural modulation with the periodicity of around 40nm at room temperature. This modulation is likely in connection with the local structural distortions within the Ca layer. In-situ cooling TEM observations of CaFe2As2 reveal the presence of complex domain structures in the low-temperature orthorhombic phase.
The structural properties of the ROFeM (R=La, Nd; M=As, P) materials have been analyzed by means of electron diffraction, high-resolution transmission-electron microscopy (TEM) and in-situ cooling TEM observations. The experimental results demonstrat
e that the layered ROFeM crystals often contain a variety of structural defects, such as stacking faults and small-angle boundaries. The in-situ TEM investigations reveal that, in association with the remarkable spin-density-wave (SDW) instability near 150 K, complex structural transitions can be clearly observed in both crystal symmetry and local microstructure features.