We have selected stress-annealed nanocrystalline Fe-based ribbons for ferromagnetic/copper/ferromagnetic sensors exhibiting high magneto-impedance ratio. Longitudinal magneto-impedance reaches 400% at 60 kHz and longitudinal magneto-resistance increases up to 1300% around 200 kHz.
The resistive and reactive components of magneto-impedance (MI) for Finemet/Copper/Finemet sandwiched structures based on stress-annealed nanocrystalline Fe75Si15B6Cu1Nb3 ribbons as functions of different fields (longitudinal and perpendicular) and f
requencies have been measured and analyzed. Maximum magneto-resistance and magneto-inductance ratios of 700% and 450% have been obtained in 30-600 kHz frequency range respectively. These large magneto-resistance and magneto-inductive ratios are a direct consequence of the large effective relative permeability due to the closed magnetic flux path in the trilayer structure. The influence of perpendicular bias fields (Hper) in the Longitudinal Magneto-impedance (LMI) configuration greatly improves the MI ratios and sensitivities. The maximum MI ratio for the resistive part increases to as large as 2500% for Hper ~ 1 Oe. The sensitivity of the magneto-resistance increases from 48%/Oe to 288%/Oe at 600 kHz frequency with the application of Hper ~ 30 Oe. Such high increase in MI ratios and sensitivities with perpendicular bias fields are due to the formation the favourable (transverse) domain structures.