Single crystal of CeAl has been grown by flux method using Ce-Al self-flux. Several needle like single crystals were obtained and the length of the needle corresponds to the [001] crystallographic direction. Powder x-ray diffraction revealed that CeA
l crystallizes in orthorhombic CrB-type structure with space group ${Cmcm}$ (no. 63). The magnetic properties have been investigated by means of magnetic susceptibility, isothermal magnetization, electrical transport, and heat capacity measurements. CeAl is found to order antiferromagnetically with a N$grave{rm e}$el temperature $T_{rm N}$ = 10K. The magnetization data below the ordering temperature reveals two metamagentic transitions for fields less than 20kOe. From the inverse magnetic susceptibility an effective moment of $2.66mu_{rm B}$/Ce has been estimated, which indicates that Ce is in its trivalent state. Electrical resistivity data clearly shows a sharp drop at 10K due to the reduction of spin disorder scattering of conduction electrons thus confirming the magnetic ordering. The estimated residual resistivity ratio (RRR) is 33, thus indicating a good quality of the single crystal. The bulk nature of the magnetic ordering is also confirmed by heat capacity data. From the Schottky anomaly of the heat capacity we have estimated the crystal field level splitting energies of the $(2J+1)$ degenerate ground state as 25K and 175K respectively for the fist and second excited states.
Single crystal of PrSi was grown by Czochralski method in a tetra-arc furnace. Powder x-ray diffraction of the as grown crystal revealed that PrSi crystallizes in FeB$-$type structure with space group $Pnma$ (no. 62). PrSi undergoes a ferromagnetic t
ransition at 52 K with [010] direction as the easy axis of magnetization. Heat capacity data confirm the bulk nature of the transition at 52 K and exhibit a huge anomaly at the transition. A sharp rise in the low temperature heat capacity has been observed (below 5 K) which is attributed to the $^{141}$Pr nuclear Schottky heat capacity arising from the hyperfine field of the Pr moment. The estimated Pr magnetic moment 2.88 $mu_{rm B}$/Pr from the hyperfine splitting is in agreement with the saturation magnetization value obtained from the magnetization data measured at 2 K. From the crystal electric field (CEF) analysis of the magnetic susceptibility, magnetization and the heat capacity data it is found that the degenerate $J = 4$ Hunds rule derived state of Pr$^{3+}$-ion splits into nine singlets with an overall splitting of 284 K, the first excited singlet state separated by just 9 K from the ground state. The magnetic ordering in PrGe appears to be due to the exchange generated admixture of low lying crystal field levels. Magnetocaloric effect (MCE) has been investigated from magnetization data along all the three principal crystallographic directions. Large magnetic entropy change, $-Delta S_M = $22.2 J/kg K, and the relative cooling power, RCP = $460$ J/kg, characteristic of giant magneto caloric effect are achieved near the transition temperature ($T_{rm C}$ = 52 K) for $H =$~70 kOe along $[010]$. Furthermore, the PrSi single crystal exhibits a giant MCE anisotropy.
Single crystal of CeMg$_{12}$ is obtained by Bridgman method. CeMg$_{12}$ crystallizes in the tetragonal structure with space group $I4/mmm$ (#139). The Laue pattern confirms the tetragonal crystal structure of CeMg$_{12}$. We have studied the magnet
ic properties by measuring magnetic susceptibility, magnetization, heat capacity and electrical transport. Specific heat measurement shows that the compound orders at 1.2 K. We have measured the magnetic susceptibility in the temperature range 1.8 to 300 K, and the susceptibility data show that [100] crystallographic direction is the easy axis of magnetization. At high temperature inverse susceptibility varies linearly with temperature, and follows the Curie-Weiss behaviour. The effective moment is close to the free ion value thus indicating Ce is in trivalent state in this compound.
We report anisotropic dc magnetic susceptibility $chi(T)$, electrical resistivity $rho(T)$, and heat capacity $C(T)$ measurements on the single crystals of CaFe$_{2-x}$Co$_x$As$_2$ for $x$ = 0 and 0.06. Large sized single crystals were grown by the h
igh temperature solution method with Sn as the solvent. For the pure compound with $x$ = 0, a high temperature transition at 170 K is observed which is attributed to a combined spin density wave (SDW) ordering and a structural phase transition. On the other hand, for the Co-doped samples for $x$ = 0.06, the SDW transition is suppressed while superconductivity is observed at $simeq$17 K. The superconducting transition has been confirmed from the magnetization and electrical resistivity studies. The $^{57}$Fe Mossbauer spectrum in CaFe$_2$As$_2$ indicates that the SDW ordering is incommensurate. In the Co-doped sample, a prominent paramagnetic line at 4.2 K is observed indicating a weakening of the SDW state.
We report the single crystal growth and anisotropic magnetic properties of the tetragonal RAg$_2$Ge$_2$ (R = Pr, Nd and Sm) compounds which crystallize in the ThCr$_2$Si$_2$ type crystal structure with the space group textit{I4/mmm}. The single cryst
als of RAg$_2$Ge$_2$ (R = Pr, Nd and Sm) were grown by self-flux method using Ag:Ge binary alloy as flux. From the magnetic studies on single crystalline samples we have found that PrAg$_2$Ge$_2$ and NdAg$_2$Ge$_2$ order antiferromagnetically at 12 K and 2 K respectively, thus corroborating the earlier polycrystalline results. SmAg$_2$Ge$_2$ also orders antiferromagnetically at 9.2 K. The magnetic susceptibility and magnetization show a large anisotropy and the easy axis of magnetization for PrAg$_2$Ge$_2$ and NdAg$_2$Ge$_2$ is along the [100] direction where as it changes to [001] direction for SmAg$_2$Ge$_2$. Two metamagnetic transitions were observed in NdAg$_2$Ge$_2$ at $H_{rm m1}$ = 1.25 T and $H_{rm m2}$ =3.56 T for the field parallel to [100] direction where as the magnetization along [001] direction was linear indicating the hard axis of magnetization.
We have successfully grown the single crystals of CeAg$_2$Ge$_2$, for the first time, by flux method and studied the anisotropic physical properties by measuring the electrical resistivity, magnetic susceptibility and specific heat. We found that CeA
g$_2$Ge$_2$ undergoes an antiferromagnetic transition at $T_{rm N}$ = 4.6 K. The electrical resistivity and susceptibility data reveal strong anisotropic magnetic properties. The magnetization measured at $T$ = 2 K exhibited two metamagnetic transitions at $H_{rm m1}$ = 31 kOe and $H_{rm m2}$ = 44.7 kOe, for $H parallel$ [100] with a saturation magnetization of 1.6 $mu_{rm B}$/Ce. The crystalline electric field (CEF) analysis of the inverse susceptibility data reveals that the ground state and the first excited states of CeAg$_2$Ge$_2$ are closely spaced indicating a quasi-quartet ground state. The specific heat data lend further support to the presence of closely spaced energy levels.